Process for preparing uniformly sized polymer particles by suspension polymerization of vibratorily excited monomers in a gaseous or liquid stream
Assignee: Dow Chemical Co
•
Filing: 1984-08-23
•
Granted: 1986-11-18
•
Expires: 2004-08-23
Abstract
Abstract Spheroidal polymer beads having a uniform size are prepared by polymerizing uniformly sized monomer droplets formed by vibratory excitation of a laminar jet of monomeric material flowing in a gas phase. For example, a laminar jet of a monomer mixture comprising styrene, divinylbenzene and a polymerization initiator can be subjected to vibratory excitation and the resulting monomer droplets polymerized to yield copolymer beads having a narrow particle size range distribution. The copolymer beads can be employed in applications where beads having diameters of 5 μm to 100 μm are useful.
Inventors
- 👤 Edward E. Timm
- 👤 Douglas E. Leng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:05
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/18; C08F2/20; B; B01; B01J; B01J10/00; B01J10/002; B01J19/00; B01J19/0053; B01J19/0066; B01J19/26; B01J2/00; B01J2/02; B01J2/04; B01J2/06; B01J2/08; B01J2/18; B01J2219/00; B01J2219/00049; B01J2219/00164; Y; Y10; Y10S; Y10S526/00; Y10S526/918; Y10S526/92
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
155 words
A method for preparing small spheroidal polymer beads having a volume average particle diameter of about 5 μm to about 100 μm, said method comprising forming a monomer jet having laminar flow characteristics by flowing a vibratorily excited liquid monomer phase comprising a polymerizable monomer through an opening into a continuous gas phase under conditions sufficient to form a plurality of monomer droplets comprising the polymerizable monomer; said monomer droplets ranging in size from about 5 μm to about 100 μm, subsequently polymerizing said monomer droplets under conditions which do not cause significant coalescence or additional dispersion thereof by (a) polymerizing said droplets which are dispersed in said gas phase, or (b) dispersing said droplets into a continuous phase comprising a liquid immiscible with the polymerizable monomer phase and containing a stabilizing amount of suspending agent and subsequently polymerizing said droplets in suspension under conditions which do not cause significant coalescence or additional dispersion thereof.
Claim 2
Independent Claim
155 words
A method for preparing small spheroidal polymer beads having a volume average particle diameter of about 5 μm to about 100 μm, said method comprising forming a monomer jet having laminar flow characteristics by flowing a vibratorily excited liquid monomer phase comprising a polymerizable monomer through an opening into a continuous gas phase under conditions sufficient to form a plurality of monomer droplets comprising the polymerizable monomer; said monomer droplets ranging in size from about 5 μm to about 100 μm, subsequently polymerizing said monomer droplets under conditions which do not cause significant coalescence or additional dispersion thereof by (a) polymerizing said droplets which are dispersed in said gas phase, or (b) dispersing said droplets into a continuous phase comprising a liquid immiscible with the polymerizable monomer phase and containing a stabilizing amount of suspending agent and subsequently polymerizing said droplets in suspension under conditions which do not cause significant coalescence or additional dispersion thereof.
Claim 3
Dependent Claim
40 words
A method of claim 1 wherein the beads so prepared have a particle size such that about 90 volume percent thereof possess a particle diameter from about 0.95 to about 1.05 times the volume average particle diameter of the particles.
Claim 4
Dependent Claim
18 words
A method of claim 1 wherein polymerization is effected in said gas phase by employing a cationic catalyst.
Claim 5
Dependent Claim
23 words
A method of claim 1 wherein the monomer droplets exhibit a particle size distribution having a coefficient of variance of less than 0.1.
Claim 6
Dependent Claim
46 words
A method of claim 1 wherein the flow characteristics of the monomer jet is defined by a Reynold's number from about 1 to about 2,000 and the vibratory excitation of the monomer jet is defined by a Strouhal number of from about 0.05 to about 5.
Claim 7
Dependent Claim
33 words
A method of claim 5 wherein the monomer jet is formed by flowing the monomer phase through a passage having an opening with a diameter from about 1 μm to about 50 μm.
Claim 8
Dependent Claim
15 words
A method of claim 1 wherein said polymerizable monomer is a suspension polymerizable, water-insoluble monomer.
Claim 9
Dependent Claim
36 words
A method of claim 7 wherein said water-insoluble monomer is a monovinylidene aromatic, a polyvinylidene aromatic, a halo-olefin, an ester of an α-β-ethylenically unsaturated carboxylic acid, or a mixture of two or more of said monomers.
Claim 10
Dependent Claim
18 words
A method of claim 6 wherein polymerization is affected in said gas phase by employing a cationic catalyst.
Claim 11
Dependent Claim
25 words
A method of claim 1 wherein the polymer beads so prepared have a volume average particle diameter of about 5 μm to about 50 μm.
Claim 12
Dependent Claim
25 words
A method of claim 1 wherein the polymer beads so prepared have a volume average particle diameter of about 5 μm to about 25 μm.
Claim 13
Dependent Claim
25 words
A method of claim 9 wherein the polymer beads so prepared have a volume average particle diameter of about 5 μm to about 50 μm.
Claim 14
Dependent Claim
15 words
A method of claim 1 wherein said monomer droplet falls downward through said gas phase.
Claim 15
Dependent Claim
13 words
A method of claim 1 wherein polymerization is performed in said gas phase.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-17 | 1990-05-19 | 1990-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-17 | 1994-05-19 | 1994-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-17 | 1998-05-19 | 1998-11-18 | $7700.00 | Window Closed / Lapsed |