Process for producing polycrystalline, translucent sintered tubes
Assignee: Ceramtec GmbH
•
Filing: 1984-08-22
•
Granted: 1986-12-16
•
Expires: 2004-08-22
Abstract
Abstract An improved process for producing polycrystalline, translucent sintered aluminum oxide tubes for use as high pressure gas discharge lamps is provided, in which an aluminum oxide powder mixture is dispersed and foamed prior to plasticizing. Into the dried powder plasticizing components based on PVA or low viscosity, weakly swelling methylcellulose adhesives in the form of a paste are mixed and the powder mixture subsequently cold formed to tubular form by extrusion. The application of these measures results not only in an especially low surface roughness with an average value of 0.2 micron, but also in a mechanical strength of at least 320 N/mm 2 and an in-line light transmission of more than 64%.
Inventors
- 👤 Heinrich Groh
- 👤 Reinhold Gradl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:16
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63404; C04B35/63416; B; B28; B28B; B28B3/00; B28B3/20; B28B3/26; C04B35/01; C04B35/10; C04B35/111; C04B35/115; C04B35/636; C04B35/6365; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
129 words
A process for producing polycrystalline, translucent sintered tubes, comprising the steps of: (a) preparing a water-soluble paste-like plasticizer mixture comprising: (1) an adhesive selected from the group consisting of polyvinyl alcohol adhesives, low-viscosity, weakly-swelling methylcellulose adhesives, and mixtures thereof, (2) at least one lubricant selected from the group consisting of fats and oils, (3) glycerol, and (4) a wetting agent; (b) mixing the plasticizer mixture from step (a) with aluminum oxide powder and water to form a homogeneous plasticizer mass; (c) cold forming the plasticized mass in an extrusion press to produce an unfired tubular body having a glossy surface and a density from about 50 to about 70% of the theoretical density of aluminum oxide; and (d) firing the extruded tubular body to a polycrystalline, translucent sintered tube.
Claim 2
Dependent Claim
129 words
A process for producing polycrystalline, translucent sintered tubes, comprising the steps of: (a) preparing a water-soluble paste-like plasticizer mixture comprising: (1) an adhesive selected from the group consisting of polyvinyl alcohol adhesives, low-viscosity, weakly-swelling methylcellulose adhesives, and mixtures thereof, (2) at least one lubricant selected from the group consisting of fats and oils, (3) glycerol, and (4) a wetting agent; (b) mixing the plasticizer mixture from step (a) with aluminum oxide powder and water to form a homogeneous plasticizer mass; (c) cold forming the plasticized mass in an extrusion press to produce an unfired tubular body having a glossy surface and a density from about 50 to about 70% of the theoretical density of aluminum oxide; and (d) firing the extruded tubular body to a polycrystalline, translucent sintered tube.
Claim 3
Dependent Claim
47 words
A process according to claim 1, wherein said firing step comprises the steps of: (ci) prefiring the extruded tubular body at temperatures from about 900° C. to about 1200° C.; and (cii) thereafter sintering the prefired body at temperatures from about 1750° C. to about 1900° C.
Claim 4
Dependent Claim
30 words
A process according to claim 1, wherein said aluminum oxide powder has a purity of at least about 99.5 percent and a grain size of less than about 1 micron.
Claim 5
Dependent Claim
76 words
A process according to claim 1, further comprising the steps of grinding the aluminum oxide powder in the presence of water and a fluidizing agent to produce an aqueous slurry of aluminum oxide, screening said slurry to remove coarse particles therefrom, adding glycerol and oil to said slurry, agitating the glycerol and oil containing slurry to incorporate air therein and produce a foamed mass, and drying said foamed mass at a temperature not exceeding 100° C.
Claim 6
Dependent Claim
41 words
A process according to claim 4, wherein a mixture of from about 0.1 to 0.5% by weight glycerol and from about 0.3 to 2.5% by weight oil in a proportion of from about 1:3 to 1:5 is added to said slurry.
Claim 7
Dependent Claim
76 words
A process according to claim 1, wherein said plasticized mass includes from about 11.2 to 19.5% by weight of said water-soluble, paste-like plasticizer mixture comprising from about 3 to 4.5% by weight PVA or low viscosity, weakly swelling methylcellulose adhesives, from about 5.5 to 8.5% by weight oils, from about 2 to 4.5% by weight fats, from about 0.5 to 1.5% by weight glycerol and from about 0.2 to 1% by weight of a wetting agent.
Claim 8
Dependent Claim
51 words
A process according to claim 6, wherein the chemical foundation of the polyvinyl alcohol adhesive consists of polymer hydroxyl compounds, that the fats are highly saturated, short chain fatty acids and that the oils consist of a mixture of naphthenic, paraffinic and aromatic hydrocarbons with natural fat derivatives and polar additives.
Claim 9
Dependent Claim
34 words
A process according to claim 2, wherein a constant sintering temperature is maintained for about two to five hours and the heating rate between 1200° and 1900° C. amounts to at least 800° C./hour.
Claim 10
Dependent Claim
60 words
A process according to claim 1, further comprising the addition to the aluminum oxide powder of magnesium oxide in an amount within a range of from about 0.03 to 0.08% by weight, and zirconium oxide within a range of from about 0.002 to 0.05% by weight, with said oxides being present in the preliminary step as chlorides, carbonates or acetates.
Claim 11
Dependent Claim
34 words
A process according to claim 7, wherein the magnesium oxide is added in an amount of about 0.05% by weight, and the zirconium oxide is added in an amount of about 0.01% by weight.
Claim 12
Dependent Claim
32 words
A process according to claim 4, wherein said fluidizing agent comprises sodium-free ammonia, and the grinding occurs in a disk mill wherein the milling disks consist of approximately 99.7% aluminum oxide ceramic.
Claim 13
Dependent Claim
44 words
A process according to claim 1, wherein the cold forming is effected by means of a piston press equipped with a low friction extrusion die and wherein the press is operated with a pressing pressure of from about 200 to 500 kg/cm 2 .
Claim 14
Dependent Claim
25 words
A process according to claim 2, wherein said prefiring takes place in an electric furnace with an oxidizing atmosphere for a period of 12 hours.
Claim 15
Dependent Claim
19 words
A process according to claim 1, wherein the firing takes place under vacuum or in a moist hydrogen atmosphere.
References Cited (Backward Citations)
US3026210A
Cited
US4020134A
Cited
US4169875A
Cited
GB2022564A
Cited
GB2071073A
Cited
DE3201750A1
Cited
US4396595A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-15 | 1990-06-16 | 1990-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-15 | 1994-06-16 | 1994-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-15 | 1998-06-16 | 1998-12-16 | $7700.00 | Window Closed / Lapsed |