Abstract
Abstract Low signal attenuation optical fibers and methods for making such fibers mimimize the internal and interface defects while providing high throughput by radial deposition of successive particulate layers about a small diameter start element and co-vitrification of the layers followed by drawing to the small final diameter that is desired. Radial vapor deposition of an interface layer on the start element, followed by an encompassing core and then a cladding provides boundaries that form transitional continuums after the structure has been vitrified. The start element remains as part of the core but is so small as to have no discernible effect on light propagation, and the number of interfaces in the light propagating portion is limited by maintaining the ratio of the cladding thickness to the core radius to less than 1.5 in the initial preform. By drawing this preform to form separate rods, additional cladding is applied to form a fiber preform from which optical fibers may be drawn.
Inventors
- 👤 Arnab Sarkar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:40
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01486; C03B37/01493; C03B37/01466; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/24; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
128 words
A process for producing optical fiber which comprises: depositing a soot comprising silica by vapor deposition along the length of a rotating thin silica target rod, to produce a first porous preform having both core and cladding portions; sintering said first porous preform with said target rod in place. drawing said sintered preform to a rod, to diminish the dimensions of said thin target rod, depositing a soot comprising silica on said drawn rod by vapor deposition along the length of said drawn rod to produce a fiber preform having both sintered and porous portions; sintering said fiber preform with said drawn rod remaining in place; and drawing said sintered fiber preform to further diminish the dimensions of said thin target rod and to provide an optical fiber.
Claim 2
Dependent Claim
128 words
A process for producing optical fiber which comprises: depositing a soot comprising silica by vapor deposition along the length of a rotating thin silica target rod, to produce a first porous preform having both core and cladding portions; sintering said first porous preform with said target rod in place. drawing said sintered preform to a rod, to diminish the dimensions of said thin target rod, depositing a soot comprising silica on said drawn rod by vapor deposition along the length of said drawn rod to produce a fiber preform having both sintered and porous portions; sintering said fiber preform with said drawn rod remaining in place; and drawing said sintered fiber preform to further diminish the dimensions of said thin target rod and to provide an optical fiber.
Claim 3
Dependent Claim
42 words
The process of claim 1, including initially depositing by vapor deposition a thin layer of silica soot on said rotating target rod to provide a soot interface of the same composition as said target rod between said target rod and said core.
Claim 4
Dependent Claim
82 words
The process of claim 1, wherein the step of producing a first porous preform comprises first depositing on the target rod a predetermined amount of silica containing a dopant that raises the refractive index and then depositing an additional layer of silica on said core, to form at least a portion of the cladding of the optical fiber, the ratio of the thickness (t) of the cladding to the radius (a) of the core being less than 1.5 in the drawn rod.
Claim 5
Dependent Claim
45 words
The process of claim 3, wherein the step of depositing silica soot on the drawn rod comprises depositing sufficient soot to provide an overall t/a ratio of from 10 to 30, and wherein the process generates only glass-soot interfaces of like material and soot-soot interfaces.
Claim 6
Dependent Claim
41 words
The process of claim 4, wherein said target has a diameter of the less than 10 mm, wherein the first porous preform is in excess of 300 gms, and wherein the drawn sintered rod is less than 10 mm in diameter.
Claim 7
Dependent Claim
98 words
The process of claim 1, wherein said soot comprising silica and a dopant forming said core, and said soot of silica forming said cladding, are each deposited in the form of layers of a dense but porous soot preform, by traversing discharge of said soot back and forth initially along the length of the rotating target rod and thereafter along the prior deposits, said layers of soot forming said core and said layer of soot forming said cladding being deposited to a predetermined thickness with the deposit of dopant being terminated at the interface between core and cladding.
Claim 8
Dependent Claim
34 words
The process of claim 6, wherein the amount of deposited soot is determined by weighing the rotating structure during deposition, and further including the step of continually heating the ends of the rotating preform.
Claim 9
Dependent Claim
44 words
The process of claim 7, wherein the first porous preform is sintered by being fed into a heated controlled environment at a rate of 0.2 to 0.35 cm/min, and wherein the sintered preform is drawn to a rod at a temperature of 1930°-2030° C.
Claim 10
Dependent Claim
25 words
The process of claim 8, the number of originally glass-soot interfaces within the light carrying region of said optical fiber being not more than 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-07 | 1990-01-06 | 1990-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-07 | 1994-01-06 | 1994-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-07 | 1998-01-06 | 1998-07-08 | $7700.00 | Window Closed / Lapsed |