Microwave circuit boards
Assignee: Rogers Corp
•
Filing: 1984-11-09
•
Granted: 1986-12-30
•
Expires: 2004-11-09
Abstract
Abstract Circuit boards, useful in microwave frequency applications, are formed from a laminate consisting initially of an insulator sandwiched between a copper foil and an aluminum plate. The boards are provided with through-hole connections by means of a procedure which includes drilling through the board to form through-holes, anodizing all exposed surfaces of the aluminum, electroplating copper over all anodized aluminum surfaces, sodium or plasma etching to alter the surface of the walls of the holes in the insulator to allow them to be "wet", and electroless copper plating the entire board to form a continuous upper coating over the copper foil, the copper plate and the walls of the through-holes.
Inventors
- 👤 Rodger P. McMonagle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:44
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/40; H05K3/42; H05K3/44; H05K9/00; H05K9/0007; H05K9/002; H05K9/0039; H05K1/00; H05K1/02; H05K1/0213; H05K1/0237; H05K1/03; H05K1/05; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0347; H05K2201/09; H05K2201/09209; H05K2201/095; H05K2201/09554; H05K2203/00; H05K2203/03; H05K2203/0315; H05K3/425; H05K3/427; Y; Y10; Y10S; Y10S428/00; Y10S428/901
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
103 words
A circuit board structure comprising: a laminate of dielectric material sandwiched between a first relatively thick layer of aluminum and a second relatively thin layer of copper; at least one through-hole in the laminate; a coating of conductive metal electroplated on all outer or exposed surfaces of said aluminum, said outer or exposed surfaces of said aluminum being anodized prior to electrodeposition of the conductive metal; and a coating of conductive electroless deposited metal on all outer or exposed surfaces of the relatively thin copper layer, the electroplated aluminum and the dielectric material, including any portions thereof defining the walls of the through-holes.
Claim 2
Dependent Claim
103 words
A circuit board structure comprising: a laminate of dielectric material sandwiched between a first relatively thick layer of aluminum and a second relatively thin layer of copper; at least one through-hole in the laminate; a coating of conductive metal electroplated on all outer or exposed surfaces of said aluminum, said outer or exposed surfaces of said aluminum being anodized prior to electrodeposition of the conductive metal; and a coating of conductive electroless deposited metal on all outer or exposed surfaces of the relatively thin copper layer, the electroplated aluminum and the dielectric material, including any portions thereof defining the walls of the through-holes.
Claim 3
Dependent Claim
22 words
A circuit board structure as in claim 1 wherein: said conductive electroplated metal coating selected from the group of copper and nickel.
Claim 4
Dependent Claim
23 words
A circuit board structure as in claim 2 wherein: said conductive electroless deposited metal coating selected from the group of copper and nickel.
Claim 5
Dependent Claim
85 words
A circuit board from a laminate of dielectric material sandwiched between layers of copper and aluminum prepared from a method comprising the steps of: forming at least one through-hole in the laminate; anodizing the exposed areas of the aluminum layer in H 3 PO 4 while electrically isolating the aluminum from the copper; electroplating a conductive metal over the anodic coating on the aluminum; etching exposed areas of the dielectric material; and electroless plating a conductive metal coating over all exposed surfaces of the laminate.
Claim 6
Dependent Claim
85 words
A circuit board from a laminate of dielectric material sandwiched between layers of copper and aluminum prepared from a method comprising the steps of: forming at least one through-hole in the laminate; anodizing the exposed areas of the aluminum layer in H 3 PO 4 while electrically isolating the aluminum from the copper; electroplating a conductive metal over the anodic coating on the aluminum; etching exposed areas of the dielectric material; and electroless plating a conductive metal coating over all exposed surfaces of the laminate.
Claim 7
Dependent Claim
44 words
The circuit board of claim 4 wherein the step of forming through-holes further comprises: forming a pattern of holes through the aluminum-dielectric-copper laminate whereby the subsequent steps of anodizing, electroplating, etching and electroless plating will establish conductive paths through the board via plated through-holes.
Claim 8
Dependent Claim
33 words
The circuit board of claim 4 wherein the step of anodizing is continued until an oxide coating having a weight in the range of 0.1 to 2.0 milligrams per square inch is formed.
Claim 9
Dependent Claim
33 words
The circuit board of claim 4 wherein the step of anodizing is continued until an oxide coating having a weight in the range of 0.1 to 2.0 milligrams per square inch is formed.
Claim 10
Dependent Claim
51 words
The circuit board of claim 4 wherein the step of electroplating includes electroplating metal selected from the group of copper and nickel under the following conditions: solution temperature=70° to 90° F. cathode current=20 to 40 amps/ft 2 anode-cathode are ratio=1:1 to 2:1 time=10 to 20 min. solution agitated with clean air
Claim 11
Dependent Claim
84 words
A circuit board from a laminate of dielectric material sandwiched between layers of copper and aluminum prepared from a method comprising the steps of: forming at least one through-hole in the laminate; anodizing the exposed areas of the aluminum layer in an anodizing solution while electrically isolating the aluminum from the copper; electroplating a conductive metal over the anodic coating on the aluminum; etching exposed areas of the dielectric material; and electroless plating a conductive metal coating over all exposed surfaces of the laminate.
Claim 12
Dependent Claim
84 words
A circuit board from a laminate of dielectric material sandwiched between layers of copper and aluminum prepared from a method comprising the steps of: forming at least one through-hole in the laminate; anodizing the exposed areas of the aluminum layer in an anodizing solution while electrically isolating the aluminum from the copper; electroplating a conductive metal over the anodic coating on the aluminum; etching exposed areas of the dielectric material; and electroless plating a conductive metal coating over all exposed surfaces of the laminate.
Claim 13
Dependent Claim
44 words
The circuit board of claim 9 wherein the step of forming through-holes further comprise: forming a pattern of holes through the aluminum-dielectric-copper laminate whereby the subsequent steps of anodizing, electroplating, etching and electroless plating will establish conductive paths through the board via plated through-holes.
Claim 14
Dependent Claim
51 words
The circuit board of claim 9 wherein the step of electroplating includes electroplating metal selected from the group of copper and nickel under the following conditions: solution temperature=70° to 90° F. cathode current=20 to 40 amps/ft 2 anode-cathode area ratio=1:1 to 2:1 time=10 to 20 min. solution agitated with clean air.
References Cited (Backward Citations)
US3694250A
Cited
DE2546301A1
Cited
US4372804A
Cited
US4293377A
Cited
US4389278A
Cited
US4525247A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |