Abstract A heat resistant resin composition comprising from 10 to 90% by weight of a copolymer A and from 90 to 10% by weight of a copolymer B, in which the copolymer A is composed of an N-aromatic maleimide monomer residue, a maleimide monomer residue, a vinyl aromatic monomer residue and, optionally other vinyl monomer residue, the total content of the N-aromatic maleimide monomer residue and the maleimide monomer residue being from 10 to 45%, the content of the N-aromatic maleimide monomer residue being greater than the content of the maleimide monomer residue, the content of the vinyl aromatic monomer residue being from 90 to 55% and the content of said other vinyl monomer residue being from 0 to 20%, and the copolymer B is composed of a vinyl cyanide monomer residue, a vinyl aromatic monomer residue and, optionally other vinyl monomer residue, the content of the vinyl cyanide monomer residue being from 20 to 55%, the content of the vinyl aromatic monomer residue being from 80 to 45% and the content of said other vinyl monomer residue being from 0 to 20%.
A process for preparing a heat resistant resin composition which comprises bulk-polymerising a vinyl aromatic monomer with from 10 to 45 molar % of a maleic acid anhydride monomer to obtain a syrup composed substantially of a first copolymer and an unreacted vinyl aromatic monomer, adding a vinyl cyanide monomer to this syrup in such an amount that the content of the vinyle cyanide monomer residue in a second copolymer to be formed by its reaction with the unreacted vinyl aromatic monomer becomes from 20 to 55%, subjecting the mixture to suspension polymerization to polymerize the unreacted vinyl aromatic monomer with the vinyl cyanide monomer to form the second copolymer, then adding an aromatic amine and ammonia to the suspension system in a total amount by mole of from 0.8 to 1.5 times the amount by mole of the maleic acid anhydride to convert the maleic acid anhydride residue in the first copolymer to its imide.
Claim 2
Dependent Claim
156 words
A process for preparing a heat resistant resin composition which comprises bulk-polymerising a vinyl aromatic monomer with from 10 to 45 molar % of a maleic acid anhydride monomer to obtain a syrup composed substantially of a first copolymer and an unreacted vinyl aromatic monomer, adding a vinyl cyanide monomer to this syrup in such an amount that the content of the vinyle cyanide monomer residue in a second copolymer to be formed by its reaction with the unreacted vinyl aromatic monomer becomes from 20 to 55%, subjecting the mixture to suspension polymerization to polymerize the unreacted vinyl aromatic monomer with the vinyl cyanide monomer to form the second copolymer, then adding an aromatic amine and ammonia to the suspension system in a total amount by mole of from 0.8 to 1.5 times the amount by mole of the maleic acid anhydride to convert the maleic acid anhydride residue in the first copolymer to its imide.
Claim 3
Dependent Claim
25 words
The process according to claim 1 wherein the amount by mole of the aromatic amine is greater than the amount by mole of the ammonia.
Claim 4
Dependent Claim
26 words
The process according to claim 1 wherein the bulk-polymerization is conducted at a temperature of from 90° to 130° C. for from 1 to 10 hours.
Claim 5
Dependent Claim
27 words
The process according to claim 1 wherein the suspension polymerization is conducted at a temperature of from 60° to 160° C. for from 1 to 10 hours.
Claim 6
Dependent Claim
35 words
The process according to claim 1 wherein the reaction to convert the maleic anhydride residue to its imide is conducted at a temperature of from 120° to 160° C. for from 0.5 to 3 hours.