Inert monovalent hydrocarbon terminated polysulfide polymers
Assignee: Dow Chemical Co
•
Filing: 1985-07-24
•
Granted: 1986-08-26
•
Expires: 2005-07-24
Abstract
Abstract Disclosed herein are inert monovalent hydrocarbon terminated polysulfide copolymers having the general structure ##STR1## wherein n is an integer from about 2 to about 8, l is zero or a positive integer, m is a positive integer, each R is independently an organic polyradical with the radicals residing on carbon atoms, p is zero or a positive integer which is the difference between the number of radicals on R and 2, and each Y is a terminal substituent that is an inert monovalent hydrocarbon radical.
Inventors
- 👤 Victor E. Meyer
- 👤 Thomas E. Dergazarian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:07
CPC Classifications
C; C08; C08L; C08L81/00; C08L81/04; C07; C07C; C07C321/00; C08F; C08F12/00; C08F12/34; C08F8/00; C08F8/34; C08G; C08G75/00; C08G75/14; C08G75/16
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
94 words
A polysulfide polymer having a molecular weight from about 3,000 to about 100,000, as represented by the general structure ##STR6## wherein R and R' at each occurrence are independently polyvalent organic polyradicals with each valence residing on a carbon atom; each Y is a terminal substituent that is an inert monovalent hydrocarbon radical; 1 is zero or a positive integer; m is a positive integer; n is a number from about 2 to about 8; and p is zero or a positive integer which is the difference between the valence of R and two.
Claim 2
Dependent Claim
94 words
A polysulfide polymer having a molecular weight from about 3,000 to about 100,000, as represented by the general structure ##STR6## wherein R and R' at each occurrence are independently polyvalent organic polyradicals with each valence residing on a carbon atom; each Y is a terminal substituent that is an inert monovalent hydrocarbon radical; 1 is zero or a positive integer; m is a positive integer; n is a number from about 2 to about 8; and p is zero or a positive integer which is the difference between the valence of R and two.
Claim 3
Dependent Claim
42 words
A polymer as in claim 1 wherein each Y is independently a (vinylaryl)alkyl substituent or an organic group which is not capable of engaging in a curing reaction, provided that fewer than 10 percent by number of the Y substituents are (vinylaryl)alkyl.
Claim 4
Dependent Claim
20 words
A polymer as in claim 2 wherein said Y substituent is an unsubstituted or inertly substituted (aryl)alkyl, or cycloalkyl group.
Claim 5
Dependent Claim
16 words
A polymer as in claim 2 wherein each Y substituent is an (aryl)alkyl or (vinylaryl)alkyl group.
Claim 6
Dependent Claim
14 words
A polymer as in claim 4 wherein each Y substituent is vinylbenzyl or benzyl.
Claim 7
Dependent Claim
14 words
A polymer as in claim 2 wherein each R is independently an aliphatic diradical.
Claim 8
Dependent Claim
23 words
A polymer as in claim 2 wherein each R is independently an alkylene diradical, bis(4-chloromethyl)phenyl ether, bis-(4-chloroacetyl)phenyl ether, 2,5-di(chloromethyl)-1,4,-dioxane or diethylene glycol bis(chloroacetate).
Claim 9
Dependent Claim
56 words
A polymer as in claim 2 wherein each R is selected such that from about 90 to about 99.5 weight percent, based on the combined weight of all the R groups, of the R groups are organic diradicals and from about 10 to about 0.5 weight percent of the R groups have at least 3 valences.
Claim 10
Dependent Claim
15 words
A polymer as in claim 2 having a molecular weight from about 3,000 to 25,000.
Claim 11
Dependent Claim
79 words
A process for making polysulfide polymers, comprising reacting a mixture comprising an alkali-or alkaline earth polysulfide, at least one unsubstituted or inertly substituted polyfunctional organic compound having a plurality of negatively charged functionalities attached to an aliphatic or alicyclic carbon atom, which functionalities will split off upon reacting with said alkali or alkaline earth polysulfide, and an inert monovalent hydrocarbon compound having a negatively charged functionality which will split off upon reacting with said alkali or alkaline earth polysulfide.
Claim 12
Dependent Claim
79 words
A process for making polysulfide polymers, comprising reacting a mixture comprising an alkali-or alkaline earth polysulfide, at least one unsubstituted or inertly substituted polyfunctional organic compound having a plurality of negatively charged functionalities attached to an aliphatic or alicyclic carbon atom, which functionalities will split off upon reacting with said alkali or alkaline earth polysulfide, and an inert monovalent hydrocarbon compound having a negatively charged functionality which will split off upon reacting with said alkali or alkaline earth polysulfide.
Claim 13
Dependent Claim
55 words
A process as in claim 10 wherein said inert monovalent hydrocarbon compound comprises a (vinylaryl)alkyl halide and a noncrosslinking inert monovalent hydrocarbon compound provided that a sufficient proportion of the terminal substituents of the polymer so made are not (vinylaryl)alkyl that the polymer is incapable of curing to a material which does not cold flow.
Claim 14
Dependent Claim
23 words
A process as in claim 11 wherein the reaction is carried out at a temperature from about 25° C. to about 90° C.
Claim 15
Dependent Claim
15 words
A process as in claim 11 wherein the reaction is carried out in an emulsion.
Claim 16
Dependent Claim
21 words
The process of claim 12 wherein the inert monovalent hydrocarbon compound comprises a mixture of a vinylbenzylhalide and a benzyl halide.
References Cited (Backward Citations)
US2349191A
Cited
US2466963A
Cited
US2986582A
Cited
US3367975A
Cited
US3968264A
Cited
US3907899A
Cited
US4438259A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-25 | 1990-02-24 | 1990-08-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-25 | 1994-02-24 | 1994-08-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-25 | 1998-02-24 | 1998-08-26 | $7700.00 | Window Closed / Lapsed |