Process for producing toner for development of electrostatic images by stepwise suspension polymerizations
Assignee: Canon Inc
•
Filing: 1983-09-27
•
Granted: 1986-07-22
•
Expires: 2003-09-27
Abstract
Abstract A polymerizable mixture containing a monomer, a polymerization initiator and a colorant is subjected to suspension polymerization, and an additional monomer is adsorbed onto the resultant polymer particles and grown by polymerization to give a toner for development of electrostatic charges excellent in toner characteristics such as triboelectric charging characteristic, storage stability and free flowing property.
Inventors
- 👤 Yoshihiko Hyosu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:34
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/087; G03G9/08784; G03G9/08793; C; C08; C08F; C08F2/00; C08F2/44; C08F257/00; C08F257/02; C08F291/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
196 words
A process for producing a toner for developing electrostatically charged images, which comprises the steps of: a. dispersing a polymerizable mixture comprising a polymerizable monomer, a polymerization initiator and a colorant in a dispersion medium in which the polymerizable monomer is substantially insoluble, under sufficient high shearing force as to produce dispersion droplets of the polymerizable mixture in sizes of 4 to 27μ wherein up to about 0.1 wt. % of surfactant based on the polymerizable mixture is present to promote the dispersion medium; b. polymerizing the dispersion of the polymerizable mixture in the dispersion medium to produce polymer particles in a weight average particle size in the range from 4 to 27μ; c. adding 5 to 100 parts by weight of an additional polymerizable monomer per 100 parts by weight of the polymerizable monomer in step a. and an oil-soluble polymerization initiator dissolved in the additional polymerizable monomer into the disperse system containing the polymeric particles formed, to have the monomer adsorbed on the polymeric particles; and d. polymerizing the additional polymerizable monomer thereby to obtain polymer particles as a toner having a weight averge particle size in the range of from 5 to 30μ.
Claim 2
Dependent Claim
196 words
A process for producing a toner for developing electrostatically charged images, which comprises the steps of: a. dispersing a polymerizable mixture comprising a polymerizable monomer, a polymerization initiator and a colorant in a dispersion medium in which the polymerizable monomer is substantially insoluble, under sufficient high shearing force as to produce dispersion droplets of the polymerizable mixture in sizes of 4 to 27μ wherein up to about 0.1 wt. % of surfactant based on the polymerizable mixture is present to promote the dispersion medium; b. polymerizing the dispersion of the polymerizable mixture in the dispersion medium to produce polymer particles in a weight average particle size in the range from 4 to 27μ; c. adding 5 to 100 parts by weight of an additional polymerizable monomer per 100 parts by weight of the polymerizable monomer in step a. and an oil-soluble polymerization initiator dissolved in the additional polymerizable monomer into the disperse system containing the polymeric particles formed, to have the monomer adsorbed on the polymeric particles; and d. polymerizing the additional polymerizable monomer thereby to obtain polymer particles as a toner having a weight averge particle size in the range of from 5 to 30μ.
Claim 3
Dependent Claim
45 words
A process according to claim 1, wherein the additional monomer and the conditions for the step d are selected so that the polymer obtained in the step d will have a glass transition temperature higher than that of the polymer obtained in the step b.
Claim 4
Dependent Claim
35 words
A process according to claim 2, wherein the polymer obtained in the step d has a glass transition temperature higher by 35° C. or more than that of the polymer obtained in the step b.
Claim 5
Dependent Claim
51 words
A process according to claim 1, wherein the additional monomer in the step c is added at a rate equal to or lower than the adsorption rate at which said additional monomer is adsorbed onto the polymer particles, whereby the formation of free liquid droplets of said additional monomer is prevented.
Claim 6
Dependent Claim
12 words
A process according to claim 1, wherein the dispersion medium comprises water.
Claim 7
Dependent Claim
14 words
A process according to claim 5, wherein the dispersion medium further contains a dispersant.
Claim 8
Dependent Claim
38 words
A process according to claim 6, wherein the dispersant comprises a combination of an inorganic dispersing agent and a surfactant, wherein the surfactant is employed in amounts from 0.001 to 0.1 weight percent based on the polymerizable mixture.
Claim 9
Dependent Claim
18 words
A process according to claim 1, wherein the polymerizable monomer in the step a contains a crosslinking agent.
Claim 10
Dependent Claim
18 words
A process according to claim 1, wherein the additional monomer in the step c contains a crosslinking agent.
Claim 11
Dependent Claim
14 words
A process according to claim 1, wherein said polymerizable mixture contains a magnetic material.
Claim 12
Dependent Claim
19 words
A process according to claim 1, wherein the disperse system formed in step a is substantially free of surfactant.
References Cited (Backward Citations)
US3959153A
Cited
GB1435821A
Cited
US4077804A
Cited
GB1538787A
Cited
GB1583564A
Cited
US4459378A
Cited
US4430409A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-21 | 1990-01-20 | 1990-07-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-21 | 1994-01-20 | 1994-07-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-21 | 1998-01-20 | 1998-07-22 | $7700.00 | Window Closed / Lapsed |