Method of making self-promoted hydrotreating catalysts
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1984-12-11
•
Granted: 1986-06-17
•
Expires: 2004-12-11
Abstract
Abstract Self-promoted molybdenum and tungsten sulfide hydrotreating catalysts are prepared by heating one or more water soluble catalyst precursors in a non-oxidizing atmosphere in the presence of sulfur at a temperature of at least about 200 DEG C. The precursors will be one or more compounds of the formula ML(MoyW1-yO4) wherein M is one or more promoter metals selected from the group consisting essentially of Mn, Fe, Co, Ni, Cu, Zn and mixtures thereof, wherein O</=y</=1 and wherein L is a nitrogen containing, neutral multidentate, chelating ligand. In a preferred embodiment the ligand L will comprise one or more chelating alkyl di or triamines and the non-oxidizing atmosphere will comprise H2S.
Inventors
- 👤 Teh C. Ho
- 👤 Larry E. McCandlish
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 05:12
CPC Classifications
B; B01; B01J; B01J31/00; B01J31/16; B01J31/1616; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J27/00; B01J27/02; B01J27/04; B01J27/047; B01J31/18; B01J31/1805; B01J37/00; B01J37/20; C; C10; C10G; C10G45/00; C10G45/02; C10G45/04; C10G45/06; C10G45/08; B01J2531/00; B01J2531/10; B01J2531/16; B01J2531/20; B01J2531/26; B01J2531/70; B01J2531/72; B01J2531/80; B01J2531/84; B01J2531/842; B01J2531/845; B01J2531/847
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
133 words
A process for preparing a supported, self-promoted catalyst, said process comprising: (i) compositing a porous, inorganic refractory oxide support with a water soluble catalyst precursor salt characterized by (ML) (Mo y W 1-y O 4 ) wherein M comprises one or more divalent promoter metals selected from the group consisting of Mn, Fe, Co, Ni, Cu, Zn and mixtures thereof, wherein y is any value ranging from 0 to 1, and wherein L is one or more neutral, nitrogen-containing ligands at least one of which is a chelating polydentate ligand; and (ii) heating said composite formed in (i) in a non-oxidizing atmosphere in the presence of excess sulfur in the form of one or more sulfur bearing compounds and at a temperature of at least about 200° C. to form said self-promoted catalyst.
Claim 2
Dependent Claim
133 words
A process for preparing a supported, self-promoted catalyst, said process comprising: (i) compositing a porous, inorganic refractory oxide support with a water soluble catalyst precursor salt characterized by (ML) (Mo y W 1-y O 4 ) wherein M comprises one or more divalent promoter metals selected from the group consisting of Mn, Fe, Co, Ni, Cu, Zn and mixtures thereof, wherein y is any value ranging from 0 to 1, and wherein L is one or more neutral, nitrogen-containing ligands at least one of which is a chelating polydentate ligand; and (ii) heating said composite formed in (i) in a non-oxidizing atmosphere in the presence of excess sulfur in the form of one or more sulfur bearing compounds and at a temperature of at least about 200° C. to form said self-promoted catalyst.
Claim 3
Dependent Claim
40 words
The process of claim 1 wherein said promoter metal M comprises at least one metal selected from the group consisting of (a) Fe, Co, Ni and mixtures thereof and (b) mixtures of (a) with Zn, Cu, Mn and mixtures thereof.
Claim 4
Dependent Claim
22 words
The process of claim 2 wherein L has a total denticity of six and is one or more chelating, polydentate alkyl amines.
Claim 5
Dependent Claim
14 words
The process of claim 3 wherein said sulfur bearing compound comprises H 2 S.
Claim 6
Dependent Claim
14 words
The process of either of claims 3 or 4 wherein said support comprises alumina.
Claim 7
Dependent Claim
15 words
The process of either of claims 1 or 2 wherein said support comprises chromium oxide.
Claim 8
Dependent Claim
19 words
The process of claim 6 wherein said chromium oxide support is supported on a refractory, inorganic oxide support material.
References Cited (Backward Citations)
US2715603A
Cited
US2914462A
Cited
US3074783A
Cited
US3148135A
Cited
US3686137A
Cited
US3893947A
Cited
US3965041A
Cited
US4243553A
Cited
US4243554A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |