Assignee: SKW Metals UK Ltd
•
Filing: 1985-11-12
•
Granted: 1986-11-11
•
Expires: 2005-11-12
Abstract
Abstract The present invention provides a molybdenum alloy which suitably comprises in the range of from 0.2 to 1.0% by weight of an oxide of a specified metal prepared by adding a salt of the metal in dissolved form to molybdenum and/or a molybdenum oxide or a mixture of different molybdenum components, reducing this mixture at a temperature of up to 1150° C. using hydrogen, pressing the reduced metal without the addition of a binder suitably under a pressure of from 150 to 300 mPA, and sintering the product at a temperature in the range of from 1750° to 2200° C. It is preferable to add salts of zirconium to the molybdenum oxide.
Inventors
- 👤 Charles E. D. Rowe
- 👤 George R. Hinch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:25
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; C22C1/045; C22C27/00; C22C27/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
126 words
A process for the preparation of a sintered molybdenum alloy which comprises the steps of blending molybdenum and/or a molybdenum oxide with a solution of a salt of a metal which solution under the conditions of the process gives rise to and oxide of the metal without further decompostion or permanent alteration from the solid phase subjecting the mixture, after, if necessary, drying, crushing, and screening,to a reducing hydrogen atmosphere at a temperature not greater than 1150° C., further processing to form a shaped article by techniques known for processing powdered molybdenum, and sintering under a hydrogen atmosphere at a temperature in the range of from 1750° C. to 2200° C., without the addition of carbon or a carbon-containing compound at any stage in the process.
Claim 2
Dependent Claim
126 words
A process for the preparation of a sintered molybdenum alloy which comprises the steps of blending molybdenum and/or a molybdenum oxide with a solution of a salt of a metal which solution under the conditions of the process gives rise to and oxide of the metal without further decompostion or permanent alteration from the solid phase subjecting the mixture, after, if necessary, drying, crushing, and screening,to a reducing hydrogen atmosphere at a temperature not greater than 1150° C., further processing to form a shaped article by techniques known for processing powdered molybdenum, and sintering under a hydrogen atmosphere at a temperature in the range of from 1750° C. to 2200° C., without the addition of carbon or a carbon-containing compound at any stage in the process.
Claim 3
Dependent Claim
33 words
A process as claimed in claim 1, wherein the solution of a metal salt is sprayed onto the molybdenum and/or molybdenum oxide and blended in a suitable mixer to give a moist mixture.
Claim 4
Dependent Claim
21 words
A process as claimed in 1 or claim 2, wherein molybdenum dioxide or molybdenum trioxide or a mixture thereof is used.
Claim 5
Dependent Claim
47 words
A process as claimed in any one of claims 1 to 3, wherein the amount of metal salt used is such that the alloy prepared contains in the range of from 0.2 to 1.0% by weight of an oxide of the metal in the resulting prepared alloy.
Claim 6
Dependent Claim
37 words
A process as claimed in claim 4, wherein the amount of metal salt used is such that the alloy prepared contains in the range of from 0.25 to 0.6% by weight of an oxide of the metal.
Claim 7
Dependent Claim
48 words
A process as claimed in any one of claims 1 to 5, wherein the salt used is a salt of a metal selected from aluminium, barium, calcium, cerium, chromium, hafnium, magnesium, silicon, strontium, thorium, yttrium, and zirconium, or a mixture of two or more such salts is used.
Claim 8
Dependent Claim
28 words
A process as claimed in claim 6, wherein a salt of aluminium, chromium, hafnium, titanium, or zirconium, or a mixture of two or more such salts is used.
Claim 9
Dependent Claim
14 words
A process as claimed in claim 7, wherein a salt of zirconium is used.
Claim 10
Dependent Claim
23 words
A process as claimed in any one of claims 6 to 8, wherein the salt is a chloride, iodide, sulphate, or nitrate salt.
Claim 11
Dependent Claim
13 words
A process as claimed in claim 9, wherein the salt is zirconium nitrate.
Claim 12
Dependent Claim
22 words
A process as claimed in claim 1 which further comprises drying, crushing, and/or screening the mixture prior to the hydrogen reducing step.
Claim 13
Dependent Claim
25 words
A process as claimed in any one of claims 1 to 11, wherein the further processing is carried out in the absence of a binder.
Claim 14
Dependent Claim
29 words
A process as claimed in any one of claims 1 to 12, wherein the sintering is carried out under a hydrogen atmosphere at atmospheric pressure or a reduced pressure.
Claim 15
Dependent Claim
17 words
A molybdenum alloy prepared by a process as claimed in any one of claims 1 to 12.
Claim 16
Dependent Claim
28 words
A molybdenum alloy as claimed in claim 14, which comprises molybdenum and in the range of from 0.2 to 1% by weight of an oxide of a metal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-10 | 1990-05-12 | 1990-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-10 | 1994-05-12 | 1994-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-10 | 1998-05-12 | 1998-11-11 | $7700.00 | Window Closed / Lapsed |