Polyester fibers
Assignee: Teijin Ltd
•
Filing: 1985-04-12
•
Granted: 1986-11-04
•
Expires: 2005-04-12
Abstract
Abstract A papermaking polyester fiber having a denier number within the range of from about 0.1 to about 3.0 and a length within the range of from about 5 mm to about 25 mm and providing a packing factor of more than about 40 and a quantity of residual fibers of less than about 1000 mg on a flat screen plate when measured by a flat screen method.
Inventors
- 👤 Mikio Tashiro
- 👤 Kou Tsukiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:16
CPC Classifications
D; D21; D21H; D21H13/00; D21H13/10; D21H13/20; D21H13/24; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2904; Y10T428/2907; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/298
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
204 words
A paper making polyester fiber, the improvement comprising that the papermaking polyester fiber comprises a copolymer containing a dicarboxylic acid component and has applied to the surface thereof a copolymerized polyester (I) which consists of (A) a polyester comprising terephthalic acid or an ester-forming derivative of terephthalic acid, isophthalic acid or an ester-forming derivative of isophthalic acid and a lower alkylene glycol (b) about 0.2 mol percent to about 40 mol percent, with respect to the quantity of the dicarboxylic acid component in the copolymer to be produced, of an ester-forming alkali metal sulfonate and (c) about 20 percent by weight to about 90 percent by weight, with respect to the quantity of the copolymer to be produced, of a polyethylene glycol having an average molecular weight within the range of from about 500 to 1200, wherein the paper making polyester fiber has a denier number within the range of from about 0.1 to about 3.0 and a length within the range from about 5 mm to about 25 mm, and provides a packing factor of more than about 40 and a quantity of residual fibers of less than about 1000 mg on a flat screen plate when measured by the flat screen method.
Claim 2
Dependent Claim
204 words
A paper making polyester fiber, the improvement comprising that the papermaking polyester fiber comprises a copolymer containing a dicarboxylic acid component and has applied to the surface thereof a copolymerized polyester (I) which consists of (A) a polyester comprising terephthalic acid or an ester-forming derivative of terephthalic acid, isophthalic acid or an ester-forming derivative of isophthalic acid and a lower alkylene glycol (b) about 0.2 mol percent to about 40 mol percent, with respect to the quantity of the dicarboxylic acid component in the copolymer to be produced, of an ester-forming alkali metal sulfonate and (c) about 20 percent by weight to about 90 percent by weight, with respect to the quantity of the copolymer to be produced, of a polyethylene glycol having an average molecular weight within the range of from about 500 to 1200, wherein the paper making polyester fiber has a denier number within the range of from about 0.1 to about 3.0 and a length within the range from about 5 mm to about 25 mm, and provides a packing factor of more than about 40 and a quantity of residual fibers of less than about 1000 mg on a flat screen plate when measured by the flat screen method.
Claim 3
Dependent Claim
31 words
A papermaking polyester fiber as set forth in claim 1, the improvement further comprising that said quantity of residual fibers on a flat screen plate is less than about 500 mg.
Claim 4
Dependent Claim
31 words
A papermaking polyester fiber as set forth in claim 1, the improvement further comprising that said quantity of residual fibers on a flat screen plate is less than about 300 mg.
Claim 5
Dependent Claim
19 words
A papermaking polyester fiber as set forth in claim 1, wherein said packing factor is more than about 45.
Claim 6
Dependent Claim
33 words
A papermaking polester fiber as set forth in claim 1, 2, 3 or 4, wherein said fiber is selected from the group consisting of fibers of polyethylene terephthalate, polyethylene terephthalate/isophthalate and polybutylene terephthalate.
Claim 7
Dependent Claim
48 words
A papermaking polyester fiber as set forth in claim 1, the improvement further comprising that the quantity of said copolymerized polyester (I) to be deposited on the polyester fiber is within the range of from about 0.01 per cent by weight to about 2 per cent by weight.
Claim 8
Dependent Claim
74 words
A papermaking polyester fiber as set forth in claim 1, the improvement further comprising that said copolymerized polyester (I) is applied to the polyester fiber in the form of a mixture with a second copolymerized polyester (II) comprising terephthalic acid or an ester-forming derivative of the terephthalic acid, isophthalic acid or an ester-forming derivative of the isophthalic acid, a lower polyalkylene glycol, and one or both of a polyalkylene glycol and a monoether thereof.
Claim 9
Dependent Claim
59 words
A papermaking polyester fiber as set forth in claim 7, the improvement further comprising that the quantities of the first and second copolymerized polyesters (I) and (II) in said mixture are selected so that the quantity of the first copolymerized polyester (I) accounts for about 20 per cent by weight or more of the total quantity of the mixture.
Claim 10
Dependent Claim
49 words
A papermaking polyester fiber as set forth in claim 7, the improvement further comprising that the ratio between terephthalic acid or the ester-forming derivative thereof and isophthalic acid or the ester-forming derivative thereof in said copolymerized polyester (II) be within the range of from about 95:5 to about 50:50.
Claim 11
Dependent Claim
53 words
A papermaking polyester fiber as set forth in claim 7, the improvement further comprising that the quantity of said mixture of the copolymerized polyesters (I) and (II) to be deposited on the polyester fiber is within the range of from about 0.01 per cent by weight to about 2 per cent by weight.
References Cited (Backward Citations)
US2905585A
Cited
US3498821A
Cited
US3528947A
Cited
US3546008A
Cited
US3702260A
Cited
US3730830A
Cited
US4156073A
Cited
US4496583A
Cited
US4483976A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-03 | 1990-05-05 | 1990-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-03 | 1994-05-05 | 1994-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-03 | 1998-05-05 | 1998-11-04 | $7700.00 | Window Closed / Lapsed |