Assignee: Atlantic Richfield Co
•
Filing: 1985-03-15
•
Granted: 1986-07-08
•
Expires: 2005-03-15
Abstract
Abstract An electrically enhanced liquid jet process particularly adapted for forming scribe lines on thin film material deposited during fabrication of thin film solar cell devices. A narrow jet of liquid solution is directed onto a thin film along a desired line while an electrical current is passed through the liquid jet and the film being processed. The liquid solution is selected to remove material along the desired line only at its point of contact with the film but to be substantially nonreactive with the film in all other areas where there is an absence of electrical enhancement.
Inventors
- 👤 David L. Bender
- 👤 Kim W. Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:13
CPC Classifications
C; C25; C25F; C25F3/00; C25F3/02; C25F3/14; H; H10; H10F; H10F71/00; H10F71/138; H10F71/1385; H10F77/00; H10F77/20; H10F77/206; H10F77/211; H10P; H10P72/00; H10P72/04; H10P72/0402; H10P72/0406; H10P72/0411; H10P72/0414; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
83 words
A method of scribing a thin film of aluminum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of aluminum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent nitric acid in water.
Claim 2
Independent Claim
83 words
A method of scribing a thin film of aluminum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of aluminum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent nitric acid in water.
Claim 3
Independent Claim
89 words
A method of scribing a thin film of aluminum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of aluminum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 6 percent to about 10 percent NaCl by weight dissolved in water.
Claim 4
Independent Claim
89 words
A method of scribing a thin film of aluminum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of aluminum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 6 percent to about 10 percent NaCl by weight dissolved in water.
Claim 5
Independent Claim
87 words
A method of scribing a thin film of tin oxide deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of tin oxide along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 30% hydrocloric acid by weight dissolved in water.
Claim 6
Independent Claim
87 words
A method of scribing a thin film of tin oxide deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of tin oxide along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 30% hydrocloric acid by weight dissolved in water.
Claim 7
Independent Claim
96 words
A method of scribing a thin film of molybdenum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of molybdenum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent to 10 pcercent hydrocloric acid acid and about 5 percent to 10 percent NaCl dissolved in water.
Claim 8
Independent Claim
96 words
A method of scribing a thin film of molybdenum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of molybdenum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent to 10 pcercent hydrocloric acid acid and about 5 percent to 10 percent NaCl dissolved in water.
Claim 9
Independent Claim
92 words
A method of scribing a thin film of molybdenum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of molybdenum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent nitric acid and about 5 percent to 10 percent NaCl dissolved in water.
Claim 10
Independent Claim
92 words
A method of scribing a thin film of molybdenum deposited on a substrate to form part of a thin film solar cell comprising: contacting the thin film of molybdenum along a desired scribe line with a jet of etching solution having a diameter of about 0.002 to about 0.008 inch while passing an electric current of about 0.020 to about 0.100 ampere through a circuit including said jet and said thin film, said etching solution comprising about 5 percent nitric acid and about 5 percent to 10 percent NaCl dissolved in water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |