Good aesthetic artificial dental materials by calcium phosphate glass-ceramic
Assignee: Krosaki Harima Corp
•
Filing: 1986-03-27
•
Granted: 1986-12-02
•
Expires: 2006-03-27
Abstract
Abstract Dental materials using calcium phosphate glass-ceramics and having the color tone with high approximation to that of natural teeth. In those dental materials, calcium phosphate composite, nickel oxide and one or more other type of compounds selected from oxides of iron, manganese, cerium, titanium and tungsten, are contained as coloring component. Also, if necessary, Al 2 O 3 and/or SiO 2 is contained as a color assisting agent in that composite. The calcium phosphate glass-ceramic according to this invention consists of the same components as that of natural teeth. Besides, it is possible to adjust the color tone delicately to match with the color tone of each individual`s teeth. Moreover, the coloring components are incorporated in crystals of calcium phosphate. Consequently, they cause no elution during use and are therefore ideal as dental material.
Inventors
- 👤 Akira Watanabe
- 👤 Yoshimitsu Takeuchi
- 👤 Hiroyasu Tokuda
- 👤 Seiji Kihara
- 👤 Yasuhiro Makino
- 👤 Keiji Kamegawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:56
CPC Classifications
A; A61; A61K; A61K6/00; A61K6/50; A61K6/58; A61K6/15; A61K6/16; A61K6/70; A61K6/71; A61K6/74; A61K6/75; A61K6/78; A61K6/80; A61K6/802; A61K6/822; A61K6/831; A61K6/833
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
90 words
Dental materials with calcium phosphate glass-ceramic consisting of: calcium phosphate composite with the atomic ratio of calcium to phosphorus Ca/P being 0.35-1.7; and a coloring component contained in said calcium phosphate composite, said coloring component being a mixture of nickel oxide and compounds selected from the group consisting of oxides of Fe, Mn, Ce, W, and Ti, the content of said coloring component is 0.3-5 wt. pt. against 100 wt. pt. of the calcium phosphate composite and the content of nickel oxide is 0.01-3.5 wt. pt. of said coloring component.
Claim 2
Dependent Claim
90 words
Dental materials with calcium phosphate glass-ceramic consisting of: calcium phosphate composite with the atomic ratio of calcium to phosphorus Ca/P being 0.35-1.7; and a coloring component contained in said calcium phosphate composite, said coloring component being a mixture of nickel oxide and compounds selected from the group consisting of oxides of Fe, Mn, Ce, W, and Ti, the content of said coloring component is 0.3-5 wt. pt. against 100 wt. pt. of the calcium phosphate composite and the content of nickel oxide is 0.01-3.5 wt. pt. of said coloring component.
Claim 3
Dependent Claim
117 words
Dental materials with calcium phosphate glass-ceramic consisting of: calcium phospate composite with the atomic ratio of calcium to phosphorus Ca/P being 0.35-1.7; a coloring component contained in said calcium phosphate composite, said coloring component being a mixture of nickel oxide and compounds selected from the group consisting of oxides of Fe, Mn, Ce, W and Ti, the content of said coloring component is 0.3-5 wt. pt. against 100 wt. pt. of the calcium phosphate composite; and a color assisting agent being selected from the group consisting of Al 2 O 3 and SiO 2 , wherein the content of said color assisting agent is less than 10 wt. pt. against 100 wt. pt. of calcium phosphate composite.
Claim 4
Dependent Claim
117 words
Dental materials with calcium phosphate glass-ceramic consisting of: calcium phospate composite with the atomic ratio of calcium to phosphorus Ca/P being 0.35-1.7; a coloring component contained in said calcium phosphate composite, said coloring component being a mixture of nickel oxide and compounds selected from the group consisting of oxides of Fe, Mn, Ce, W and Ti, the content of said coloring component is 0.3-5 wt. pt. against 100 wt. pt. of the calcium phosphate composite; and a color assisting agent being selected from the group consisting of Al 2 O 3 and SiO 2 , wherein the content of said color assisting agent is less than 10 wt. pt. against 100 wt. pt. of calcium phosphate composite.
References Cited (Backward Citations)
US4167417A
Cited
JPS5511625A
Cited
US4189325A
Cited
US4366253A
Cited
US4417912A
Cited
US4309485A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-01 | 1990-06-02 | 1990-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-01 | 1994-06-02 | 1994-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-01 | 1998-06-02 | 1998-12-02 | $7700.00 | Window Closed / Lapsed |