Abstract
Abstract A method of enhancing the brightness (beneficiating) of kaolin clays by removing titanium impurities is disclosed. The claimed method is a selective flocculation process wherein clay solids are blunged (dispersed) in water together with a dispersing agent and an ammonium salt conditioning agent. When a water-dispersible anionic polymer is added to the dispersed and conditioned clay suspension, titanium flocs are separated from the suspension yielding a whiter kaolin clay product. Unlike prior art selective flocculation processes, the use of highly-dilute dispersions and/or multiple washing steps is not required.
Inventors
- 👤 Joseph C. S. Shi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:44
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/40; C09C1/42; B; B03; B03D; B03D3/00; B03D3/06; C01; C01P; C01P2006/00; C01P2006/22; C01P2006/60; C01P2006/80
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
168 words
A method of removing titanium impurities from kaolin clay comprising the following steps in sequence: (A) blunging an aqueous kaolin clay suspension having 45 to 70 percent solids by weight, said suspension containing (i) an amount of dispersing agent sufficient to achieve minimum viscosity for said suspension and substantially free of excess dispersing agents, and (ii) 0.1 pounds to 10.0 pounds, per ton of dry clay, of a conditioning agent consisting essentially of a water-soluble ammonium salt; (B) diluting the blunged clay suspension with an amount of water sufficient to form a clay slip having 10 to 40 percent solids by weight; (C) adding 0.01 pounds to 5.0 pounds, per ton of dry clay, of a water-dispersible anionic polymer to said clay slip, whereby a separation of titanium-containing flocs is effected from said slip and (D) separating a white claim product from said titanium-containing flocs; wherein steps A, B and C are performed in a substantially continuous manner, without aging said blunged clay suspension or said clay slip.
Claim 2
Dependent Claim
27 words
The method of claim 1 wherein said ammonium salt conditioning agent is present in an amount between 0.5 pounds and 5.0 pounds per ton of dry clay.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein the pH of said aqueous clay suspension during said blunging step is in the range 5 to 11.
Claim 4
Dependent Claim
11 words
The method of claim 3 wherein said pH is approximately neutral.
Claim 5
Dependent Claim
25 words
The method of claim 1 wherein the solids level of said aqueous clay suspension during said blunging step is approximately 65 percent solids by weight.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said dispersing agent is selected from the group consisting of (a) a mixture of sodium hexametaphosphate and sodium metasilicate; and (b) a mixture of sodium hexametaphosphate and soda ash.
Claim 7
Dependent Claim
12 words
The method of claim 1 wherein said conditioning agent is ammonium chloride.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein the solids level of said blunged clay suspension during said slip-forming step is approximately 20 percent solids by weight.
Claim 9
Dependent Claim
55 words
The method of claim 1, further including an iron-removal procedure, comprising the following steps in sequence: coagulating said white clay product with a mixture of sulfuric acid and/or aluminum sulfate; leaching the coagulated clay product with an iron-reducing material selected from the group consisting of zinc and sodium hydrosulfite; and filtering said coagulated clay product.
Claim 10
Independent Claim
175 words
A method of removing titanium impurities from kaolin clay comprising the following steps in sequence: (A) blunging an aqueous kaolin clay suspension having 45 to 70 percent solids by weight, said suspension containing an amount of dispersing agent sufficient to achieve minimum viscosity for said suspension and substantially free of excess dispersing agents; (B) adding 0.1 pounds to 10.0 pounds, per ton of dry clay, of a conditioning agent to said blunged clay suspension, said conditioning agent consisting essentially of a water-soluble ammonium salt; (C) diluting said clay suspension with an amount of water sufficient to form a clay slip having 10 to 40 percent solids by weight; (D) adding 0.01 pounds to 5.0 pounds, per ton of dry clay, of a water-dispersible anionic polymer to said clay slip, whereby a separation of titanium-containing flocs is effected from said slip, and (E) separating a white clay product from said titanium-containing flocs; wherein steps A, B, C and D are performed in a substantially continuous manner, without aging said blunged clay suspension or said clay slip.
Claim 11
Independent Claim
175 words
A method of removing titanium impurities from kaolin clay comprising the following steps in sequence: (A) blunging an aqueous kaolin clay suspension having 45 to 70 percent solids by weight, said suspension containing an amount of dispersing agent sufficient to achieve minimum viscosity for said suspension and substantially free of excess dispersing agents; (B) adding 0.1 pounds to 10.0 pounds, per ton of dry clay, of a conditioning agent to said blunged clay suspension, said conditioning agent consisting essentially of a water-soluble ammonium salt; (C) diluting said clay suspension with an amount of water sufficient to form a clay slip having 10 to 40 percent solids by weight; (D) adding 0.01 pounds to 5.0 pounds, per ton of dry clay, of a water-dispersible anionic polymer to said clay slip, whereby a separation of titanium-containing flocs is effected from said slip, and (E) separating a white clay product from said titanium-containing flocs; wherein steps A, B, C and D are performed in a substantially continuous manner, without aging said blunged clay suspension or said clay slip.
Claim 12
Dependent Claim
27 words
The method of claim 10 wherein said ammonium salt conditioning agent is present in an amount between 0.5 pounds and 5.0 pounds per ton of dry clay.
Claim 13
Dependent Claim
24 words
The method of claim 10 wherein the pH of said aqueous clay suspension during said blunging step is in the range 5 to 11.
Claim 14
Dependent Claim
11 words
The method of claim 12 wherein said pH is approximately neutral.
Claim 15
Dependent Claim
25 words
The method of claim 10 wherein the solids level of said aqueous clay suspension during said blunging step is approximately 65 percent solids by weight.
Claim 16
Dependent Claim
35 words
The method of claim 10 wherein said dispersing agent is selected from the group consisting of (a) a mixture of sodium hexametaphosphate and sodium metasilicate; and (b) a mixture of sodium hexametaphosphate and soda ash.
Claim 17
Dependent Claim
12 words
The method of claim 10 wherein said conditioning agent is ammonium chloride.
Claim 18
Dependent Claim
25 words
The method of claim 10 wherein the solids level of said blunged clay suspension during said slip-forming step is approximately 20 percent solids by weight.
Claim 19
Dependent Claim
55 words
The method of claim 10 further including an iron-removal procedure, comprising the following steps in sequence: coagulating said white clay product with a mixture of sulfuric acid and/or aluminum sulfate; leaching the coagulated clay product with an iron-reducing material selected from the group consisting of zinc and sodium hydrosulfite; and filtering said coagulated clay product.
References Cited (Backward Citations)
US2710244A
Cited
US3371988A
Cited
US3701417A
Cited
US3857781A
Cited
DE2412787A1
Cited
US4186027A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-04 | 1990-02-03 | 1990-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-04 | 1994-02-03 | 1994-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-04 | 1998-02-03 | 1998-08-05 | $7700.00 | Window Closed / Lapsed |