Method of producing glass fiber mat reinforced plastic panels with smooth surfaces

Claim 1

A method of producing a smooth surface layer on the surface of a premolded glass fiber mat reinforced polyurethane panel situated in a matched mold where protruding fibers produce a rough surface, said method comprising: positioning said premolded panel in the cavity of the lower mold piece of said matched mold, coating and leveling off the rough surface of said premolded panel with a liquid mixture of a room temperature curable polyurethane composition such that the thickness of said coating is at least adequate to fill the valleys created between the protruding fibers in the surface, said premolded panel being at room temperature prior to and during said coating operation, applying sufficient pressure on said coated surface through an upper mold piece positioned on said panel to cause said coating to fill the valleys between the protruding fibers and to flow evenly to cover the entire surface of said panel, and relieving said pressure while said coating is still in its fluid state and allowing said coating composition to sufficiently harden under the dead weight of said upper mold piece, whereby the cured coating provides a smooth surface layer on said panel that masks said protruding fibers.

Claim 2

A method of producing a smooth surface layer on the surface of a premolded glass fiber mat reinforced polyurethane panel situated in a matched mold where protruding fibers produce a rough surface, said method comprising: positioning said premolded panel in the cavity of the lower mold piece of said matched mold, coating and leveling off the rough surface of said premolded panel with a liquid mixture of a room temperature curable polyurethane composition such that the thickness of said coating is at least adequate to fill the valleys created between the protruding fibers in the surface, said premolded panel being at room temperature prior to and during said coating operation, applying sufficient pressure on said coated surface through an upper mold piece positioned on said panel to cause said coating to fill the valleys between the protruding fibers and to flow evenly to cover the entire surface of said panel, and relieving said pressure while said coating is still in its fluid state and allowing said coating composition to sufficiently harden under the dead weight of said upper mold piece, whereby the cured coating provides a smooth surface layer on said panel that masks said protruding fibers.

Claim 3

A method of producing a smooth decorative surface by laminating a predecorated carrier film having a first decorated surface and a second undecorated surface to the surface of a premolded glass fiber mat reinforced polyurethane panel where protruding fibers produce a rough surface, said method when practiced in a matched mold comprising the steps of: positioning said predecorated carrier film into the first half of said matched mold with the first decorated surface of the carrier film facing the mold surface; applying a layer of a room temperature curable thermoset polymeric resin coating to the second undecorated surface of the carrier film to a minimum thickness adequate to substantially cover all the valleys created between the protruding fibers in the surface layer of said premolded panel in a subsequent operation; positioning said premolded panel over the coating resin, said panel being at room temperature prior to and during said lamination process; applying sufficient pressure on said premolded panel through the second half of the matched mold positioned thereon to cause said coating resin to substantially fill the valleys between the protruding fibers and to flow evenly to cover the entire surface of said panel; and relieving said pressure while said coating resin is still in its fluid state and allowing said coating resin to sufficiently harden under the dead weight of said second half of the matched mold, whereby said decorative layer is bonded to the rough surface of the premolded panel and said resin layer is evenly distributed between said decorative layer and said rough surface to hide the protruding glass fibers.

Claim 4

A method of producing a smooth decorative surface by laminating a predecorated carrier film having a first decorated surface and a second undecorated surface to the surface of a premolded glass fiber mat reinforced polyurethane panel where protruding fibers produce a rough surface, said method when practiced in a matched mold comprising the steps of: positioning said predecorated carrier film into the first half of said matched mold with the first decorated surface of the carrier film facing the mold surface; applying a layer of a room temperature curable thermoset polymeric resin coating to the second undecorated surface of the carrier film to a minimum thickness adequate to substantially cover all the valleys created between the protruding fibers in the surface layer of said premolded panel in a subsequent operation; positioning said premolded panel over the coating resin, said panel being at room temperature prior to and during said lamination process; applying sufficient pressure on said premolded panel through the second half of the matched mold positioned thereon to cause said coating resin to substantially fill the valleys between the protruding fibers and to flow evenly to cover the entire surface of said panel; and relieving said pressure while said coating resin is still in its fluid state and allowing said coating resin to sufficiently harden under the dead weight of said second half of the matched mold, whereby said decorative layer is bonded to the rough surface of the premolded panel and said resin layer is evenly distributed between said decorative layer and said rough surface to hide the protruding glass fibers.