Abstract A powdered material is provided for thermal spraying comprising a mixture of self-fluxing matrix allow powder and a powder of at least one metal carbide, the carbide content of the mixture consisting essentially between 20 and 80 percent by thereof and the matrix alloy having the following composition, in percent by weight: ______________________________________ Cr 18.0-35.0%
Fe 0.1-25.0%
B 0.5-4.5%
Si 0.5-5.5%
C 0.01-2.0%
Mo 0-15.0%
Nb 0-2.0%
Ni Remainder.
______________________________________
Inventors
👤 Wolfgang Simm
👤 Hans-Theo Steine
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-07 06:08
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; C23C4/06
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
131 words
A powdered material for thermal spraying comprising a mixture of a self-fluxing matrix alloy powder and of a powder of at least one metal carbide, the carbide content of the mixture consisting essentially between 20 and 80 percent by weight thereof and the matrix alloy having the following composition, in percent by weight: ______________________________________
Cr 18.0-35.0%
Fe 0.1-25.0%
B 0.5-4.5%
Si 0.5-5.5%
C 0.01-2.0%
Mo 0-15.0%
Nb 0-2.0%
Ni Remainder
______________________________________ said powdered material characterized, when thermally sprayed onto a metal substrate to form a bonded coating thereon comprising particles of said carbide dispersed through a zone of said matrix metal, by a decreased presence of M 6 C-carbide between said matrix zone and the carbide particles and by a marked improvement in elasticity and in resistance to corrosion and erosion.
Claim 2
Dependent Claim
131 words
A powdered material for thermal spraying comprising a mixture of a self-fluxing matrix alloy powder and of a powder of at least one metal carbide, the carbide content of the mixture consisting essentially between 20 and 80 percent by weight thereof and the matrix alloy having the following composition, in percent by weight: ______________________________________
Cr 18.0-35.0%
Fe 0.1-25.0%
B 0.5-4.5%
Si 0.5-5.5%
C 0.01-2.0%
Mo 0-15.0%
Nb 0-2.0%
Ni Remainder
______________________________________ said powdered material characterized, when thermally sprayed onto a metal substrate to form a bonded coating thereon comprising particles of said carbide dispersed through a zone of said matrix metal, by a decreased presence of M 6 C-carbide between said matrix zone and the carbide particles and by a marked improvement in elasticity and in resistance to corrosion and erosion.
Claim 3
Dependent Claim
15 words
A material in accordance with claim 1, characterized in that said carbide is tungsten monocarbide.
Claim 4
Dependent Claim
19 words
A material in accordance with claim 1 or 2, characterized in that the carbide particles are coated with Ni.
Claim 5
Dependent Claim
60 words
The powdered material in accordance with claim 1, characterized in that the composition is made up of about 50% by weight of fused tungsten monocarbide and about 50% by weight of the matrix alloy, the composition of said matrix alloy being approximately 22% Cr, 4% Fe, 3.5% B, 4.1% Si, 0.6% C, 2.5% Mo, 0.1% Nb and Ni the remainder.