Process for the production of porous products made from boron or boron compounds
Assignee: Commissariat à l'Énergie Atomique et Aux Énergies Alternatives
•
Filing: 1985-04-24
•
Granted: 1986-09-30
•
Expires: 2005-04-24
Abstract
Abstract The invention relates to a process for the production of porous products of boron or boron compounds. This process comprises the following stages: (1) suspending the boron powder in a solution of an alkali metal salt, hydroxide and/or oxide, (2) then separating the powder from the suspension liquid by settling, (3) drying the thus separated powder to obtain an agglomerated powder, and (4) subjecting the thus obtained agglomerated powder to at least two heat treatments performed at different temperatures, the final stage of the heat treatment being performed at a temperature of 1500 DEG to 2200 DEG C. and the first stage being performed at a temperature below that of the final stage. The heat treatment can be performed in three stages, as shown in the attached graph.
Inventors
- 👤 Marcel Boncoeur
- 👤 Bernard Hansz
- 👤 Thierry Lieven
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 14:28
CPC Classifications
C; C01; C01B; C01B35/00; C01B35/02; C01B35/023; C01B35/04
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
101 words
A process for the production of porous boron products comprising successively the following stages: (1) suspending the boron powder in a solution of an alkali metal salt, hydroxide and/or oxide, (2) then separating the powderfrom the suspension liquid by settling, (3) drying the thus separated powder to obtain an agglomerated powder, and (4) subjecting the thus obtained agglomerated powder to at least two heat treatments performed at different temperatures, the final stage of the heat treatment being performed at a temperature of 1500° to 2200° C. and the first stage being performed at a temperature below that of the final stage.
Claim 2
Dependent Claim
101 words
A process for the production of porous boron products comprising successively the following stages: (1) suspending the boron powder in a solution of an alkali metal salt, hydroxide and/or oxide, (2) then separating the powderfrom the suspension liquid by settling, (3) drying the thus separated powder to obtain an agglomerated powder, and (4) subjecting the thus obtained agglomerated powder to at least two heat treatments performed at different temperatures, the final stage of the heat treatment being performed at a temperature of 1500° to 2200° C. and the first stage being performed at a temperature below that of the final stage.
Claim 3
Dependent Claim
135 words
A process for the production of porous products of a boride of a metal M or a metalloid, wherein it successively comprises the following stages: (1) suspending, accompanied by stirring, the boron powder and the powder of an oxide of metal M or an oxide of the metalloid in a solution of an alkali metal salt, oxide and/or hydroxide, (2) then separating the powder mixture from the suspension liquid by settling, (3) drying the thus separated powder mixture to obtain an agglomerated powder, and (4) subjecting the thus obtained agglomerated powder to a heat treatment comprising at least two stages performed at different temperatures, so as to purify the boron and transform the boride powder of metal M or the metalloid by reaction with the oxide of metal M or the oxide of the metalloid.
Claim 4
Dependent Claim
135 words
A process for the production of porous products of a boride of a metal M or a metalloid, wherein it successively comprises the following stages: (1) suspending, accompanied by stirring, the boron powder and the powder of an oxide of metal M or an oxide of the metalloid in a solution of an alkali metal salt, oxide and/or hydroxide, (2) then separating the powder mixture from the suspension liquid by settling, (3) drying the thus separated powder mixture to obtain an agglomerated powder, and (4) subjecting the thus obtained agglomerated powder to a heat treatment comprising at least two stages performed at different temperatures, so as to purify the boron and transform the boride powder of metal M or the metalloid by reaction with the oxide of metal M or the oxide of the metalloid.
Claim 5
Dependent Claim
26 words
A process according to either of the claims 1 or 2, wherein the alkali metal hydroxide is chosen from the group including NaOH, LiOH or KOH.
Claim 6
Dependent Claim
30 words
A process according to either of the claims 1 or 2, wherein the alkali metal salt is or Na 2 B 4 O 7 or Na 2 CO 3 .
Claim 7
Dependent Claim
24 words
A process according to either of the claims 1 or 2, wherein use is made of an aqueous soda solution for preparing the suspension.
Claim 8
Dependent Claim
85 words
A process according to claim 1, wherein the heat treatment comprises three stages: a first stage performed at a temperature of 150° to 225° C. for a time adequate for converting the boric acid into boric anhydride, a second stage performed at a temperature of 1500° to 1980° C. for a time adequate for stabilizing the pressure at a level below 10 2 Pa, and a third stage performed at a temperature of 1980° to 2020° C. for a time between 60 and 30 h.
Claim 9
Dependent Claim
56 words
A process according to claim 2, wherein the heat treatment comprises at least three stages performed at temperatures of 800° to 2200° C., each of the stages being performed at a temperature higher than that of the preceding stage and each of the stages is performed under vacuum or under a neutral gas, such as helium.
Claim 10
Dependent Claim
24 words
A process according to claim 2, wherein the metal M is chosen from the group including rare earth, uranium, thorium, silicon, titanium and zirconium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-29 | 1990-03-31 | 1990-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-29 | 1994-03-31 | 1994-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-29 | 1998-03-31 | 1998-09-30 | $7700.00 | Window Closed / Lapsed |