Fast response, high rate, gas diffusion electrode and method of making same
Assignee: Eltech Systems Corp
•
Filing: 1984-09-27
•
Granted: 1986-10-07
•
Expires: 2004-09-27
Abstract
Abstract Disclosed are gas fed, porous electrodes capable of steady, high current density operation for practical periods of service, e.g. as oxygen cathodes in metal-air batteries. The subject electrodes feature at least two bonded composite layers, one of which is a form-stable, conductive wetproofing layer while the other is an unusually thin active layer containing active carbon particles predominantly between about 2 and about 20 micrometers and having a high internal surface area, e.g. a B.E.T. surface area of over 1000 m2/gram. A simple and highly successful method of preparing such electrodes is also disclosed, which avoids the necessity of separately forming and handling the thin active layer.
Inventors
- 👤 Frank Solomon
- 👤 Charles Grun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:57
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9008; H01M4/96; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
116 words
A fast response, high current density oxygen cathode comprising: a form-stable, electrically conductive, wetproofing layer composed essentially of an intimate, consolidated and heat sintered mixture of carbon black and particulate hydrophobic polymeric binder derived predominantly from tetrafluoroethylene, having at least one anisometric electroconductive reinforcing material incorporated therein; and, directly adhered to one surface of said wetproofing layer, a porous active layer having a thickness between about 0.03 and about 0.1 millimeter and composed essentially of a mixture of particles of a polymer of tetrafluoroethylene and cobalt catalyst-containing particles of an active carbon predominantly of a size between about 2 and about 20 micrometers and having a B.E.T. surface area of over about 1000 m 2 /gram.
Claim 2
Dependent Claim
116 words
A fast response, high current density oxygen cathode comprising: a form-stable, electrically conductive, wetproofing layer composed essentially of an intimate, consolidated and heat sintered mixture of carbon black and particulate hydrophobic polymeric binder derived predominantly from tetrafluoroethylene, having at least one anisometric electroconductive reinforcing material incorporated therein; and, directly adhered to one surface of said wetproofing layer, a porous active layer having a thickness between about 0.03 and about 0.1 millimeter and composed essentially of a mixture of particles of a polymer of tetrafluoroethylene and cobalt catalyst-containing particles of an active carbon predominantly of a size between about 2 and about 20 micrometers and having a B.E.T. surface area of over about 1000 m 2 /gram.
Claim 3
Dependent Claim
33 words
An oxygen cathode as in claim 1 wherein said reinforcing material comprises at least one coextensive layer of fine mesh or gauze having a thickness of between about 50 and about 200 micrometers.
Claim 4
Dependent Claim
18 words
An oxygen cathode as in claim 1 wherein said reinforcing material comprises short, chopped fibers of fine denier.
Claim 5
Dependent Claim
28 words
An oxygen cathode as in claim 3 wherein said fibers are between about 1 and about 10 millimeters in length and about 5 to 100 micrometers in diameter.
Claim 6
Dependent Claim
14 words
An oxygen cathode as in claim 4 wherein said fibers are carbon or graphite.
Claim 7
Dependent Claim
22 words
An oxygen cathode as in claim 1 wherein said carbon black has a particle size between about 50 and about 3000 Angstroms.
Claim 8
Dependent Claim
16 words
An oxygen cathode as in claim 6 wherein said carbon black is an acetylene carbon black.
Claim 9
Dependent Claim
33 words
An oxygen cathode as in claim 1 wherein said cobalt catalyst-containing particles of active carbon contain between about 5% and about 25% by weight of a cobalt effective in promoting reduction of oxygen.
Claim 10
Dependent Claim
17 words
An oxygen cathode as in claim 8 wherein said catalyst is a macrocyclic organic compound of cobalt.
Claim 11
Dependent Claim
24 words
An oxygen cathode as in claim 9 wherein said catalyst is cobalt tetramethoxyphenylporphyrin (which is heat treated after being deposited on said active carbon).
Claim 12
Dependent Claim
22 words
An oxygen cathode as in claim 1 wherein the thickness of said active layer is between about 50 and about 80 micrometers.
Claim 13
Dependent Claim
22 words
An oxygen cathode as in claim 1 wherein polytetrafluoroethylene is the predominant polymeric constituent in both the wetproofing and the active layers.
Claim 14
Dependent Claim
27 words
An oxygen cathode as in claim 1 wherein a thin outer layer of submicron sized silver particles is deposited on the exposed face of said active layer.
Claim 15
Dependent Claim
19 words
An oxygen cathode as in claim 13 wherein said layer of silver particles is thinner than said active layer.
Claim 16
Dependent Claim
24 words
An oxygen cathode as in claim 1 wherein said active carbon particles are predominantly in the range between about 5 and about 10 micrometers.
Claim 17
Dependent Claim
16 words
An oxygen cathode as in claim 1 wherein said wetproofing layer is thicker than 0.1 millimeter.
Claim 18
Dependent Claim
81 words
An oxygen cathode as in claim 1 wherein said reinforcing material is fibrous and it accounts for between about 3% and about 25% of the combined weight of carbon black and binder and the weight proportion of carbon black to hydrophobic polymeric binder therein is between about 3 to 2 and about 4 to 1, while the weight proportion of catalyzed active carbon to polymer particles in said active layer is between about 7 to 3 and about 9 to 1.
Claim 19
Dependent Claim
15 words
An oxygen cathode as in claim 1 wherein said active layer is also heat sintered.
Claim 20
Dependent Claim
12 words
A metal-air battery contining an oxygen cathode as defined in claim 1.
References Cited (Backward Citations)
US3385780A
Cited
US3553022A
Cited
US3462307A
Cited
US3668014A
Cited
US4362790A
Cited
US4255498A
Cited
US4357262A
Cited
US4337139A
Cited
US4440617A
Cited
US4456521A
Cited
US4459197A
Cited
US4468362A
Cited
US4447505A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |