Porous sheet
Assignee: TOKUYAMA SODA A CORP OF JAPAN KK
•
Filing: 1984-02-09
•
Granted: 1986-09-23
•
Expires: 2004-02-09
Abstract
Abstract A process for the preparation of soft porous sheets, comprises forming into a sheet a composition comprising (i) 40 to 80% by weight of an inorganic filler and (ii) 60 to 20% by weight of a polyolefin type thermoplastic elastomer composition comprising at least 50% by weight of a polyolefin type thermoplastic elastomer substantially free of a polar group, in which the tensile stress at a temperature of 25 DEG C. under 100% stretching (100% modulus) is 10 to 100 Kg/cm2, the elongation at break under stretching is at least 100% and the permanent strain under 100% stretching is less than 50% and up to 50% by weight of a thermoplastic plastomer, and stretching the sheet at a temperature lower than the softening temperature of the polyolefin type thermoplastic elastomer. A porous sheet obtained according to this process has a good combination of flexibility, air permeability and water resistance.
Inventors
- 👤 Shunichi Nakamura
- 👤 Kenji Okamura
- 👤 Shingo Kaneko
- 👤 Kiyoshi Sumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 04:42
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/16; C08K; C08K3/00; C08K3/01; C08K3/013; C08K3/18; C08K3/24; C08K3/26; C08K5/00; C08K5/04; C08K5/14; C08L23/04; C08L23/06; C08L23/08; C08L23/0807; C08L23/0815; C08L23/10; C08L67/00; C08L2312/00; C08L2666/00; C08L2666/02; C08L2666/04; Y; Y10; Y10S; Y10S264/00; Y10S264/47
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
191 words
A porous sheet comprising (i) 40 to 80% by weight of an inorganic filler and (ii) 60 to 20% by weight of a polyolefin type thermoplastic elastomer composition comprising at least 50% by weight of a polyolefin type thermoplastic elastomer selected from the group consisting of an ethylene-propylene copolymer, an ethylene-propylene-diene copolymer and an ethylene-butene-1 copolymer, in which the tensile stress at a temperature of 25° C. under 100% stretching (100% modulus) is 10 to 100 kg/cm 2 , the elongation at break under stretching is at least 100% and the permanent strain under 100% stretching is less than 50% and up to 50% by weight of a thermoplastic polyolefin resin plastomer, said sheet being stretched in at least one direction and having fine communicating pores in the interior thereof, wherein the initial tensile elastic modulus is lower than 500 kg/cm 2 , the permanent strain after 50% stretching is lower than 50%, the air permeability is lower than 10000 sec/100 cc, the water pressure resistance is at least 1000 mmH 2 O, the maximum pore size is smaller than 10 microns and the elongation at break is at least 50%.
Claim 2
Dependent Claim
191 words
A porous sheet comprising (i) 40 to 80% by weight of an inorganic filler and (ii) 60 to 20% by weight of a polyolefin type thermoplastic elastomer composition comprising at least 50% by weight of a polyolefin type thermoplastic elastomer selected from the group consisting of an ethylene-propylene copolymer, an ethylene-propylene-diene copolymer and an ethylene-butene-1 copolymer, in which the tensile stress at a temperature of 25° C. under 100% stretching (100% modulus) is 10 to 100 kg/cm 2 , the elongation at break under stretching is at least 100% and the permanent strain under 100% stretching is less than 50% and up to 50% by weight of a thermoplastic polyolefin resin plastomer, said sheet being stretched in at least one direction and having fine communicating pores in the interior thereof, wherein the initial tensile elastic modulus is lower than 500 kg/cm 2 , the permanent strain after 50% stretching is lower than 50%, the air permeability is lower than 10000 sec/100 cc, the water pressure resistance is at least 1000 mmH 2 O, the maximum pore size is smaller than 10 microns and the elongation at break is at least 50%.
Claim 3
Dependent Claim
26 words
A sheet as set forth in claim 1, wherein the average pore size is 0.05 to 5 microns as measured according to the mercury pressure method.
Claim 4
Dependent Claim
57 words
The sheet of claim 1 wherein the polyolefin type thermoplasticl elastomer composition comprises a mixture of an ethylene-butene-1 copolymer having an ethylene content of 85%, a 100% modulus of 60 kg/cm 2 , an elongation at break of 70%, and a permanent strain after 100% stretching of 5%, and polypropylene having a melt flow index of 4.0.
Claim 5
Dependent Claim
26 words
The sheet of claim 3 wherein the weight ratio of the ethylene-butene-1 copolymer of polypropylene is in the rage of from about 4:1 to about 3:2.
Claim 6
Dependent Claim
74 words
The sheet of claim 1 in which the polyolefin type thermoplasic elastomer composition comprises a mixture of an ethylene-propylene-diene copolymer having a tensile strength at 25° C. under 100% stretching of 15 kg/cm 2 , an elongation at break of 1000% and a permanent strain after 100% stretching of 10% and a powdery polypropylene having a melt flow index of 4 at a weight ratio of ethylene-propylene-diene copolymer to powderyl polypropylene of about 35/15.
Claim 7
Dependent Claim
44 words
The sheet according to claim 1 wherein the polyolefin type thermoplastic elastomer composition comprises a mixture of an ethylene-butene-1 copolymer and linear low density polyethylene and the inorganic filler is selected from the group consisting of calcium carbonate, talc, magnesium, hydroxide, and diatomaceous earth.
Claim 8
Dependent Claim
25 words
The porous sheet of claim 1 wherein the polyolefin type thermoplastic elastomer composition consists substantially of 100% by weight of the polyolefin type thermoplastic elastomer.
Claim 9
Dependent Claim
22 words
The porous sheet of claim 1 which is stretched in at least one direction at a stretching ratio of at least 1.5.
References Cited (Backward Citations)
US3649611A
Cited
US3880966A
Cited
US3903234A
Cited
US4024213A
Cited
US3843761A
Cited
US4138459A
Cited
US4472328A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-22 | 1990-03-24 | 1990-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-22 | 1994-03-24 | 1994-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-22 | 1998-03-24 | 1998-09-23 | $7700.00 | Window Closed / Lapsed |