Interpolymers of ethylene and unsaturated carboxylic acids
Assignee: DIAMOND TECHNOLOGY PARTNERSHIP Co
•
Filing: 1983-06-13
•
Granted: 1986-07-08
•
Expires: 2003-06-13
Abstract
Abstract Homogeneous, random interpolymers of ethylene and lesser amounts by weight of olefinically-unsaturated comonomers are prepared in a substantially constant environment, substantially steady-state reaction mixture, in a well-stirred autoclave reactor, in continuous single-phase operation, using elevated synthesis conditions wherein the temperature and pressure are elevated to an amount high enough to approach, reach, or surpass the molecular weight distribution boundary.
Inventors
- 👤 Osborne K. McKinney
- 👤 David P. Flores
- 👤 David A. Eversdyk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:12
CPC Classifications
C; C08; C08F; C08F210/00; C08F210/02
Claims Analysis
Total Claims: 47
Claim 1
Independent Claim
209 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of at least one olefinically unsaturated comonomer selected from the group comprising unsaturated carboxylic acids, alkylacrylates, alkyl methacrylates and vinyl esters, said process comprising interpolymerizing the monomers in a substantially constant constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the raection mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer, thereby producing an interpolymer having less gels and/or grain.
Claim 2
Dependent Claim
209 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of at least one olefinically unsaturated comonomer selected from the group comprising unsaturated carboxylic acids, alkylacrylates, alkyl methacrylates and vinyl esters, said process comprising interpolymerizing the monomers in a substantially constant constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the raection mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer, thereby producing an interpolymer having less gels and/or grain.
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein the olefinically-unsaturated comonomer comprises acrylic acid or methacrylic acid.
Claim 4
Dependent Claim
12 words
The process of claim 1 wherein the olefinically-unsaturated comonomer is acrylic acid.
Claim 5
Dependent Claim
11 words
The process of claim 1 wherein the olefinically-unsaturated comonomer is methacrylic
Claim 6
Dependent Claim
32 words
The process of claim 1 wherein the so-produced interpolymers comprise from about 99% to about 88% by weight of ethylene units in the polymer chain, the remaining percentage comprising acrylic acid units.
Claim 7
Dependent Claim
25 words
The process of claim 1 wherein the so-produced interpolymers comprise from about 99% to about 88% by weight of ethylene units in the polymer chain.
Claim 8
Dependent Claim
99 words
The process of claim 1 wherein the synthesis conditions comprise an elevated temperature which is in the range of about 150° C. to about 350° C. and an elevated pressure which is in the range of about 18,000 to about 50,000 psi, wherein said pressure is at least about 2000 psi above, and said temperature is at least 15° above, the minimum amount needed to produce a single-phase reaction mixture and wherein elevated temperature and elevated pressure are sufficient to substantially exceed the temperature and presusre at which the molecular weight distribution boundary of the so-produced interpolymer is reached.
Claim 9
Dependent Claim
152 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to about 35% by weight of at least one copolymerizable olefinically-unsaturated comonomer selected from the group comprising an unsaturated carboxylic acid, alkyl acrylates, alkyl methacrylates and vinyl esters, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 10
Dependent Claim
152 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to about 35% by weight of at least one copolymerizable olefinically-unsaturated comonomer selected from the group comprising an unsaturated carboxylic acid, alkyl acrylates, alkyl methacrylates and vinyl esters, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 11
Dependent Claim
15 words
The process of claim 8 wherein the copolymerizable olefinically-unsaturated comonomer is an unsaturated carboxylic acid.
Claim 12
Dependent Claim
16 words
The process of claim 8 wherein the copolymerizable olefinically-unsaturated comonomer is acrylic acid or methacrylic acid.
Claim 13
Dependent Claim
13 words
The process of claim 8 wherein the copolymerizable olefinically-unsaturated comonomer is acrylic acid.
Claim 14
Dependent Claim
18 words
The process of claim 8 wherein the interpolymer comprises at least about 88% by weight of ethylene groups.
Claim 15
Dependent Claim
213 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising at least one olefinically-unsaturated comonomer selected from the group comprising unsaturated carboxylic acids, alkyl acrylates, alkyl methacrylates and vinyl esters, said interpolymer being further characterized as having a weight average molecular weight/number average molecular weight ratio as defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2)(wt.fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log(MWw/MWn) max . plot for a given comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for a given comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for a given comonomer, C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44 and as having lower levels of gels and/or grain.
Claim 16
Dependent Claim
213 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising at least one olefinically-unsaturated comonomer selected from the group comprising unsaturated carboxylic acids, alkyl acrylates, alkyl methacrylates and vinyl esters, said interpolymer being further characterized as having a weight average molecular weight/number average molecular weight ratio as defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2)(wt.fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log(MWw/MWn) max . plot for a given comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for a given comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for a given comonomer, C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44 and as having lower levels of gels and/or grain.
Claim 17
Dependent Claim
20 words
The interpolymer of claim 13 wherein the ethylene monomer comprises about 88% to about 99% by weight of the polymer.
Claim 18
Dependent Claim
26 words
The interpolymer of claim 13 wherein the ethylene monomer comprises about 88% to about 99% by weight of the polymer and the comonomer comprises acrylic acid.
Claim 19
Dependent Claim
13 words
The interpolymer of claim 13 wherein the comonomer is an olefinically-unsaturated carboxylic acid.
Claim 20
Dependent Claim
11 words
The interpolymer of claim 13 wherein the comonomer is acrylic acid.
Claim 21
Dependent Claim
11 words
The interpolymer of claim 13 wherein the comonomer is methacrylic acid.
Claim 22
Dependent Claim
11 words
The process of claim 1 wherein the comonomer is an alkylacrylate.
Claim 23
Dependent Claim
11 words
The process of claim 1 wherein the comonomer is an alkylmethacrylate.
Claim 24
Dependent Claim
12 words
The process of claim 1 wherein the comonomer is a vinyl ester.
Claim 25
Dependent Claim
11 words
The product of claim 13 wherein the comonomer is an alkylacrylate.
Claim 26
Dependent Claim
11 words
The product of claim 13 wherein the comnomer is an alkylmethacrylate.
Claim 27
Dependent Claim
12 words
The product of claim 13 wherein the comonomer is a vinyl ester.
Claim 28
Dependent Claim
191 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of acrylic acid comonomer, said process comprising interpolymerizing the monomers in a substantially constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the reaction mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer, thereby producing an interpolymer having less gels and/or grain.
Claim 29
Dependent Claim
191 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of acrylic acid comonomer, said process comprising interpolymerizing the monomers in a substantially constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the reaction mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer, thereby producing an interpolymer having less gels and/or grain.
Claim 30
Dependent Claim
25 words
The process of claim 25 wherein the so-produced interpolymers comprise from about 99% to about 88% by weight of ethylene units in the polymer chain.
Claim 31
Dependent Claim
100 words
The process of claim 25 wherein the synthesis conditions comprise an elevated temperature which is in the range of about 150° C. to about 350° C. and an elevated pressure which is in the range of about 18,000 to about 50,000 psi, wherein said pressure is at least about 2000 psi above, and said temperature is at least 15° C. above, the minimum amount needed to produce a single-phase reaction mixture and wherein elevated temperature and elevated pressure are sufficient to substantially exceed the temperature and pressure at which the molecular weight distribution boundary of the so-produced interpolymer is reached.
Claim 32
Dependent Claim
133 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to aboul 35% by weight of acrylic acid comonomer, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 33
Dependent Claim
133 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to aboul 35% by weight of acrylic acid comonomer, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 34
Dependent Claim
18 words
The process of claim 28 wherein the interpolymer comprises at least about 88% by weight of ethylene groups.
Claim 35
Dependent Claim
197 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising acrylic acid comonomer, said interpolymer being further characterized as having a weight average molecular weight/number average molecuar weight ratio a defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2) (wt. fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log (MWw/MWn) max . plot for the comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for the comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the comonomer, and C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44, and as having lower levels of gels and/or grains.
Claim 36
Dependent Claim
197 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising acrylic acid comonomer, said interpolymer being further characterized as having a weight average molecular weight/number average molecuar weight ratio a defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2) (wt. fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log (MWw/MWn) max . plot for the comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for the comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the comonomer, and C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44, and as having lower levels of gels and/or grains.
Claim 37
Dependent Claim
20 words
The interpolymer of claim 30 wherein the ethylene monomer comprises about 88% to about 99% by weight of the polymer.
Claim 38
Dependent Claim
191 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of methacrylic acid comonomer, said process comprising interpolymerizing the monomers in a substantially constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the reaction mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer thereby producing an interpolymer having less gels and/or grain.
Claim 39
Dependent Claim
191 words
A process for producing homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer and about 1% to about 35% by weight of methacrylic acid comonomer, said process comprising interpolymerizing the monomers in a substantially constant environment, under steady state conditions, in a single-phase reaction mixture, under the influence of a free-radical initiator, and in a well-stirred autoclave reactor operated in a continuous manner as the monomers are fed into the reactor and the reaction mixture is withdrawn, said process being characterized by the use of synthesis conditions of temperature and pressure which are elevated to a level high enough above the phase boundary between two-phase and single-phase operation such that the molecular weight distribution (MWD) boundary is reached, or surpassed, the said molecular weight distribution boundary being the highest ratio of weight average molecular weight/number average molecular weight obtainable in single-phase operation, said elevated pressure being greater than 2000 psi above, and said elevated temperature being greater than 15° C. above, the synthesis conditions required at the phase boundary for a given mixture of ethylene and comonomer thereby producing an interpolymer having less gels and/or grain.
Claim 40
Dependent Claim
25 words
The process of claim 32 wherein the so-produced interpolymers comprise from about 99% to about 88% by weight of ethylene units in the polymer chain.
Claim 41
Dependent Claim
100 words
The process of claim 32 wherein the synthesis conditions comprise an elevated temperature which is in the range of about 150° C. to about 350° C. and an elevated pressure which is in the range of about 18,000 to about 50,000 psi, wherein said pressure is at least about 2000 psi above, and said temperature is at least 15° C. above, the minimum amount needed to produce a single-phase reaction mixture and wherein elevated temperature and elevated pressure are sufficient to substantially exceed the temperature and pressure at which the molecular weight distribution boundary of the so-produced interpolymer is reached.
Claim 42
Dependent Claim
133 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to about 35% by weight of methacrylic acid comonomer, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 43
Dependent Claim
133 words
A process for producing substantially homogeneous, random interpolymers comprising about 99% to about 65% by weight of ethylene monomer with about 1% to about 35% by weight of methacrylic acid comonomer, said process comprising interpolymerizing the monomers in a well-stirred autoclave reactor operated in a continuous manner at steady state conditions using a free-radical polymerization initiator under substantially constant conditions of temperature, pressure, and flow rates, wherein the conditions of temperature and pressure required to produce operation at the phase boundary are exceeded, respectively, by using a temperature of at least 15° C. above that at the phase boundary and a pressure of more than 2000 psi above that at the phase boundary, whereby the molecular weight distribution (MWD) boundary is reached or surpassed, thereby producing an interpolymer having less gels and/or grain.
Claim 44
Dependent Claim
18 words
The process of claim 35 wherein the interpolymer comprises at least about 88% by weight of ethylene groups.
Claim 45
Dependent Claim
195 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising methacrylic acid comonomer, said interpolymer being further characterized as having a weight average molecular weight/number average molecular weight ratio as defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2)(wt.fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for the comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the given comonomer, and C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44, and as having lower levels of gels and/or grains.
Claim 46
Dependent Claim
195 words
A random, homogeneous, single-phase interpolymer product comprising about 65% to about 99% by weight of ethylene monomer, the remaining percentage comprising methacrylic acid comonomer, said interpolymer being further characterized as having a weight average molecular weight/number average molecular weight ratio as defined by the formula log(MWw/MWn)=(C.sub.1 +(C.sub.2)(wt.fraction comonomer))×(C.sub.4) where MWw is the weight average molecular weight, MWn is the number average molecular weight, C 1 is the intercept of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the comonomer, where (MWw/MWn) max . is the ratio of weight average molecular weight to number average molecular weight at the MWD boundary for the comonomer, C 2 is the slope of the wt. fraction comonomer versus log(MWw/MWn) max . plot for the given comonomer, and C 4 is a numerical value in the range of about 1.0 to about 0.1, representing conditions at, and beyond, the MWD boundary, with C 4 being equal to unity at the MWD boundary, said interpolymer being further characterized as having a ratio of weight percent adjacent comonomer unit to total weight percent comonomer in the polymer of less than 0.44, and as having lower levels of gels and/or grains.
Claim 47
Dependent Claim
20 words
The interpolymer of claim 37 wherein the ethylene monomer comprises about 88% to about 99% by weight of the polymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |