Catalyst rejuvenation process for removal of metal contaminants
Assignee: IFP Energies nouvelles
•
Filing: 1984-04-30
•
Granted: 1986-06-17
•
Expires: 2004-04-30
Abstract
Abstract Spent catalysts removed from a catalytic hydrogenation process for hydrocarbon feedstocks, and containing carbon undesired metals contaminants deposits, are rejuvenated for reuse. Following solvent washing to remove process oils, the catalyst is treated either with chemicals which form sulfate or oxysulfate compounds with the metals contaminants, or with acids which remove the metal contaminants, such as 5-50 W % sulfuric acid in aqueous solution and 0-10 W % ammonium ion solutions to substantially remove the metals deposits. The acid treating occurs within the temperature range of 60 DEG -250 DEG F. for 5-120 minutes at substantially atmospheric pressure, after which the rejuvenated catalyst containing carbon deposits can be effectively reused in the catalytic hydrogenation process.
Inventors
- 👤 Partha S. Ganguli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:40
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/90; B01J23/94; C; C10; C10G; C10G1/00; C10G1/08; C10G1/086; C10G47/00; C10G47/02; Y; Y10; Y10S; Y10S502/00; Y10S502/515; Y10S502/516
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
126 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst containing metals and carbon deposits with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with an aqueous solution consisting of sulfuric acid solution and an ammonium ion which converts the metal contaminants to their respective sulfate compounds and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove the metal contaminants from the catalysts; and (c) washing the treated catalyst to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 2
Dependent Claim
126 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst containing metals and carbon deposits with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with an aqueous solution consisting of sulfuric acid solution and an ammonium ion which converts the metal contaminants to their respective sulfate compounds and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove the metal contaminants from the catalysts; and (c) washing the treated catalyst to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 3
Dependent Claim
27 words
The process of claim 1, wherein the aqueous solution used for treating the oil-free catalyst is 5-50 W % sulfuric acid and 0-10 W % ammonium ion.
Claim 4
Dependent Claim
54 words
The process of claim 1, wherein the used catalyst is removed from a coal liquefaction process and contains deposits comprising iron, titanium, calcium, and sodium, and said catalyst is treated with dilute sulfuric acid and ammonium ion solution at 60°-250° F. temperature for a time sufficient to remove the metal deposits from the catalyst.
Claim 5
Dependent Claim
56 words
The process of claim 1, wherein the used catalyst is removed from a petroleum residua conversion process and contains deposits of iron, vanadium and nickel, and said catalyst is treated with 5-50 W % sulfuric acid and ammonium ions solutions at 60°-250° F. temperature for a time sufficient to remove the metal deposits from the catalyst.
Claim 6
Dependent Claim
13 words
The process of claim 1, wherein the catalyst treating time is 5-120 minutes.
Claim 7
Dependent Claim
133 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in a process for upgrading hydrocarbons, comprising: (a) washing the used catalyst containing metal and carbon deposits with a hydrocarbon solvent to remove process oils; (b) washing the oil-free catalyst with water to substantially fill the catalyst pores with water; (c) treating the catalyst having pores substantially water filled with an aqueous acid solution which removes the metal contaminants and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove metal contaminants from the catalyst; and (d) washing the treated catalyst with a polar solvent to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 8
Dependent Claim
133 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in a process for upgrading hydrocarbons, comprising: (a) washing the used catalyst containing metal and carbon deposits with a hydrocarbon solvent to remove process oils; (b) washing the oil-free catalyst with water to substantially fill the catalyst pores with water; (c) treating the catalyst having pores substantially water filled with an aqueous acid solution which removes the metal contaminants and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove metal contaminants from the catalyst; and (d) washing the treated catalyst with a polar solvent to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 9
Dependent Claim
28 words
The process of claim 6, wherein the oil free catalyst is treated with an acid selected from the group consisting of sulfuric, sulfonic, nitric, acetic and citric acids.
Claim 10
Dependent Claim
125 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in a process for upgrading hydrocarbon feed materials, the process comrising; (a) washing the used catalyst containing metals and carbon deposits with a hydrocaron solvent to remove process oils; (b) treating the oil-free catalyst with a 5-10 W% aqueous solution of ammonium peroxydisulfate which converts the metal contaminants to their respective sulfate compounds at a temperature within the range of 60° to 150° F. for at least about 5 minutes to remove the metal contaminants from the catalyst; and (c) washing the treated catalyst to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 11
Dependent Claim
125 words
A catalyst rejuvenation process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in a process for upgrading hydrocarbon feed materials, the process comrising; (a) washing the used catalyst containing metals and carbon deposits with a hydrocaron solvent to remove process oils; (b) treating the oil-free catalyst with a 5-10 W% aqueous solution of ammonium peroxydisulfate which converts the metal contaminants to their respective sulfate compounds at a temperature within the range of 60° to 150° F. for at least about 5 minutes to remove the metal contaminants from the catalyst; and (c) washing the treated catalyst to remove the aqueous solution, thereby providing a rejuvenated catalyst containing substantially all the carbon deposits of the used catalyst.
Claim 12
Dependent Claim
24 words
The process of claim 8, wherein said hydrocarbon feed materials are selected from the group consisting of, shale oil, tar sand bitumen and petroleum.
References Cited (Backward Citations)
US2668798A
Cited
US2704281A
Cited
US3220956A
Cited
US3562150A
Cited
US3839191A
Cited
US3791989A
Cited
US4007131A
Cited
US4301125A
Cited
US4089806A
Cited
US4268415A
Cited
US4267032A
Cited
US4454240A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-16 | 1989-12-16 | 1990-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-16 | 1993-12-16 | 1994-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-16 | 1997-12-16 | 1998-06-17 | $7700.00 | Window Closed / Lapsed |