Poly(p-phenylene sulfide) film and process for production thereof
Assignee: DIC Corp
•
Filing: 1986-01-06
•
Granted: 1986-12-16
•
Expires: 2006-01-06
Abstract
Abstract A biaxially oriented crystalline poly(p-phenylene sulfide) film wherein said polymer contains at least 90 mole % of recurring units of the formula <IMAGE> and has a melt viscosity of at least 0.12 dl/g and when said film is heat-treated at 270 DEG C. for 10 minutes under relaxation and then stretched at 23 DEG C. at a rate of 200%/min., its tensile strength, stress at 5% stretch and elongation show a percent retention of at least 60%, at least 80%, and 80 to 120%, respectively, based on these properties of the same film which has been stretched under said conditions without the heat-treatment; and a process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature in the range of from 3 DEG C. above its melting point measured by a differential scanning calorimeter to 350 DEG C. at a constant length or under tension or in a moderate relaxed condition.
Inventors
- 👤 Toshinori Sugie
- 👤 Fumihiro Kobata
- 👤 Takashi Kawamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 02:24
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/0209; C08G75/0213; C08G75/0231; C08G75/025; C08G75/0254; C08G75/0277; C08G75/14; C08J2381/00; C08J2381/02
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
101 words
A biaxially oriented crystalline poly(p-phenylene sulfide) film wherein said polymer contains at least 90 mole % of recurring units of the formula ##STR11## and has a melt viscosity of at least 0.12 dl/g and when said film is heat-treated at 270° C. for 10 minutes under relaxation and then stretched at 23° C. at a rate of 200%/min., its tensile strength, stress at 5% stretch and elongation show a percent retention of at least 60%, at least 80%, and 80 to 120%, respectively, based on these properties of the same film which has been stretched under said conditions without the heat-treatment.
Claim 2
Dependent Claim
101 words
A biaxially oriented crystalline poly(p-phenylene sulfide) film wherein said polymer contains at least 90 mole % of recurring units of the formula ##STR11## and has a melt viscosity of at least 0.12 dl/g and when said film is heat-treated at 270° C. for 10 minutes under relaxation and then stretched at 23° C. at a rate of 200%/min., its tensile strength, stress at 5% stretch and elongation show a percent retention of at least 60%, at least 80%, and 80 to 120%, respectively, based on these properties of the same film which has been stretched under said conditions without the heat-treatment.
Claim 3
Dependent Claim
17 words
The film of claim 1 wherein the polymer has a solution viscosity of 0.12 to 1.0 dl/g.
Claim 4
Dependent Claim
19 words
The film of claim 1 which has a percent retention of stress at 5% stretch of 80 to 110%.
Claim 5
Dependent Claim
16 words
The film of claim 1 which has a percent retention of elongation of 90 to 120%.
Claim 6
Dependent Claim
28 words
The film of claim 1 which has a shrinkage of not more than 2% when it is dipped in a solder bath at 260° C. for 30 seconds.
Claim 7
Dependent Claim
55 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature in the range of from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C. at a constant length or under tension or in a moderate relaxed condition.
Claim 8
Dependent Claim
55 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature in the range of from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C. at a constant length or under tension or in a moderate relaxed condition.
Claim 9
Dependent Claim
101 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature of main heat-treatment ranging from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C. at a constant length or under tension or in a moderate relaxed condition, and then heat-treating the film at a temperature of after heat-treatment of 150° to 345° C. at a constant length or under tension or in a moderate relaxed condition, said temperature of main heat-treatment being at least 5° C. higher than said temperature of after heat-treatment.
Claim 10
Dependent Claim
101 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature of main heat-treatment ranging from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C. at a constant length or under tension or in a moderate relaxed condition, and then heat-treating the film at a temperature of after heat-treatment of 150° to 345° C. at a constant length or under tension or in a moderate relaxed condition, said temperature of main heat-treatment being at least 5° C. higher than said temperature of after heat-treatment.
Claim 11
Dependent Claim
98 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature of preliminary heat-treatment of 150° to 345° C. at a constant length or under tension or in a moderate relaxed condition, and then heat-treating it at a main heat-treatment temperature in the range of from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C., which is at least 5° C. higher than said temperature of preliminary heat-treatment, at a constant length or under tension or in a moderate relaxed condition.
Claim 12
Dependent Claim
98 words
A process for producing a crystalline poly(p-phenylene sulfide) film, which comprises heat-treating a biaxially oriented amorphous poly(p-phenylene sulfide) film at a temperature of preliminary heat-treatment of 150° to 345° C. at a constant length or under tension or in a moderate relaxed condition, and then heat-treating it at a main heat-treatment temperature in the range of from 3° C. above its melting point measured by a differential scanning calorimeter to 350° C., which is at least 5° C. higher than said temperature of preliminary heat-treatment, at a constant length or under tension or in a moderate relaxed condition.
Claim 13
Dependent Claim
20 words
The process of claim 6 wherein the heat-treatment is carried out for a period of not more than 120 seconds.
Claim 14
Dependent Claim
23 words
The process of claim 7 wherein the heat-treatment at the temperature of after heat-treatment is carried out for 0.01 second to 10 minutes.
Claim 15
Dependent Claim
26 words
The process of any one of claims 6 to 8 wherein the amorphous biaxially oriented poly(p-phenylene sulfide) film has a thickness of 0.5 to 1000 μm.
Claim 16
Dependent Claim
38 words
The process of any one of claims 6 to 8 wherein the heat-treatment is carried out in an atmosphere of air, nitrogen, helium, oxygen, hydrogen, argon, steam, a vapor of a lower-boiling organic compound, or a mixture thereof.
Claim 17
Dependent Claim
41 words
The process of any one of claims 6 to 8 wherein the heat-treatment is carried out by using hot water, an organic compound which is liquid and inert at the heat-treating temperature, a metal, wood or ceramic as a heat medium.
Claim 18
Dependent Claim
27 words
The process of claim 13 wherein the organic compound is diphenyl ether, diphenyl, diphenyl oxide, ethyl diphenyl, terphenyl, hydrogenated terphenyl, diphenylene oxide, triethylene glycol, dodecane or dodecanol.
Claim 19
Dependent Claim
30 words
The process of claim 13 wherein the metal is stainless steel, iron, gold, silver, copper, brass, tin, nickel, cobalt, zinc, lead, aluminum or an alloy of any one of these.
Claim 20
Dependent Claim
16 words
The process of claim 13 wherein the ceramic is titanium oxide, zirconia, alumina or silicon nitride.
Claim 21
Dependent Claim
30 words
The process of any one of claims 6 to 8 wherein the amorphous biaxially oriented poly(p-phenylene sulfide) film is under a restricted shrinkage or stretch of not more than 25%.
Claim 22
Dependent Claim
23 words
The process of any one of claims 6 to 8 wherein the biaxially oriented crystalline poly(p-phenylene sulfide) film is kept at constant length.
Claim 23
Dependent Claim
15 words
The process of claim 6 wherein the temperature is from 290° C. to 330° C.
Claim 24
Dependent Claim
24 words
The film of claim 1 having a degree of crystallization of 20 to 48% and a density of 1.341 to 1.371 g/cm 3 .
Claim 25
Dependent Claim
22 words
The process of claim 7 or 8 wherein the main heat-treatment is at a temperature of from 290° C. to 330° C.
Claim 26
Dependent Claim
21 words
The process of claim 6 wherein the heat-treating temperature is from 3° C. to 45° C. higher than the melting point.
Claim 27
Dependent Claim
25 words
The process of claim 7 or 8 wherein the main heat-treatment is at a temperature of from 3° to 45° C. above the melting point.
Claim 28
Dependent Claim
20 words
The process of claim 6 wherein the heat-treatment is carried out for a time of from 0.1 to 60 seconds.
References Cited (Backward Citations)
US4286018A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-15 | 1990-06-16 | 1990-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-15 | 1994-06-16 | 1994-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-15 | 1998-06-16 | 1998-12-16 | $7700.00 | Window Closed / Lapsed |