Insole composites and processes for manufacturing insole composites and footwear materials
Assignee: DVSG Holding GmbH
•
Filing: 1984-04-10
•
Granted: 1986-07-29
•
Expires: 2004-04-10
Abstract
Abstract Novel, improved insole composites comprising a non-woven fiber batt needle-punched to one side of a woven polymeric scrim and which is subsequently impregnated or saturated with a curable or cross-linkable polymer. The invention also presents novel processes for producing the insole composites and for manufacturing footwear comprising the novel, improved insole composites.
Inventors
- 👤 Anthony Dergarabedian
- 👤 Robert L. Daigneault
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:30
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; A; A43; A43B; A43B13/00; A43B13/38; B32B5/02; B32B5/06; B32B5/28; D; D04; D04H; D04H1/00; D04H1/40; D04H1/44; D04H1/46; D04H1/48; D04H1/488; D04H1/498; D06; D06N; D06N3/00; D06N3/0002; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/023; B32B2260/04; B32B2260/046; B32B2262/00; B32B2262/02; B32B2262/0276; B32B2437/00; B32B2437/02; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/252; Y10T428/27; Y10T428/31504; Y10T428/31826; Y10T442/00; Y10T442/10; Y10T442/102; Y10T442/159
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
144 words
A composite comprising a non-woven fiber batt needle-punched to a woven polymeric scrim and a cured copolymer saturant distributed throughout the interstices of the composite and distributed about the surface of the composite to render said composite resistant to air flow and effectively impervious to molded footwear components, said copolymer saturant comprising from about 15 to about 35 percent by weight acrylonitrile, from about 20 to about 30 percent by weight styrene and from about 35 to about 65 percent by weight butadiene and being curable at temperatures between about 250° F. to about 300° F. and having a glass transition temperature between about -10° C. to about -40° C. and said composite having a tensile strength of about 100 pounds per square inch or more and a resistance to elongation of no more than about 2 percent at 20 pounds per inch load.
Claim 2
Dependent Claim
144 words
A composite comprising a non-woven fiber batt needle-punched to a woven polymeric scrim and a cured copolymer saturant distributed throughout the interstices of the composite and distributed about the surface of the composite to render said composite resistant to air flow and effectively impervious to molded footwear components, said copolymer saturant comprising from about 15 to about 35 percent by weight acrylonitrile, from about 20 to about 30 percent by weight styrene and from about 35 to about 65 percent by weight butadiene and being curable at temperatures between about 250° F. to about 300° F. and having a glass transition temperature between about -10° C. to about -40° C. and said composite having a tensile strength of about 100 pounds per square inch or more and a resistance to elongation of no more than about 2 percent at 20 pounds per inch load.
Claim 3
Dependent Claim
27 words
A composite of claim 1 where the copolymer is a carboxylated acrylonitrile styrene butadiene copolymer having a degree of carboxylation between about 0.5 to about 5.0 percent.
Claim 4
Dependent Claim
31 words
A composite of claim 1 where the saturant further comprises clay in an amount up to about 65 percent by weight clay based on the total weight of copolymer and clay.
Claim 5
Dependent Claim
30 words
A composite of claim 3 where the amount of clay is between about 45 to about 55 percent by weight clay based on the total weight of copolymer and clay.
Claim 6
Dependent Claim
25 words
A composite of claim 1 or claim 2 or claim 3 or claim 4 where the non-woven fiber batt includes polyester fibers of mixed denier.
Claim 7
Dependent Claim
123 words
A composite of claim 1 or claim 2 or claim 3 or claim 4 where the non-woven fiber batt has a thickness between about 0.030 to about 0.050 inches, a weight between about 4.0 to about 8.0 ounces per square yard and comprises from about 20 to about 60 percent by weight of about 6.0 denier polyester fiber and from about 20 to about 60 percent by weight polyester fiber of mixed denier and where the scrim comprises polypropylene yarn and has a weight between about 2.5 ounces to about 3.5 ounces per square yard, a thickness between about 0.010 to about 0.020 inches and a weave consisting of and from about 10 to about 15 threads in the warp and weft direction.
Claim 8
Dependent Claim
140 words
A process for preparing a composite comprising the steps of: a. needle punching a non-woven fiber batt to a woven polymeric scrim, b. saturating the needle punched product with a polymer dispersion comprising a nitrile containing polymer curable at temperatures between about 250° F. to about 300° F. and having a glass transition temperature between about -10° C. to about -40° C. to distribute the polymer throughout the interstices of the product and about the surface of the product and c. heating the saturated product at temperatures between about 250° F. to about 300° F. to dry the saturated product and cure the polymer to provide a composite having a tensile strength of about 100 pounds per square inch or more and a resistance to elongation of no more than about 2 percent at 20 pounds per square inch load.
Claim 9
Dependent Claim
140 words
A process for preparing a composite comprising the steps of: a. needle punching a non-woven fiber batt to a woven polymeric scrim, b. saturating the needle punched product with a polymer dispersion comprising a nitrile containing polymer curable at temperatures between about 250° F. to about 300° F. and having a glass transition temperature between about -10° C. to about -40° C. to distribute the polymer throughout the interstices of the product and about the surface of the product and c. heating the saturated product at temperatures between about 250° F. to about 300° F. to dry the saturated product and cure the polymer to provide a composite having a tensile strength of about 100 pounds per square inch or more and a resistance to elongation of no more than about 2 percent at 20 pounds per square inch load.
Claim 10
Dependent Claim
46 words
A process of claim 7 where the copolymer is an acrylonitrile styrene butadiene copolymer comprising from about 15 to about 35 percent by weight acrylonitrile, from about 20 to about 30 percent by weight styrene and from about 35 to about 65 percent by weight butadiene.
Claim 11
Dependent Claim
27 words
A process of claim 8 where the copolymer is a carboxylated acrylonitrile styrene butadiene copolymer having a degree of carboxylation between about 0.5 to about 5.0 percent.
Claim 12
Dependent Claim
30 words
A process of claim 7 where the saturant further comprises clay in an amount up about 65 percent by weight clay based on the total weight of copolymer and clay.
Claim 13
Dependent Claim
30 words
A process of claim 10 where the amount of clay is between about 45 to about 55 percent by weight clay based on the total weight of copolymer and clay.
Claim 14
Dependent Claim
28 words
A process of claim 7 or claim 8 or claim 9 or claim 10 or claim 11 where the non-woven fiber batt includes polyester fibers of mixed denier.
Claim 15
Dependent Claim
126 words
A process of claim 7 or claim 8 or claim 9 or claim 10 or claim 11 where the non-woven fiber batt has a thickness between about 0.030 to about 0.050 inches, a weight between about 4.0 to about 8.0 ounces per square yard and comprises from about 20 to about 60 percent by weight of about 6.0 denier polyester fiber and from about 20 to about 60 percent by weight polyester fiber of mixed denier and where the scrim comprises polypropylene yarn and has a weight between about 2.5 ounces to about 3.5 ounces per square yard, a thickness between about 0.010 to about 0.020 inches and a weave consisting of and from about 10 to about 15 threads in the warp and weft direction.
References Cited (Backward Citations)
US3312584A
Cited
US3307990A
Cited
US3284872A
Cited
US3546059A
Cited
US4154335A
Cited
US4243446A
Cited
US4172170A
Cited
US4277531A
Cited
US4504538A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-28 | 1990-01-27 | 1990-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-28 | 1994-01-27 | 1994-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-28 | 1998-01-27 | 1998-07-29 | $7700.00 | Window Closed / Lapsed |