Composite structure for rotating anode of an X-ray tube
Assignee: General Electric Co
•
Filing: 1984-04-25
•
Granted: 1986-06-24
•
Expires: 2004-04-25
Abstract
Abstract In a composite anode structure having a refractory metal portion with a graphite portion attached thereto, an intersparsed zirconium brazing layer is isolated from the graphite material by a thin layer of platinum to thereby prevent the formation of embrittling carbides when the combination is raised to operating temperatures. The platinum is mechanically bonded to the graphite, and the zirconium is diffusion bonded to both the molybdenum portion and the platinum layer to form a high-strength, lasting bond.
Inventors
- 👤 Edward Akpan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:31
CPC Classifications
H; H01; H01J; H01J35/00; H01J35/02; H01J35/04; H01J35/08; H01J35/10; H01J35/108
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
85 words
An X-ray tube target comprising a graphite substrate forming a portion of the target and having an upper surface; a platinum layer bonded to said substrate upper surface; a zirconium layer bonded to said platinum layer and isolated by said platinum layer from said substrate so as not to be susceptible to the formation of carbides when exposed to higher temperatures; and a metal portion bonded to said zirconium layer and having on its exposed surface a focal track for receiving electrons for producing X-rays.
Claim 2
Dependent Claim
85 words
An X-ray tube target comprising a graphite substrate forming a portion of the target and having an upper surface; a platinum layer bonded to said substrate upper surface; a zirconium layer bonded to said platinum layer and isolated by said platinum layer from said substrate so as not to be susceptible to the formation of carbides when exposed to higher temperatures; and a metal portion bonded to said zirconium layer and having on its exposed surface a focal track for receiving electrons for producing X-rays.
Claim 3
Dependent Claim
22 words
An X-ray tube target as set forth in claim 1 wherein said platinum layer is no greater than 1/16 mils in thickness.
Claim 4
Dependent Claim
24 words
An X-ray tube target as set forth in claim 1 wherein the thickness of said platinum layer is in the range of 5-10 angstroms.
Claim 5
Dependent Claim
22 words
An X-ray tube target as set forth in claim 1 wherein said zirconium layer is no greater than 2 mils in thickness.
Claim 6
Dependent Claim
23 words
An X-ray tube target as set forth in claim 1 wherein said metal portion is comprised of a molybdenum or molybdenum alloy material.
Claim 7
Dependent Claim
57 words
A composite target for an X-ray tube comprising a graphite substrate portion and a metal portion, the two portions being bonded together by successive interspersed layers of platinum and zirconium, wherein said platinum layer is disposed between said graphite substrate portion and said zirconium layer and wherein said platinum layer is less than 1/16 mils in thickness.
Claim 8
Dependent Claim
57 words
A composite target for an X-ray tube comprising a graphite substrate portion and a metal portion, the two portions being bonded together by successive interspersed layers of platinum and zirconium, wherein said platinum layer is disposed between said graphite substrate portion and said zirconium layer and wherein said platinum layer is less than 1/16 mils in thickness.
Claim 9
Dependent Claim
20 words
A composite target as set forth in claim 1 wherein said zirconium layer is less than 2 mils in thickness.
Claim 10
Dependent Claim
82 words
In a composite X-ray target of the type having a graphite substrate portion to which a metal portion is attached, a bonding structure comprising a first layer formed of a noncarbide-forming material selected from the group consisting of platinum, palladium and rhodium bonded to said graphite portion, and a second layer composed of zirconium and disposed between and acting to bond said target together, wherein said noncarbide-forming material isolates said zirconium layer from said graphite portion to prevent the formation of carbides.
Claim 11
Dependent Claim
82 words
In a composite X-ray target of the type having a graphite substrate portion to which a metal portion is attached, a bonding structure comprising a first layer formed of a noncarbide-forming material selected from the group consisting of platinum, palladium and rhodium bonded to said graphite portion, and a second layer composed of zirconium and disposed between and acting to bond said target together, wherein said noncarbide-forming material isolates said zirconium layer from said graphite portion to prevent the formation of carbides.
Claim 12
Dependent Claim
17 words
A bonding structure as set forth in claim 8 wherein said first layer is composed of platinum.
Claim 13
Independent Claim
90 words
A method of joining a metal portion of an X-ray tube target to a graphite substrate portion thereof comprising the steps of (1) applying a first layer to one face of the graphite substrate portion, said first layer being composed of a noncarbide-forming material; (2) applying a layer of zirconium to said first layer, which zirconium layer is isolated from said substrate by said noncarbide-forming material; (3) placing the metal portion over said zirconium layer; and (4) heating the combination to thereby braze the metal portion to the graphite portion.
Claim 14
Independent Claim
90 words
A method of joining a metal portion of an X-ray tube target to a graphite substrate portion thereof comprising the steps of (1) applying a first layer to one face of the graphite substrate portion, said first layer being composed of a noncarbide-forming material; (2) applying a layer of zirconium to said first layer, which zirconium layer is isolated from said substrate by said noncarbide-forming material; (3) placing the metal portion over said zirconium layer; and (4) heating the combination to thereby braze the metal portion to the graphite portion.
Claim 15
Dependent Claim
25 words
A method as set forth in claim 10 wherein said first layer is applied by screen printing said noncarbide-forming material on the graphite substrate portion.
Claim 16
Dependent Claim
22 words
A method as set forth in claim 10 wherein said first layer is applied with a thickness of less than 1/16 mils.
Claim 17
Dependent Claim
21 words
A method as set forth in claim 10 wherein said zirconium layer is applied with a thickness not exceeding 2 mils.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-23 | 1989-12-23 | 1990-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-23 | 1993-12-23 | 1994-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-23 | 1997-12-23 | 1998-06-24 | $7700.00 | Window Closed / Lapsed |