Elevated temperature comminution of vulcanized rubber and other elastomers
Assignee: NRI Pennsylvania Inc
•
Filing: 1985-01-04
•
Granted: 1986-12-02
•
Expires: 2005-01-04
Abstract
Abstract A slurry pump (40) pumps a slurry of vulcanized rubber pellets and water from a slurry mixing region (30) to a mill (B). The slurry passes through a comminuting zone (80) defined between an abrasive stator (66) and an abrasive rotor (76). As the slurry is comminuted in the comminuting zone, heat is generated, which heat is absorbed by at least the water. The comminuted rubber particles and water pass from the mill to a separator (C) which separates the rubber particles from the heated water. The heated water is conveyed to a hot water reservoir (24) from which it is recirculated to the slurry mixing region. Additional pellets from a pellet supply (10) are fed to the mixing region to be mixed with the recirculated heated water. In this manner, the slurry is preheated above room temperature prior to comminution. It has been found that increasing the water temperature to about 130° F. rather than using city water of about 55° F., increases the production rate of the mill by about 20 to 25 percent.
Inventors
- 👤 Ronald L. Brubaker
- 👤 Robert Calevich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:58
CPC Classifications
B; B02; B02C; B02C19/00; B02C19/0056; B02C23/00; B02C23/18; B02C7/00; B02C7/02; B29; B29B; B29B13/00; B29B13/10; Y; Y10; Y10S; Y10S241/00; Y10S241/31
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
198 words
A method of comminuting pellets to micron range particles, the method comprising: pumping a slurry of liquid and pellets to be comminuted to a comminuting zone defined between mating abrasive surfaces of a rotor and a stator; concurrently, rotating the rotor relative to the stator and pressing the rotor and stator abrasive surfaces together with a high pressure such that the rotor and stator shear the liquid as well as the pellets, energy expended to rotate the rotor and stator is in part utilized to comminute the pellets to micron range particles, is in part wasted shearing the liquid, is in part utilized by the rotor and stator mating abrasive surfaces wearing each other away, and in part heats the liquid and micron range particles to at least 130° F.; separating the micron range particles and the heated liquid; mixing the separated, heated liquid with additional pellets to be comminuted to form additional, heated slurry which is pumped to the comminuting zone, the heated liquid having a lower viscosity than cooler liquid such that less energy is wasted shearing the liquid during the rotating and pressing step, whereby recirculating heated liquid improves energy efficiency of the comminuting method.
Claim 2
Independent Claim
198 words
A method of comminuting pellets to micron range particles, the method comprising: pumping a slurry of liquid and pellets to be comminuted to a comminuting zone defined between mating abrasive surfaces of a rotor and a stator; concurrently, rotating the rotor relative to the stator and pressing the rotor and stator abrasive surfaces together with a high pressure such that the rotor and stator shear the liquid as well as the pellets, energy expended to rotate the rotor and stator is in part utilized to comminute the pellets to micron range particles, is in part wasted shearing the liquid, is in part utilized by the rotor and stator mating abrasive surfaces wearing each other away, and in part heats the liquid and micron range particles to at least 130° F.; separating the micron range particles and the heated liquid; mixing the separated, heated liquid with additional pellets to be comminuted to form additional, heated slurry which is pumped to the comminuting zone, the heated liquid having a lower viscosity than cooler liquid such that less energy is wasted shearing the liquid during the rotating and pressing step, whereby recirculating heated liquid improves energy efficiency of the comminuting method.
Claim 3
Dependent Claim
19 words
The comminuting method as set forth in claim 1 wherein the pellets include rubber and the fluid includes water.
Claim 4
Dependent Claim
15 words
The comminuting method as set forth in claim 2 wherein the rubber pellets are vulcanized.
Claim 5
Dependent Claim
26 words
The comminuting method as set forth in claim 2 wherein the entering water is heated to about a range of 80° F. to its boiling point.
Claim 6
Independent Claim
130 words
A method of comminuting elastomers, the method comprising: forming a slurry by mixing a liquid and pellets of an elastomer which with increasing temperature becomes increasingly more sticky and viscous and requires increasingly more energy to comminute than at lower temperatures; feeding the slurry to a comminuting zone defined between a rotor and a stator; concurrently rotating the rotor relative to the stator and pressing the rotor and stator together with a sufficiently high pressure to comminute the elastomer pellets to fine, elastomeric particles, to shear the liquid, and to heat the liquid and the fine particles; separating the heated liquid and the fine elastomeric particles; recirculating heat from the separated, heated liquid to the mixing step to increase the temperature of the formed by liquid and elastomeric pellet slurry.
Claim 7
Independent Claim
130 words
A method of comminuting elastomers, the method comprising: forming a slurry by mixing a liquid and pellets of an elastomer which with increasing temperature becomes increasingly more sticky and viscous and requires increasingly more energy to comminute than at lower temperatures; feeding the slurry to a comminuting zone defined between a rotor and a stator; concurrently rotating the rotor relative to the stator and pressing the rotor and stator together with a sufficiently high pressure to comminute the elastomer pellets to fine, elastomeric particles, to shear the liquid, and to heat the liquid and the fine particles; separating the heated liquid and the fine elastomeric particles; recirculating heat from the separated, heated liquid to the mixing step to increase the temperature of the formed by liquid and elastomeric pellet slurry.
Claim 8
Dependent Claim
34 words
The method as set forth in claim 5 wherein the recirculating step includes mixing the separated, heated liquid with additional elastomeric pellets to make heated, additional slurry to be fed to the comminuting zone.
Claim 9
Dependent Claim
14 words
The comminuting method as set forth in claim 6 wherein the pellets include rubber.
Claim 10
Dependent Claim
14 words
The comminuting method as set forth in claim 7 wherein the fluid includes water.
Claim 11
Dependent Claim
29 words
The comminuting method as set forth in claim 8 wherein the rotor and stator are constructed of bonded abrasive grits in the range of pb 20 to 100 mesh.
References Cited (Backward Citations)
US2560807A
Cited
US2211518A
Cited
US2909332A
Cited
US2833483A
Cited
DE2316389A1
Cited
US4383650A
Cited
US4394977A
Cited
US4469284A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-01 | 1990-06-02 | 1990-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-01 | 1994-06-02 | 1994-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-01 | 1998-06-02 | 1998-12-02 | $7700.00 | Window Closed / Lapsed |