Alkoxy-functional one component RTV silicone rubber compositions

Claim 2

A one-component RTV silicone rubber composition comprising a base diorganopolysiloxane polymer having a viscosity in the range of 100 to 1,000,000 centipoise at 25° C. having one alkoxy group on each terminal silicon atom in the polymer chain and having at least one hydrolyzable leaving group on each terminal silicon atom in the polymer chain wherein the hydrolyzable leaving group is selected from the group consisting of silazy, cyclic amido, amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals and the organo groups are C 1-13 monovalent hydrocarbon radicals; an effective amount of a condensation catalyst; and a stabilizing amount of scavenger for hydroxy functional groups.

Claim 3

The composition of claim 1 wherein the base diorganopolysiloxane polymer has the formula, ##STR20## where R is independently selected from a C 1-13 monovalent hydrocarbon radical, R 1 is independently selected from a C 1-13 monovalent hydrocarbon radical and R 2 is independently selected from a C 1-13 monovalent hydrocarbon radical, b is a whole number that is 0 or 1, l is a whole number that is 1 or 2, and the sum of (b+l) is always 2 and n is a whole number that varies from 50 to 2,500 where X is a hydrolyzable leaving group selected from the group consisting of silazy, cyclic amido, amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals.

Claim 4

The composition of claim 2 wherein the stabilizing amount of scavenger for hydroxy-functional groups has the formula ##STR21## where R 1 is a C 1-8 aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone and alkylcyano radicals, or a C 7-13 aralkyl radical, R 2 is a C 1-13 monovalent substituted or unsubstituted hydrocarbon radical, X is a hydrolyzable leaving group selected from the group consisting of silazy, cyclic amido, amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals and, c is a whole number equal to 0 to 3 inclusive, f is an integer equal to 1 to 4 inclusive and the sum of c+f is equal to 1 to 4 inclusive.

Claim 5

The composition of claim 3 wherein the silane has the formula ##STR22## where R 1 is a C 1-8 aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone and alkylcyano radicals, or a C 7-13 aralkyl radical, R 2 is a C 1-13 monovalent substituted or unsubstituted hydrocarbon radical, X is a hydrolyzable leaving group selected from the group consisting of silazy, cyclic amido, amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals; and, a is an integer equal to 1 to 2 inclusive, b is a whole number equal to 0 to 1 inclusive, and the sum of b+a is equal to 1 to 2 inclusive and the silane is both the silane scavenger for hydroxy-functional groups and a polyalkoxysilane cross-linking agent.

Claim 6

A room temperature vulcanizable composition in with claim 2 having an effective amount of a cross-linking silane of the formula ##STR23## where R 1 is a C 1-8 aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone and alkylcyano radicals, or a C 7-13 aralkyl radical, R 2 is a C 1-13 monovalent substituted or unsubstituted hydrocarbon radical, and b is a whole number equal to 0 or 1.

Claim 7

A room temperature vulcanizable composition in accordance with claim 2, which contains a tin compound as the condensation catalyst.

Claim 8

A room temperature vulcanizable composition in accordance with claim 2, containing an effective amount of curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof.

Claim 9

A room temperature vulcanizable composition in accordance with claim 6 wherein the condensation catalyst is dibutyltindiacetate.

Claim 10

A one-package room temperature vulcanizable composition in accordance with claim 5, where the crosslinking silane is methyltrimethoxysilane.

Claim 11

The composition of claim 2 wherein the stabilizing amount of scavenger for hydroxy-functional groups is selected from the class consisting of a non-cyclic silyl nitrogen scavenger of the formula ##STR24## and cyclic silyl nitrogen scavengers having at least one or all of the units of the formula ##STR25## and the rest of the units, if any, having the formula ##STR26## where R 10 is a C 1-8 aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone, alkylcyano, and aryl, R 11 is a C 1-8 monovalent substituted or unsubstituted hydrocarbon radical, Q is selected from hydrogen, C 1-8 monovalent substituted or unsubstituted hydrocarbon radicals and radicals of the formula ##STR27## where R 10 , R 11 are as previously defined, where a varies from 0 to 2, f varies from 0 to 3, h is 0 or 1, where s is a whole number that varies from 1 to 25, d is a whole number that varies from 1 to 25, R 22 is selected from hydrogen and C 1-8 monovalent hydrocarbon radicals and R 23 is independently selected from C 1-8 hydrocarbon and hydrocarbonoxy radicals, A is selected from the class consisting of hydrogen and C 1-8 monovalent substituted or unsubstituted hydrocarbon radicals and radicals of the formula ##STR28## where R 10 , R 11 are as previously defined, g varies from 0 to 3 and in the above scavengers there is at least one hydrocarbonoxy group in the molecule, R 12 is defined the same as R 10 , and R 13 is defined the same as R 11 , and R 14 is defined the same as R 11 .

Claim 12

The composition of claim 2 wherein the stabilizing amount of silane scavenger for hydroxy functional groups is a silicon-nitrogen compound selected from the class consisting of (A) a silicon-nitrogen compound having the formula ##STR29## where Y is selected from R"' and R" 2 N-- and (B) a silicon-nitrogen polymer comprising (1) from 3 to 100 mole percent chemically combined structural units having the formula ##STR30## (2) from 0 to 97 mole percent chemically combined structural units represented by the formula ##STR31## where the silicon atoms of said silicon-nitrogen polymer are joined to each other by a member selected from an SiOSi linkage and an SiNR"Si linkage, the free valences of said silicon atoms other than those joined to oxygen to form a siloxy unit and nitrogen to form a silazy unit are joined to a member selected from an R"' radical and an (R") 2 N radical, and where the ratio of the sum of said R"' radicals and said (R") 2 N radicals to the silicon atoms of said silicon-nitrogen polymer has a value of 1.5 to 3, inclusive, and R" and R"' are selected from the class consisting of hydrogen, monovalent hydrocarbon radicals and fluoroalkyl radicals, and c is a whole number equal to 0 to 3, inclusive.