Process for stepwise heating up metallic strips or foils
Assignee: Rio Tinto Switzerland AG
•
Filing: 1985-03-18
•
Granted: 1986-09-09
•
Expires: 2005-03-18
Abstract
Abstract Metal strips or foils more than 800 mm wide are brought to an end temperature of 100°-300° C. by stepwise heating. The strips or foils are deflected at an angle (α) of 15°-150° C. over 2 to 6 rolls set at increasing temperatures in the direction of throughput, at least the last roll having a double outer layer that can be heated, and the last roll being set at the final, desired temperature. The increases in temperature from one roll to the next lie between 20° and 70° C., preferably between 50° and 60° C. Usefully all the increases are the same. The process according to the invention is employed in the manufacture of composites and in the laminating and lacquering or painting of metal strips or foils.
Inventors
- 👤 Rene Bregenzer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:11
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/52; C21D9/54; C21D9/56; C21D9/562; C21D9/563; B; B32; B32B; B32B38/00; B32B38/18; B32B38/1825; C22; C22F; C22F1/00; F; F27; F27B; F27B9/00; F27B9/28; Y; Y10; Y10T; Y10T156/00; Y10T156/17; Y10T156/1702; Y10T156/1712; Y10T156/1722; Y10T156/1727; Y10T156/1741; Y10T29/00; Y10T29/51; Y10T29/5198
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
145 words
A process for the stepwise heating of a metallic strip having a width of at least 800 mm so as to prevent the formation of wrinkles on said strip to a final temperature of about between 100° to 300° C. comprising providing a plurality of rolls, arranging said plurality of rolls such that said metallic strip is deflected over each of said plurality of rolls at an angle of about between 60 to 120 degrees, heating said plurality of rolls such that the temperature of said plurality of rolls increases in the direction of metallic strip throughput from about between 20° to 70° C. from roll to roll wherein the last of said plurality of rolls is heated to the desired final temperature of said metallic strip, and passing said metallic strip having a width of at least 800 mm over said plurality of rolls.
Claim 2
Dependent Claim
145 words
A process for the stepwise heating of a metallic strip having a width of at least 800 mm so as to prevent the formation of wrinkles on said strip to a final temperature of about between 100° to 300° C. comprising providing a plurality of rolls, arranging said plurality of rolls such that said metallic strip is deflected over each of said plurality of rolls at an angle of about between 60 to 120 degrees, heating said plurality of rolls such that the temperature of said plurality of rolls increases in the direction of metallic strip throughput from about between 20° to 70° C. from roll to roll wherein the last of said plurality of rolls is heated to the desired final temperature of said metallic strip, and passing said metallic strip having a width of at least 800 mm over said plurality of rolls.
Claim 3
Dependent Claim
25 words
A process according to claim 1 including heating said plurality of rolls such that the difference in temperature between successive rolls is substantially the same.
Claim 4
Dependent Claim
32 words
A process according to claim 1 including heating said plurality of rolls such that the temperature between successive rolls of said plurality of rolls is from about between 50° to 60° C.
Claim 5
Dependent Claim
25 words
A process according to claim 3 including heating said plurality of rolls such that the difference in temperature between successive rolls is substantially the same.
Claim 6
Dependent Claim
33 words
A process according to claim 1 including heating said plurality of rolls such that said plurality of rolls exhibit temperature variations on their work face of less than or equal to ±1° C.
Claim 7
Dependent Claim
21 words
A process according to claim 1 including laminating said heated metallic strip to a core so as to form a composite.
Claim 8
Dependent Claim
11 words
A process according to claim 6 including providing a plastic core.
Claim 9
Dependent Claim
11 words
A process according to claim 6 including providing a paper core.
Claim 10
Dependent Claim
17 words
A process according to claim 6 including painting said metallic strip prior to laminating to said core.
Claim 11
Dependent Claim
17 words
A process according to claim 6 including lacquering said metallic strip prior to laminating to said core.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-08 | 1990-03-10 | 1990-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-08 | 1994-03-10 | 1994-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-08 | 1998-03-10 | 1998-09-09 | $7700.00 | Window Closed / Lapsed |