US4609718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ultraviolet curable buffer coatings for optical glass fiber based on long chain oxyalkylene diamines
Assignee: Stamicarbon BV
•
Filing: 1985-05-08
•
Granted: 1986-09-02
•
Expires: 2005-05-08
Abstract
Abstract An ultraviolet curing liquid coating composition is provided which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber having adequate strength at room or expected elevated temperature and stability at such elevated temperature, a high index of refraction above 1.48, and a low tensile modulus which remains low to resist microbending difficulties down to around -60° C. This coating composition consists essentially of a linear acrylate-terminated polyurethane oligomer including urea groups introduced by the presence in the oligomer of the reaction product with isocyanate functionality of about 30% to about 90% by weight of the acrylate-terminated oligomer of a polyoxyalkylene diamine having a molecular weight in the range of from about 1000 to about 8000 in which the alkylene group contains from 2-4 carbon atoms.
Inventors
- 👤 Timothy E. Bishop
- 👤 Clive J. Coady
- 👤 John M. Zimmerman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 04:31
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/671; C08G18/672; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C08G18/40; C08G18/48; C08G18/50; C08G18/5021; C08G18/5024; C08G18/673; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C08G18/81; C08G18/8141; C08G18/815; C08G18/8158; C08G18/8175
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
134 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber having adequate strength at room or expected elevated temperature and stability at such elevated temperature, a high index of refraction above 1.48, and a low tensile modulus which remains low to resist microbending difficulties down to around -60° C., said coating composition consisting essentially of a linear acrylate-terminated polyurethane oligomer including urea groups introduced by the presence in the oligomer of the reaction product with isocyanate functionality of about 30% to about 90% by weight of the acrylate-terminated oligomer of a polyoxyalkylene diamine having a molecular weight in the range of from about 1000 to about 8000 in which the alkylene group contains from 2-4 carbon atoms.
Claim 2
Dependent Claim
134 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber having adequate strength at room or expected elevated temperature and stability at such elevated temperature, a high index of refraction above 1.48, and a low tensile modulus which remains low to resist microbending difficulties down to around -60° C., said coating composition consisting essentially of a linear acrylate-terminated polyurethane oligomer including urea groups introduced by the presence in the oligomer of the reaction product with isocyanate functionality of about 30% to about 90% by weight of the acrylate-terminated oligomer of a polyoxyalkylene diamine having a molecular weight in the range of from about 1000 to about 8000 in which the alkylene group contains from 2-4 carbon atoms.
Claim 3
Dependent Claim
61 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminated polyurethane oligomer has a molecular weight in the range from about 2000 to about 10000, and the cured coatings posses a minimal tensile modulus at 25° C. of at least about 100 psi. and a maximum tensile modulus at -60° C. of less than 175,000 psi.
Claim 4
Dependent Claim
24 words
An ultraviolet curing liquid coating composition as recited in claim 2 in which said diamine has a molecular weight of from 1500 to 5000.
Claim 5
Dependent Claim
19 words
An ultraviolet curing liquid coating composition as recited in claim 3 in which said diamine is a polyoxypropylene diamine.
Claim 6
Dependent Claim
42 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminate polyurethane oligomer is used in admixture with an acrylate-functional liquid which does not increase the low temperature hardness and which provides the liquidity needed for coating application.
Claim 7
Dependent Claim
39 words
An ultraviolet curing liquid coating composition as recited in claim 5 in which said acrylate-functional liquid is a monoacrylate monomer having a glass transition temperature below about 0° C. which provides the composition with a viscosity suitable for coating.
Claim 8
Dependent Claim
25 words
An ultraviolet curing liquid coating composition as recited in claim 6 in which said monoacrylate monomer has a glass transition temperature below about -20° C.
Claim 9
Dependent Claim
35 words
An ultraviolet curing liquid coating composition as recited in claim 7 in which said low glass transition temperature monomer is selected from the group consisting of ethoxyethoxyethyl acrylate, phenoxyethyl acrylate, butoxyethyl acrylate, and 2-hydroxyethyl acrylate.
Claim 10
Dependent Claim
56 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminated polyurethane oligomer is used in admixture with a linear aliphatic diacrylate in which the two acrylate groups are separated by a chain of at least 6 carbon atoms or by a molecular weight of at least 400 up to about 4000.
Claim 11
Dependent Claim
30 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said diamine is present in said acrylate-terminated polyurethane oligomer in an amount of from 45% to 80%.
Claim 12
Dependent Claim
47 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminated polyurethane oligomer has a molecular weight of from about 2500 to about 6000, and contains from 2 to about 10 urethane groups per molecule and from 2 to about 6 urea groups.
Claim 13
Dependent Claim
39 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminate polyurethane oligomer is based on a diisocyanate in which a linear aliphatic chain containing at least 6 carbon atoms separates the two isocyanate groups.
Claim 14
Dependent Claim
22 words
An ultraviolet curing liquid coating composition as recited in claim 12 in which said diisocyanate is provided by dimer fatty acid diisocyanate.
Claim 15
Dependent Claim
22 words
An ultraviolet curing liquid coating composition as recited in claim 13 in which said dimer fatty acid diisocyanate contains 36 carbon atoms.
Claim 16
Dependent Claim
26 words
An ultraviolet curing liquid coating composition as recited in claim 2 in which said coating composition cures to provide an index of refraction is about 1.54-1.55.
Claim 17
Dependent Claim
23 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said oligomer is capped with a monohydric mono- or polyacrylate.
Claim 18
Dependent Claim
28 words
An ultraviolet curing liquid coating composition as recited in claim 1 in which said acrylate-terminated polyurethane oligomer is a liquid present in the substantial absence of other liquids.
Claim 19
Dependent Claim
15 words
An optical glass fiber coated with an ultraviolet-cured coating of the composition of claim 1.
Claim 20
Dependent Claim
15 words
An optical glass fiber coated with an ultraviolet-cured coating of the composition of claim 17.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-01 | 1990-03-03 | 1990-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-01 | 1994-03-03 | 1994-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-01 | 1998-03-03 | 1998-09-02 | $7700.00 | Window Closed / Lapsed |