Wood-like molded product of synthetic resin
Assignee: Individual
•
Filing: 1984-12-19
•
Granted: 1986-09-09
•
Expires: 2004-12-19
Abstract
Abstract The present invention relates to wood-like molded products of synthetic resin which are manufactured by mixing a synthetic resin material with a fine aggregate of cellulose base such as wood meal, chaffs, begasse and in which the internal residual stress which may cause deformation (for example, warping and twisting) of the products at the time or after molding is eliminated in advance to prevent chronological deformation. More particularly, it relates to a method of eliminating said residual stress by subjecting the molded products containing cellulose-base aggregate, especially the resinous skin layer thereof, to re-heating, curing and sanding or jetting treatments (sand blasting, shot peening, grit blasting) under predetermined conditions.
Inventors
- 👤 Sadao Nishibori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:13
CPC Classifications
B; B44; B44C; B44C5/00; B44C5/06; B44C3/00; B44C3/04; B44C3/08; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/1052; Y10T156/1082; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24438; Y10T428/24479; Y10T428/2457; Y10T428/25; Y10T428/253
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
74 words
A wood-like molded product of synthetic resin comprising a molded cross-linked thermoplastic resin product of fine cellulose-base aggregate having only the skin layers on top and bottom surfaces of the molded product removed after molding, by first contracting said molded product in longitudinal direction under heat treatment so as to exude the concentrated resin on the skin layers prior to removing the skin layers, the resultant hardened product being free of warping and shrinking.
Claim 2
Dependent Claim
74 words
A wood-like molded product of synthetic resin comprising a molded cross-linked thermoplastic resin product of fine cellulose-base aggregate having only the skin layers on top and bottom surfaces of the molded product removed after molding, by first contracting said molded product in longitudinal direction under heat treatment so as to exude the concentrated resin on the skin layers prior to removing the skin layers, the resultant hardened product being free of warping and shrinking.
Claim 3
Dependent Claim
21 words
The wood-like molded product of synthetic resin as claimed in claim 1 wherein said surface skin layer is removed by sanding.
Claim 4
Dependent Claim
20 words
The wood-like molded product of synthetic resin as claimed in claim 1 wherein said surface skin is removed by jetting.
Claim 5
Dependent Claim
29 words
The wood-like molded product of synthetic resin as claimed in claim 1 wherein the surface after the removal of the surface skin layer is embossed with a wood-grain pattern.
Claim 6
Dependent Claim
32 words
The wood-like molded product of synthetic resin as claimed in claim 1 wherein the surface after removal of the surface skin layer is provided with grooves to block the internal residual stress.
Claim 7
Dependent Claim
34 words
The wood-like molded product of synthetic resin as claimed in claim 1 wherein the surface after the removal of the skin layer forms an adhesion surface to allow other materials to be bonded therewith.
References Cited (Backward Citations)
US3309444A
Cited
US3511744A
Cited
US3536574A
Cited
US3873662A
Cited
US4104429A
Cited
US4064301A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-08 | 1990-03-10 | 1990-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-08 | 1994-03-10 | 1994-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-08 | 1998-03-10 | 1998-09-09 | $7700.00 | Window Closed / Lapsed |