US4599320A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Refractory lining material for electrolytic reduction cell for aluminum production and method of making the same
Assignee: Rio Tinto Alcan International Ltd
•
Filing: 1983-12-27
•
Granted: 1986-07-08
•
Expires: 2003-12-27
Abstract
Abstract A method of making a refractory material, e.g. suitable for use in lining Al electrolytic cells, comprises passing molten Al containing suspended particles of a transition metal diboride (e.g. TiB 2 ) through a refractory filter, on and in which the particles are deposited. The filter can be used as it is, or compressed and sintered, or comminuted and formed into bodies. The concentration of the diboride may be at least 25% on the upstream surface of the filter but progressively reduced with increasing distance from that surface.
Inventors
- 👤 Martin R. Reeve
- 👤 Adam J. Gesing
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:33
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/653; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/64; C04B35/65; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/51; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C25; C25C; C25C3/00; C25C3/06; C25C3/08
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
101 words
A method of making a composite refractory material containing a proportion of transition metal diboride particles characterized by establishing a body of molten aluminium containing suspended transition metal diboride particles, filtering said molten aluminium by passing it through a body of a refractory substance other than said transition metal diboride, said refractory substance being inert with respect to aluminium metal and the transition metal diboride and insoluble in aluminium metal, to deposit said transition metal diboride particles on and in said body of refractory substance, and then subjecting the refractory substance carrying the transition metal diboride particles to a sintering operation.
Claim 2
Independent Claim
101 words
A method of making a composite refractory material containing a proportion of transition metal diboride particles characterized by establishing a body of molten aluminium containing suspended transition metal diboride particles, filtering said molten aluminium by passing it through a body of a refractory substance other than said transition metal diboride, said refractory substance being inert with respect to aluminium metal and the transition metal diboride and insoluble in aluminium metal, to deposit said transition metal diboride particles on and in said body of refractory substance, and then subjecting the refractory substance carrying the transition metal diboride particles to a sintering operation.
Claim 3
Dependent Claim
17 words
A method according to claim 1, further characterized in that the transition metal diboride is titanium diboride.
Claim 4
Dependent Claim
31 words
A method according to claim 1, further characterized in that said other refractory substance is selected for properties of resistance to attack by molten aluminium for use in aluminium reduction cells.
Claim 5
Dependent Claim
24 words
A method according to claim 1, further characterized in that said body of refractory substance is constituted by a body of loose refractory granules.
Claim 6
Dependent Claim
42 words
A method according to claim 1, further characterized in that said body of refractory substance is in the form of a coherent porous mass, permeable to aluminium, said method including collecting a transition metal diboride-rich layer adjacent one face of said mass.
Claim 7
Dependent Claim
35 words
A method according to claim 1, further characterized in that after passage of transition metal diboride-bearing molten aluminium, said body of refractory substance is comminuted, formed into green shapes and fired to form ceramic bodies.
Claim 8
Dependent Claim
27 words
A method according to claim 6, further characterized in that said comminuted refractory materials are mixed with reactive alumina or silicon powder before forming into green shapes.
Claim 9
Dependent Claim
36 words
A method according to claim 6, further characterized in that silicon is incorporated in said comminuted refractory material and the green shapes are fired in a nitrogen atmosphere to promote the growth of silicon nitride therein.
Claim 10
Dependent Claim
36 words
A method according to claim 5, wherein the mass incldes aluminium metal or an alloy thereof and the sintering operation is carried out in a nitrogen atmosphere so as to promote the formation of aluminium nitride.
References Cited (Backward Citations)
US3198625A
Cited
US4257810A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |