US4606785A — Simplified method of making high strength resin b…

Claim 1

Independent Claim 224 words

A method of making a flexible, porous, resin bonded mica tape comprising the steps: (1) providing a composite of a resin permeable mica sheet and a resin permeable open weave fabric backing material wherein the backing material has a higher resin permeability than the mica sheet; (2) providing a solution of 100 parts by weight of an epoxy mica bonding resin consisting essentially of epoxy novolac and cycloaliphatic epoxy, which will permeate both the mica sheet and the backing material, and from about 100 parts by weight to about 150 parts by weight of a polyester adhesive resin consisting essentially of linear, saturated polyester exhibiting cohesive properties having a ball and ring softening point at from about 125° C. to about 180° C. and an elongation to about 20°%, and linear, saturated polyester exhibiting adhesive properties having a ball and ring softening point at from about 70° C. to about 115° C. and an elongation greater than about 800%, which will permeate the backing material but not the mica sheet; (3) contacting the backing material of the composite with said solution so that the mica bonding resin permeates the mica sheet and the adhesive resin permeates only the backing sheet; and (4) removing the resin solvent, thereby binding the mica in the mica sheet together and adhering the backing material to the mica sheet.

Claim 2

Independent Claim 224 words

A method of making a flexible, porous, resin bonded mica tape comprising the steps: (1) providing a composite of a resin permeable mica sheet and a resin permeable open weave fabric backing material wherein the backing material has a higher resin permeability than the mica sheet; (2) providing a solution of 100 parts by weight of an epoxy mica bonding resin consisting essentially of epoxy novolac and cycloaliphatic epoxy, which will permeate both the mica sheet and the backing material, and from about 100 parts by weight to about 150 parts by weight of a polyester adhesive resin consisting essentially of linear, saturated polyester exhibiting cohesive properties having a ball and ring softening point at from about 125° C. to about 180° C. and an elongation to about 20°%, and linear, saturated polyester exhibiting adhesive properties having a ball and ring softening point at from about 70° C. to about 115° C. and an elongation greater than about 800%, which will permeate the backing material but not the mica sheet; (3) contacting the backing material of the composite with said solution so that the mica bonding resin permeates the mica sheet and the adhesive resin permeates only the backing sheet; and (4) removing the resin solvent, thereby binding the mica in the mica sheet together and adhering the backing material to the mica sheet.

Claim 3

Dependent Claim 68 words

The method of claim 1 wherein the adhesive resin bonds to the epoxy resin in the mica sheet at the mica-backing contact interface providing a dried, flexible, porous, resin bonded, consolidated mica tape composite containing from about 2 wt. % to about 15 wt. % resin solids and the consolidated mica tape composite is characterized as remaining a consolidated composite upon bending, without disintegration of the mica sheet.

Claim 4

Dependent Claim 54 words

The method of claim 1, wherein the mica in the mica sheet is selected from the group consisting of felted paper, and flakes, the backing material is selected from the group consisting of glass fabric, cotton fabric, nylon fabric, and polyethylene terephthalate fabric and the mica tape composite is wound around an electrical coil.

Claim 5

Independent Claim 275 words

A method of making a flexible, porous, resin bonded mica tape comprising the steps: (1) contacting a mica sheet with a flexible open weave fabric backing material to form a composite; (2) applying a bonding resin admixture solution of polyester resin and epoxy resin to the backing material, where the polyester and epoxy permeate the backing material and the epoxy permeates the mica sheet, where the resin admixture solution consists essentially of: (a) from about 100 parts by weight to about 150 parts by weight of a polyester resin component consisting essentially of: (i) linear, saturated polyester exhibiting cohesive properties having a ball and ring softening point at from about 125° C. to about 180° C. and an elongation of up to about 20%; and (ii) linear, saturated polyester exhibiting adhesive properties having a ball and ring softening point at from about 70° C. to about 115° C. and an elongation of greater than about 800%; and (b) 100 parts weight of an epoxy resin component consisting essentially of: (i) epoxy novolac; and (ii) cycloaliphatic epoxy: (c) latent catalyst for the epoxy resin component; and (d) solvent for the polyester resin component and the epoxy resin component; and (3) drying the resin containing composite for a time and at a temperature that is effective to remove solvent but not cure the bonding resin; to provide a bond between the epoxy resin in the mica sheet and the polyester resin in the backing material at the mica-backing contact interface, providing a dried, flexible, porous, resin bonded, consolidated mica tape composite, characterized as capable of remaining a consolidated composite upon bending, without disintegration of the mica sheet.

Claim 6

Independent Claim 275 words

A method of making a flexible, porous, resin bonded mica tape comprising the steps: (1) contacting a mica sheet with a flexible open weave fabric backing material to form a composite; (2) applying a bonding resin admixture solution of polyester resin and epoxy resin to the backing material, where the polyester and epoxy permeate the backing material and the epoxy permeates the mica sheet, where the resin admixture solution consists essentially of: (a) from about 100 parts by weight to about 150 parts by weight of a polyester resin component consisting essentially of: (i) linear, saturated polyester exhibiting cohesive properties having a ball and ring softening point at from about 125° C. to about 180° C. and an elongation of up to about 20%; and (ii) linear, saturated polyester exhibiting adhesive properties having a ball and ring softening point at from about 70° C. to about 115° C. and an elongation of greater than about 800%; and (b) 100 parts weight of an epoxy resin component consisting essentially of: (i) epoxy novolac; and (ii) cycloaliphatic epoxy: (c) latent catalyst for the epoxy resin component; and (d) solvent for the polyester resin component and the epoxy resin component; and (3) drying the resin containing composite for a time and at a temperature that is effective to remove solvent but not cure the bonding resin; to provide a bond between the epoxy resin in the mica sheet and the polyester resin in the backing material at the mica-backing contact interface, providing a dried, flexible, porous, resin bonded, consolidated mica tape composite, characterized as capable of remaining a consolidated composite upon bending, without disintegration of the mica sheet.

Claim 7

Dependent Claim 99 words

The method of claim 4, wherein the polyester exhibiting cohesive properties has a tensile strength grater than about 6,000 psi., and the polyester exhibiting adhesive properties has a tensile strength of up to about 150 psi., where both polyesters are hydroxyl terminated and do not have any vinyl saturation in the polymer, the solids weight ratio of polyester exhibiting cohesive properties:polyester exhibiting adhesive properties is from about 1:2 to 5, the resin bonded tape contains from about 2 wt. % to about 15 wt. % resin solids and the dried mica tape is wound on a roll for storage.

Claim 8

Dependent Claim 102 words

The method of claim 4, where the solids weight ratio of epoxy resin component:polyester resin component:latent catalyst is from about 100:100 to 150:0.05 to 0.5, the the solids content of the resin admixture solution is from about 5 wt. % to about 55 wt. %, the epoxy equivalent weight of the epoxy novolac is from about 170 to about 220, the epoxy equivalent weight of the cycloaliphatic epoxy is from about 90 to about 160, the latent catalyst is an organo tin compound, and the resin containing composite is dried in an oven at from about 60° C. to about 100° C.

Claim 9

Dependent Claim 20 words

The method of claim 4, where the dried mica tape is wound around an electrical coil as a last step.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1989-08-18	1990-02-17	1990-08-19	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1993-08-18	1994-02-17	1994-08-19	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1997-08-18	1998-02-17	1998-08-19	$7700.00	Window Closed / Lapsed

Simplified method of making high strength resin bonded mica tape

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag