Process for cracking with silica-alumina
Assignee: Phillips Petroleum Co
•
Filing: 1985-05-20
•
Granted: 1986-10-14
•
Expires: 2005-05-20
Abstract
Abstract A process for preparing silica-alumina compositions suitable as catalyst material comprises mixing a first aqueous solution containing an aluminum salt (preferably KAl(SO 4 ) 2 ) and an ammonium salt (preferably (NH 4 ) 2 SO 4 ) with a second solution containing an alkali metal silicate (preferably Na 2 SiO 3 ), wherein the concentration of the ammonium salt is chosen so as to afford coprecipitation of silica-alumina hydrogel (preferably at a pH of about 3-6). The silica-alumina hydrogel is then separated, optionally dried, and calcined. Calcined silica-alumina can be employed as cracking catalysts or as supports for hydrofining/hydrocracking catalysts.
Inventors
- 👤 Yen-Shin Shyr
- 👤 Marvin M. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 15:18
CPC Classifications
C; C10; C10G; C10G49/00; C10G49/02; B; B01; B01J; B01J21/00; B01J21/12; B01J37/00; B01J37/02; B01J37/03; C10G11/00; C10G11/02; C10G11/04
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
162 words
A process for cracking a hydrocarbon containing feed stream comprising the step of contacting said feed stream with a silica-alumina catalyst composition under such conditions as to produce hydrocarbon products having lower boiling ranges than said feed stream, wherein said silica-alumina composition is prepared by a method comprising the steps of (A) mixing a first aqueous solution containing an aluminum salt and an ammonium salt of an acid having a pKa of less than 2 with a second aqueous solution containing an alkali metal silicate, wherein the mol ratio of the alkali metal silicate to the aluminum salt is in the range of from about 2:1 to about 20:1 and the amount of the ammonium salt in said first solution is such that a coprecipitated silica-alumina hydrogel is formed after said mixing; (B) separating the coprecipitated silica-alumina hydrogel from the mixture of said two solutions; (C) calcining said hydrogel under such conditions as will result in the formation of an acidic silica-alumina.
Claim 2
Dependent Claim
162 words
A process for cracking a hydrocarbon containing feed stream comprising the step of contacting said feed stream with a silica-alumina catalyst composition under such conditions as to produce hydrocarbon products having lower boiling ranges than said feed stream, wherein said silica-alumina composition is prepared by a method comprising the steps of (A) mixing a first aqueous solution containing an aluminum salt and an ammonium salt of an acid having a pKa of less than 2 with a second aqueous solution containing an alkali metal silicate, wherein the mol ratio of the alkali metal silicate to the aluminum salt is in the range of from about 2:1 to about 20:1 and the amount of the ammonium salt in said first solution is such that a coprecipitated silica-alumina hydrogel is formed after said mixing; (B) separating the coprecipitated silica-alumina hydrogel from the mixture of said two solutions; (C) calcining said hydrogel under such conditions as will result in the formation of an acidic silica-alumina.
Claim 3
Dependent Claim
30 words
A process in accordance with claim 1, wherein wherein the aluminum salt is potassium aluminum sulfate, the ammonium salt is ammonium sulfate, and the alkali metal silicate is sodium silicate.
Claim 4
Dependent Claim
81 words
A process in accordance with claim 1, wherein said contacting is carried out in the presence of hydrogen, and said preparation method further comprises the steps of (E) impregnating said calcined silica-alumina with a solution containing at least one compound of at least one transition metal selected from metals belonging to Groups VB, VIB, VIIB, VIII and IB of the Periodic Table, and (F) calcining said impregnated silica-alumina composition under such conditions as to convert said metal compounds to metal oxides.
Claim 5
Dependent Claim
52 words
A process in accordance with claim 1, wherein said acidic silica-alumina has a Si:Al mol ratio ranging from about 2:1 to about 10:1, a surface area ranging from about 200 m 2 /g to about 500 m 2 /g and a pore volume ranging from about 0.3 cc/g to about 0.8 cc/g.
Claim 6
Dependent Claim
52 words
A process in accordance with claim 2, wherein the concentration of potassium aluminum sulfate ranges from about 0.1 mol/l to about 0.5 mol/l, the concentration of ammonium sulfate ranges from about 0.1 mol/l to about 0.5 mol/l, and the concentration of sodium silicate ranges from about 0.1 mol/l to about 1 mol/l.
Claim 7
Dependent Claim
69 words
A process in accordance with claim 3, wherein said at least one transition metal is selected from the group consisting of molybdenum and nickel, and said contacting is carried out at a temperature ranging from about 700° to about 900° F., a hydrogen pressure ranging from about 500 to about 5000 psig, and a liquid hourly space velocity ranging from about 0.2 to about 3 volume feed oil/volume catalyst/hour.
References Cited (Backward Citations)
US2146718A
Cited
US2437533A
Cited
US2565886A
Cited
US2908635A
Cited
US2844523A
Cited
US2886511A
Cited
US3210293A
Cited
US3274124A
Cited
US3346509A
Cited
US3905916A
Cited
US3912619A
Cited
US4097365A
Cited
US4142995A
Cited
US4239651A
Cited
US4289653A
Cited
US4247420A
Cited
US4380509A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-13 | 1990-04-14 | 1990-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-13 | 1994-04-14 | 1994-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-13 | 1998-04-14 | 1998-10-14 | $7700.00 | Window Closed / Lapsed |