Process for producing ceramic body for surgical implantation
Assignee: Niterra Co Ltd
•
Filing: 1985-03-27
•
Granted: 1986-12-02
•
Expires: 2005-03-27
Abstract
Abstract A process for producing a ceramic body suitable for surgical implantation that has high strength and toughness and good compatibility with bone material. A porous material is provided by semi-sintering a ceramic compact. The pores in the surface of the porous material are filled with a first powder of either tricalcium phosphate or apatite or both, or with a material of the fine powder and a powder of a material substantially the same as the material of the ceramic compact. The porous material is then fired at the sintering temperature of the ceramic compact. Following sintering, the surface of the porous material is coated with a fine apatite powder or a finally pulverized mixture of apatite and a calcium phosphate base frit. The resulting assembly is then fired at a temperature up to about 1,350° C.
Inventors
- 👤 Kazuo Kondo
- 👤 Masahiko Okuyama
- 👤 Masakazu Watanabe
- 👤 Satoshi Iio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:54
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/40; A61L27/42; A61L27/427; C; C04; C04B; C04B35/00; C04B35/01; C04B35/447; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5076; C04B41/5092; C04B41/80; C04B41/81; C04B41/85; C04B2111/00; C04B2111/00474; C04B2111/00836
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
142 words
A process for producing a ceramic body for surgical implantation, comprising the steps of: providing a porous material by semi-sintering a ceramic compact of a ceramic material having a sintering temperature higher than the sintering temperature of apatite; filling pores in the surface of said porous material with a powder selected from the group consisting of a fine powder of at least one of tricalcium phosphate and apatite, and a mixture of said fine powder and a powder of said ceramic material; firing said porous material at the sintering temperature of said ceramic compact; coating the surface of said fired porous material with a material selected from the group consisting of (1) a fine apatite powder and (2) a finely pulverized mixture of apatite and a calcium phosphate base frit; and sintering the ceramic body at a temperature up to 1,350° C.
Claim 2
Dependent Claim
142 words
A process for producing a ceramic body for surgical implantation, comprising the steps of: providing a porous material by semi-sintering a ceramic compact of a ceramic material having a sintering temperature higher than the sintering temperature of apatite; filling pores in the surface of said porous material with a powder selected from the group consisting of a fine powder of at least one of tricalcium phosphate and apatite, and a mixture of said fine powder and a powder of said ceramic material; firing said porous material at the sintering temperature of said ceramic compact; coating the surface of said fired porous material with a material selected from the group consisting of (1) a fine apatite powder and (2) a finely pulverized mixture of apatite and a calcium phosphate base frit; and sintering the ceramic body at a temperature up to 1,350° C.
Claim 3
Dependent Claim
19 words
The process according to claim 1, wherein said ceramic compact is made of a partially stabilized zirconia ceramic material.
Claim 4
Dependent Claim
120 words
A process for producing a ceramic body for surgical implantation, comprising the steps of: providing a porous material by semi-sintering a ceramic compact of a ceramic material having a sintering temperature higher than the sintering temperature of apatite; impregnating the pores in the surface of the porous material with a calcium ion containing solution and a phosphate ion containing solution; firing said porous material at the sintering temperature of said ceramic compact; coating the surface of said first porous material with a material selected from the group consisting of (1) a fine apatite powder and (2) a finely divided mixture of apatite and a calcium phosphate base frit; and sintering the ceramic body at a temperature up to 1,350° C.
Claim 5
Dependent Claim
120 words
A process for producing a ceramic body for surgical implantation, comprising the steps of: providing a porous material by semi-sintering a ceramic compact of a ceramic material having a sintering temperature higher than the sintering temperature of apatite; impregnating the pores in the surface of the porous material with a calcium ion containing solution and a phosphate ion containing solution; firing said porous material at the sintering temperature of said ceramic compact; coating the surface of said first porous material with a material selected from the group consisting of (1) a fine apatite powder and (2) a finely divided mixture of apatite and a calcium phosphate base frit; and sintering the ceramic body at a temperature up to 1,350° C.
Claim 6
Dependent Claim
19 words
The process according to claim 3, wherein said ceramic compact is made of a partially stabilized zirconia ceramic material.
References Cited (Backward Citations)
DE2601550A1
Cited
JPS53118411A
Cited
FR2378733A1
Cited
US4308064A
Cited
US4376168A
Cited
JPS58126649A
Cited
US4560666A
Cited
US4525464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-01 | 1990-06-02 | 1990-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-01 | 1994-06-02 | 1994-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-01 | 1998-06-02 | 1998-12-02 | $7700.00 | Window Closed / Lapsed |