Assignee: JGC Catalysts and Chemicals Ltd
•
Filing: 1985-03-20
•
Granted: 1986-07-29
•
Expires: 2005-03-20
Abstract
Abstract Incorporation of a lithium component in a composition comprising a porous siliceous matrix and a crystalline aluminosilicate dispersed therein provides a hydrocarbon catalytic cracking catalyst having superior cracking activity and selectivity and also having a superior thermal and hydrothermal stability.
Inventors
- 👤 Goro Sato
- 👤 Masamitsu Ogata
- 👤 Izumi Takano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:04
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
83 words
A hydrocarbon catalytic cracking catalyst composition comprising: a porous siliceous matrix, a crystalline aluminosilicate zeolite dispersed in said matrix, and a lithium component, the Na 2 O content of said composition being less than 1.0% by weight, said composition having been prepared by spray-drying an aqueous slurry of a mixture of a precursor of said porous siliceous matrix and said crystalline aluminosilicate zeolite and thereby obtaining spherical particles, washing said particles and then introducing and uniformly dispersing said lithium component throughout the particles.
Claim 2
Dependent Claim
83 words
A hydrocarbon catalytic cracking catalyst composition comprising: a porous siliceous matrix, a crystalline aluminosilicate zeolite dispersed in said matrix, and a lithium component, the Na 2 O content of said composition being less than 1.0% by weight, said composition having been prepared by spray-drying an aqueous slurry of a mixture of a precursor of said porous siliceous matrix and said crystalline aluminosilicate zeolite and thereby obtaining spherical particles, washing said particles and then introducing and uniformly dispersing said lithium component throughout the particles.
Claim 3
Dependent Claim
26 words
A catalyst composition according to claim 1 wherein the amount of said lithium component is 0.1-5.0% by weight of the catalyst composition, calculated as the oxide.
Claim 4
Dependent Claim
22 words
A catalyst composition according to claim 1 which contains said crystalline aluminosilicate in an amount ranging from 5 to 50 wt. %.
Claim 5
Dependent Claim
23 words
A catalyst composition according to claim 1 which contains silica derived from the matrix in an amount of 5 wt. % or more.
Claim 6
Dependent Claim
34 words
A catalyst composition according to claim 1 in which said zeolite is selected from the group consisting of hydrogen exchanged-zeolite and rare earth metal exchanged-zeolite and said particles are impregnated with said lithium component.
Claim 7
Dependent Claim
153 words
A hydrocarbon catalytic cracking catalyst composition comprising: a porous siliceous matrix, from 5 to 50% by weight of crystalline aluminosilicate zeolite dispersed in said matrix, said crystalline aluminosilicate zeolite being selected from the group consisting of hydrogen exchanged-zeolites and rare earth metal exchanged-zeolites, and a lithium component, the Na 2 O content of said catalyst composition being less than 1.0% by weight, said catalyst composition having been prepared by spray-drying an aqueous slurry of a mixture of a precursor of said porous siliceous matrix and said crystalline aluminosilicate zeolite and thereby obtaining spherical particles, washing said particles until the Na 2 O content of said particles is less than 1.0% by weight, drying said particles, then uniformly impregnating said particles with an aqueous solution of an inorganic, water-soluble lithium compound so that said particles contain from 0.1 to 5% by weight of lithium, calculated as Li 2 O, and then drying said particles.
Claim 8
Dependent Claim
153 words
A hydrocarbon catalytic cracking catalyst composition comprising: a porous siliceous matrix, from 5 to 50% by weight of crystalline aluminosilicate zeolite dispersed in said matrix, said crystalline aluminosilicate zeolite being selected from the group consisting of hydrogen exchanged-zeolites and rare earth metal exchanged-zeolites, and a lithium component, the Na 2 O content of said catalyst composition being less than 1.0% by weight, said catalyst composition having been prepared by spray-drying an aqueous slurry of a mixture of a precursor of said porous siliceous matrix and said crystalline aluminosilicate zeolite and thereby obtaining spherical particles, washing said particles until the Na 2 O content of said particles is less than 1.0% by weight, drying said particles, then uniformly impregnating said particles with an aqueous solution of an inorganic, water-soluble lithium compound so that said particles contain from 0.1 to 5% by weight of lithium, calculated as Li 2 O, and then drying said particles.
Claim 9
Dependent Claim
28 words
A catalyst composition according to claim 6 in which said lithium compound is selected from the group consisting of lithium chloride, lithium nitrate, lithium sulfate and lithium hydroxide.
References Cited (Backward Citations)
US3939058A
Cited
GB1245349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-28 | 1990-01-27 | 1990-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-28 | 1994-01-27 | 1994-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-28 | 1998-01-27 | 1998-07-29 | $7700.00 | Window Closed / Lapsed |