Solid particle erosion resistant coating utilizing titanium carbide, process for applying and article coated therewith
Assignee: General Electric Co
•
Filing: 1985-02-07
•
Granted: 1986-10-07
•
Expires: 2005-02-07
Abstract
Abstract A solid particle erosion resistant coating includes angular titanium carbide particles uniformly dispersed through a high chromium iron matrix. In one form, the aggregate comprises, by weight, about 30-50% TiC, about 10-30% Cr, about 1.5-5% C and the balance essentially iron in the form of ferrite. The matrix also includes metallurgically identifiable amounts of high chromium content M 7 C 3 carbides therethrough. The coating does not exhibit austenitic or martensitic structure therehthough. A powder alloy consolidated body also includes a surface adjacent region having a similar TiC and high chromium iron matrix. Further, a method for obtaining the coating includes heating above the austenitization temperature of the matrix alloy and below the melting temperature of iron, and cooling the aggregate so as to attain iron in the form of ferrite in the matrix.
Inventors
- 👤 Donald R. Spriggs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:35
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0292; B; B22; B22F; B22F3/00; B22F3/12; B22F3/14; B22F3/15; C23; C23C; C23C24/00; C23C24/08; C23C24/082; C23C30/00; C23C30/005
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
44 words
A composition of matter comprising by weight about 30% to about 50% angular titantium carbide particles dispersed in a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron.
Claim 2
Dependent Claim
44 words
A composition of matter comprising by weight about 30% to about 50% angular titantium carbide particles dispersed in a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron.
Claim 3
Dependent Claim
15 words
The composition as in claim 1, wherein the iron is in the form of ferrite.
Claim 4
Dependent Claim
26 words
The composition as in claim 2, wherein the weight fraction ratio of chromium to carbon in the matrix alloy is between about 4:1 to about 10:1.
Claim 5
Dependent Claim
22 words
The composition as in claim 2 wherein the weight fraction ratio of chromium to carbon in the matrix alloy is about 8:1.
Claim 6
Dependent Claim
46 words
The composition as in claim 2 including chromium carbides selected from the group consisting of Cr 7 C 3 and Cr x A y C 3 , wherein A is selected from the group consisting of iron, cobalt, nickel, tungsten and molybdenum, and x+y equals seven.
Claim 7
Dependent Claim
19 words
The composition as in claim 1, including by weight about 35 to about 45 percent angular titanium carbide particles.
Claim 8
Dependent Claim
31 words
The composition as in claim 6, wherein the matrix alloy further includes by weight about 25% to about 30% chromium, about 2.8% to about 3.2% carbon and the balance essentially iron.
Claim 9
Dependent Claim
20 words
The composition as in claim 1 wherein the angular titanium carbide particles are unalloyed with other constituents of the composition.
Claim 10
Dependent Claim
42 words
The composition as in claim 1, wherein said matrix includes metallurgically identifiable amounts of high chromium content M 7 C 3 carbides, wherein M represents the total of iron and chromium atoms which are bonded to carbon in the ratio of 7:3.
Claim 11
Dependent Claim
18 words
The composition as in claim 1, wherein said titanium carbide particles are substantially uniformly dispersed through said matrix.
Claim 12
Independent Claim
94 words
A method for producing a solid particle erosion and oxidation resistant material, comprising: consolidating angular titanium carbide and a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron, at a temperature above the austenitization temperature of the matrix alloy and below the melting temperature of iron in an inert atmosphere at a pressure of about 10 to about 20 ksi; and cooling the resulting consolidated composition at a rate such that the iron will attain a ferrite configuration.
Claim 13
Independent Claim
94 words
A method for producing a solid particle erosion and oxidation resistant material, comprising: consolidating angular titanium carbide and a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron, at a temperature above the austenitization temperature of the matrix alloy and below the melting temperature of iron in an inert atmosphere at a pressure of about 10 to about 20 ksi; and cooling the resulting consolidated composition at a rate such that the iron will attain a ferrite configuration.
Claim 14
Dependent Claim
21 words
The method as in claim 11, wherein the step of consolidation further includes consolidating at a temperature above about 2000° F.
Claim 15
Dependent Claim
25 words
The method as in claim 12, wherein the step of consolidating further includes consolidating at a temperature of about 2150° F. to about 2250° F.
Claim 16
Dependent Claim
21 words
The method as in claim 13 wherein the step of consolidating further includes consolidating at a temperature of about 2200° F.
Claim 17
Dependent Claim
21 words
The method as in claim 11 wherein the step of consolidating further includes consolidating at a pressure of about 15 ksi.
Claim 18
Dependent Claim
25 words
The method as in claim 15 wherein the step of consolidating further includes consolidating at a temperature of about 2150° F. to about 2250° F.
Claim 19
Dependent Claim
73 words
The method as in claim 11 wherein the weight fraction ratio of chromium to carbon in the matrix alloy is between about 4:1 to about 10:1 and the step of consolidating further includes forming chromium carbides selected from the group consisting of Cr 7 C 3 and Cr x A y C 3 , wherein A is selected from the group consisting of iron, nickel, cobalt, tungsten and molybdenum, and x+y equals seven.
Claim 20
Dependent Claim
22 words
The method as in claim 17, wherein the weight fraction ratio of chromium to carbon in the matrix alloy is about 8:1.
Claim 21
Dependent Claim
26 words
The method as in claim 11 wherein the step of consolidating further includes inhibiting alloy formation between the titanium carbide and other constituents of said material.
Claim 22
Dependent Claim
24 words
The method as in claim 11 wherein the step of cooling includes cooling at a rate not greater than about 8° C. per minute.
Claim 23
Dependent Claim
25 words
The method as in claim 20 wherein the step of cooling further includes cooling at a rate not greater than about 5° C. per minute.
Claim 24
Dependent Claim
129 words
A composition of matter comprising by weight about 30% to about 50% titanium carbide particles dispersed in a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron, wherein the iron is substantially in the form of ferrite and the matrix alloy includes M 7 C 3 carbides, wherein M represents the total of iron and chromium atoms which are bonded to carbon in the ratio of 7:3 and further wherein the matrix alloy includes chromium carbides selected from the group consisting of Cr 7 C 3 and Cr x A y C 3 , wherein A is selected from the group consisting of iron, cobalt, nickel, tungsten and molybdenum, and x+y equals seven.
Claim 25
Dependent Claim
129 words
A composition of matter comprising by weight about 30% to about 50% titanium carbide particles dispersed in a matrix alloy, the matrix alloy including by weight about 10% to about 30% chromium, about 1.5% to about 5% carbon and the balance essentially iron, wherein the iron is substantially in the form of ferrite and the matrix alloy includes M 7 C 3 carbides, wherein M represents the total of iron and chromium atoms which are bonded to carbon in the ratio of 7:3 and further wherein the matrix alloy includes chromium carbides selected from the group consisting of Cr 7 C 3 and Cr x A y C 3 , wherein A is selected from the group consisting of iron, cobalt, nickel, tungsten and molybdenum, and x+y equals seven.
Claim 26
Dependent Claim
17 words
The composition as in claim 22, wherein titanium carbide is in the form of angular titanium carbide.
Claim 27
Dependent Claim
26 words
The composition as in claim 23, wherein the weight fraction ratio of chromium to carbon in the matrix alloy is between about 4:1 to about 10:1.
Claim 28
Dependent Claim
18 words
The composition as in claim 22, wherein the titanium carbide is unalloyed with other constituents of the composition.
Claim 29
Dependent Claim
18 words
The composition as in claim 22, wherein said titanium carbide particles are substantially uniformly dispersed through said matrix.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |