Abstract
Abstract A method of fabricating a thin magnetic film having improved magnetoresistive readout characteristics as a binary memory device is disclosed. The film is initially formed from a metal vapor as a series of discrete grains upon a substrate surface that is heated to approximately 300° C. Upon continued growth of the film, the grains merge at their boundaries forming a continuous thin film, the grain boundary heights of which, e.g., 1000 Å, are substantially greater than the thickness, e.g., 320 Å, of the eventual thin magnetizable film. The thin film is then rotated while being ion milled at an oblique angle to a substantially uniform film thickness of e.g. 320 Å.
Inventors
- 👤 Maynard C. Paul
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:16
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/14; H01F41/18; H10; H10N; H10N50/00; H10N50/01
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
141 words
In a thin film magnetic film the method of improving its magnetoresistive effect, comprising: forming a thin magnetic film upon a suitable substrate, initially said film consisting of separated grains, at a temperature that is in the range of approximately 300° C. to 320° C.; increasing the thickness of said thin magnetic film until the thin magnetic film becomes continuous, with the boundary height between grains substantially greater than a pre-determined thin magnetic film thickness; rotating said substrate about an axis that is perpendicular to the plane of said substrate; directing an ion beam upon said thin magnetic film at an angle with respect to the normal to the plane of said substrate; and ion-milling said thin magnetic film to said predetermined thin magnetic film thickness in a manner that modifies the usual grain structure for a film of that thickness.
Claim 2
Dependent Claim
141 words
In a thin film magnetic film the method of improving its magnetoresistive effect, comprising: forming a thin magnetic film upon a suitable substrate, initially said film consisting of separated grains, at a temperature that is in the range of approximately 300° C. to 320° C.; increasing the thickness of said thin magnetic film until the thin magnetic film becomes continuous, with the boundary height between grains substantially greater than a pre-determined thin magnetic film thickness; rotating said substrate about an axis that is perpendicular to the plane of said substrate; directing an ion beam upon said thin magnetic film at an angle with respect to the normal to the plane of said substrate; and ion-milling said thin magnetic film to said predetermined thin magnetic film thickness in a manner that modifies the usual grain structure for a film of that thickness.
Claim 3
Dependent Claim
14 words
The method of claim 1 in which said boundary height is approximately 1000 Å.
Claim 4
Dependent Claim
30 words
The method of claim 1 in which said ion-milling is performed with the direction of ion bombardment being directed approximately 60° to the normal to the plane of said substrate.
Claim 5
Dependent Claim
17 words
The method of claim 1 in which said predetermined thin magnetic film thickness is approximately 320 Å.
Claim 6
Dependent Claim
117 words
In a thin magnetic film the method of improving the magnetoresistive effect, comprising: depositing a magnetic film upon a suitable substrate as a series of separated grains at a temperature in the range of approximately 300° C. to 320° C.; continuing the deposition of said magnetic film until said magnetic film becomes continuous with the boundary height between grains being substantially greater than a predetermined thin magnetic film thickness; rotating said substrate about an axis that is normal to its surface; and directing an ion beam upon the surface of said magnetic film at an angle that is inclined with respect to said axis for ion milling said magnetic film to said predetermined thin magnetic film thickness.
Claim 7
Dependent Claim
117 words
In a thin magnetic film the method of improving the magnetoresistive effect, comprising: depositing a magnetic film upon a suitable substrate as a series of separated grains at a temperature in the range of approximately 300° C. to 320° C.; continuing the deposition of said magnetic film until said magnetic film becomes continuous with the boundary height between grains being substantially greater than a predetermined thin magnetic film thickness; rotating said substrate about an axis that is normal to its surface; and directing an ion beam upon the surface of said magnetic film at an angle that is inclined with respect to said axis for ion milling said magnetic film to said predetermined thin magnetic film thickness.
Claim 8
Dependent Claim
23 words
The method of claim 5 in which said predetermined thin magnetic film thickness is in the range of 250 Å to 400 Å.
Claim 9
Dependent Claim
35 words
The method of claim 5 in which said ion milling is performed with the direction of ion bombardment being directed at a low angle of incidence with respect to the surface of said magnetic film.
Claim 10
Dependent Claim
33 words
The method of claim 5 in which said deposition temperature is approximately 300° C.; said grain boundary height is approximately 980 Å; and said predetermined thin magnetic film thickness is approximately 320 Å.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-04 | 1990-02-03 | 1990-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-04 | 1994-02-03 | 1994-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-04 | 1998-02-03 | 1998-08-05 | $7700.00 | Window Closed / Lapsed |