US4594202A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making cylindrical fibrous filter structures
Assignee: Pall Corp
•
Filing: 1984-01-06
•
Granted: 1986-06-10
•
Expires: 2004-01-06
Abstract
Abstract Cylindrical fibrous structures comprising a fibrous mass of nonwoven, synthetic, polymeric microfibers wherein the microfibers are substantially free of fiber-to-fiber bonding and secured to each other by mechanical entanglement of intertwining, the fiber structure having a substantially constant voids volume over at least a substantial portion of the structure and, preferably, a graded fiber diameter structure, both as measured in the radial direction. The structures are particularly useful as depth filters. The process for preparing such fibrous structures comprises the steps of: (a) extruding synthetic, polymeric material from a fiberizing die and attenuating the extruded polymeric material to form microfibers by the application of one or more gas streams directed toward a rotating mandrel and a forming roll in operative relationship with the mandrel; (b) cooling the synthetic, polymeric microfibers prior to their collection on the mandrel to a temperature below that at which they bond or fuse together, thereby substantially eliminating fiber-to-fiber bonding; and (c) collecting the cooled microfibers on the mandrel as a nonwoven, synthetic fibrous mass while applying a force on the exterior surface of the collected microfibers by the forming roll; wherein the process variables are controlled to form the cylindrical fiber structure with at least the major portion of the fibrous mass having a substantially constant voids volume.
Inventors
- 👤 David B. Pall
- 👤 Colin F. Harwood
- 👤 Arthur Bradley
- 👤 Timothy R. Brennan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:35
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/08; D01D5/098; D01D5/0985; B; B01; B01D; B01D39/00; B01D39/14; B01D39/16; B01D39/1607; B01D39/1623; B01D39/163; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/56; D04H3/00; D04H3/02; D04H3/07; D04H3/077; D04H3/08; D04H3/16; B01D2239/00; B01D2239/04; B01D2239/06; B01D2239/065; B01D2239/0654; B01D2239/069; B01D2239/0695; B01D2239/10; B01D2239/12; B01D2239/1233
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
197 words
A method of manufacturing a cylindrical fibrous structure comprising a fibrous mass of nonwoven, synthetic, polymeric microfibers, said microfibers substantially free of fiber-to-fiber bonding and secured to each other by mechanical entanglement or intertwining, comprising the steps of: (a) extruding synthetic, polymeric material from a fiberizing die and attenuating said extruded polymeric material to form said synthetic, polymeric microfibers by the application of one or more gas streams directed toward a rotating, reciprocating mandrel and a rotating forming roll in operative relationship with said mandrel; (b) cooling said synthetic, polymeric microfibers prior to their collection on said mandrel to a temperature below that at which said microfibers bond or fuse to each other, thereby substantially eliminating fiber-to-fiber bonding; and (c) collecting said cooled microfibers on said mandrel as a nonwoven, synthetic fibrous mass while applying a force to the exterior surface of the collected microfibers by said forming roll; wherein the process variables are controlled to form said cylindrical fibrous structure with said fibrous mass having a substantially constant voids volume and varying fiber diameter over at least a substantial portion thereof as measured in the radial direction to achieve a varying pore size over said portion.
Claim 2
Independent Claim
197 words
A method of manufacturing a cylindrical fibrous structure comprising a fibrous mass of nonwoven, synthetic, polymeric microfibers, said microfibers substantially free of fiber-to-fiber bonding and secured to each other by mechanical entanglement or intertwining, comprising the steps of: (a) extruding synthetic, polymeric material from a fiberizing die and attenuating said extruded polymeric material to form said synthetic, polymeric microfibers by the application of one or more gas streams directed toward a rotating, reciprocating mandrel and a rotating forming roll in operative relationship with said mandrel; (b) cooling said synthetic, polymeric microfibers prior to their collection on said mandrel to a temperature below that at which said microfibers bond or fuse to each other, thereby substantially eliminating fiber-to-fiber bonding; and (c) collecting said cooled microfibers on said mandrel as a nonwoven, synthetic fibrous mass while applying a force to the exterior surface of the collected microfibers by said forming roll; wherein the process variables are controlled to form said cylindrical fibrous structure with said fibrous mass having a substantially constant voids volume and varying fiber diameter over at least a substantial portion thereof as measured in the radial direction to achieve a varying pore size over said portion.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein at least the major portion of said synthetic, polymeric microfibers contact said forming roll prior to collection on said rotating mandrel.
Claim 4
Dependent Claim
71 words
The method of claim 1 wherein said substantially constant voids volume is obtained by varying one or more of (1) the rate of delivery of said polymeric material to the fiberizing die, (2) the gas flow rate of said one or more gas streams, (3) the force applied to the exterior surface of the collected microfibers by said forming roll and (4) the quantity and type of cooling of said microfibers.
Claim 5
Dependent Claim
33 words
The method of claim 1 wherein at least a portion of said microfibers contact an auxiliary collection member in operative relationship with said forming roll prior to collection on said rotating reciprocating mandrel.
Claim 6
Dependent Claim
43 words
The method of claim 1, wherein said microfibers are thermoplastic and have diameters in the range of from about 1.5 to about 20 micrometers and said fibrous mass has a voids volume in the range of from about 64 to about 93 percent.
Claim 7
Dependent Claim
39 words
The method of claim 1 wherein said fibrous mass has a substantially constant voids volume over substantially its entire structure and a graded fiber diameter structure over at least an upstream portion thereof, both measured in the radial direction.
Claim 8
Independent Claim
256 words
A method of manufacturing a cylindrical fibrous structure comprising a fibrous mass of nonwoven, synthetic, polymeric, thermoplastic microfibers having a voids volume in the range of from about 64 to about 93 percent, said microfibers having diameters in the range of from about 1.5 to about 20 micrometers and being substantially free of fiber-to-fiber bonding and secured to each other by mechanical entanglement or intertwining, comprising the steps of: (a) extruding synthetic, polymeric, thermoplastic resin from a fiberizing die and attenuating said extruded polymeric, thermoplastic resin to form said synthetic, polymeric, thermoplastic microfibers by the application of one or more gas streams directed toward a rotating, reciprocating mandrel and a rotating forming roll in operative relationship with said mandrel; (b) cooling said synthetic, polymeric, thermoplastic microfibers prior to their collection on said mandrel to a temperature below that at which said microfibers bond or fuse to each other, thereby substantially eliminating fiber-to-fiber bonding; and (c) collecting said cooled microfibers on said mandrel as a nonwoven, synthetic fibrous mass while applying a force to the exterior surface of the collected microfibers by said forming roll; wherein at least the major portion of said synthetic, polymeric, thermoplastic microfibers contacts said forming roll prior to collection on said rotating, reciprocating mandrel and the process variables are controlled to form said cylindrical fibrous structure with said fibrous mass having a substantially constant voids volume and varying fiber diameter over at least a substantial portion thereof as measured in the radial direction to achieve a varying pore size over said portion.
Claim 9
Independent Claim
256 words
A method of manufacturing a cylindrical fibrous structure comprising a fibrous mass of nonwoven, synthetic, polymeric, thermoplastic microfibers having a voids volume in the range of from about 64 to about 93 percent, said microfibers having diameters in the range of from about 1.5 to about 20 micrometers and being substantially free of fiber-to-fiber bonding and secured to each other by mechanical entanglement or intertwining, comprising the steps of: (a) extruding synthetic, polymeric, thermoplastic resin from a fiberizing die and attenuating said extruded polymeric, thermoplastic resin to form said synthetic, polymeric, thermoplastic microfibers by the application of one or more gas streams directed toward a rotating, reciprocating mandrel and a rotating forming roll in operative relationship with said mandrel; (b) cooling said synthetic, polymeric, thermoplastic microfibers prior to their collection on said mandrel to a temperature below that at which said microfibers bond or fuse to each other, thereby substantially eliminating fiber-to-fiber bonding; and (c) collecting said cooled microfibers on said mandrel as a nonwoven, synthetic fibrous mass while applying a force to the exterior surface of the collected microfibers by said forming roll; wherein at least the major portion of said synthetic, polymeric, thermoplastic microfibers contacts said forming roll prior to collection on said rotating, reciprocating mandrel and the process variables are controlled to form said cylindrical fibrous structure with said fibrous mass having a substantially constant voids volume and varying fiber diameter over at least a substantial portion thereof as measured in the radial direction to achieve a varying pore size over said portion.
Claim 10
Dependent Claim
71 words
The method of claim 7 wherein said substantially constant voids volume is obtained by varying one or more of (1) the rate of delivery of said thermoplastic resin to the fiberizing die, (2) the gas flow rate of said one or more gas streams, (3) the force applied to the exterior surface of the collected microfibers by said forming roll and (4) the quantity and type of cooling of said microfibers.
Claim 11
Dependent Claim
40 words
The method of claim 7 wherein said fibrous mass has a substantially constant voids volume over substantially its entire structure and a graded fiber diameter structure over at least an upstream portion thereof, both as measured in the radial direction.
Claim 12
Dependent Claim
20 words
The method of claim 7 wherein said thermoplastic resin is selected from the group consisting of polyolefins, polyamides and polyesters.
Claim 13
Dependent Claim
41 words
The method of claim 7 wherein said thermoplastic resin is polypropylene, said voids volume is in the range of from about 75 to about 85 percent and said microfibers have diameters in the range from about 1.9 to about 12.6 micrometers.
Claim 14
Dependent Claim
45 words
The method of claim 11 wherein at least a portion of said microfibers have diameters of about 2.5 micrometers or larger, and said type of cooling of said microfibers includes the application of a water spray to said microfibers prior to collection on said mandrel.
Claim 15
Dependent Claim
33 words
The method of claim 7 wherein at least a portion of said microfibers contact an auxiliary collection member in operative relationship with said forming roll prior to collection on said rotating reciprocating mandrel.
References Cited (Backward Citations)
US2413551A
Cited
US2411660A
Cited
US2539768A
Cited
US2826265A
Cited
US3251475A
Cited
US3248465A
Cited
US2980204A
Cited
US3158532A
Cited
US3210229A
Cited
US3252270A
Cited
US3261473A
Cited
US3268442A
Cited
US3690852A
Cited
US3599797A
Cited
US3801400A
Cited
US3904798A
Cited
US3972759A
Cited
US4211736A
Cited
US3933557A
Cited
US4021281A
Cited
US4112159A
Cited
US3959421A
Cited
US4044404A
Cited
US4116738A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-09 | 1989-12-09 | 1990-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-09 | 1993-12-09 | 1994-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-09 | 1997-12-09 | 1998-06-10 | $7700.00 | Window Closed / Lapsed |