Soft ceramic kitchenware internally coated with a non-stick resin
Assignee: T V S SpA TRASANNI URBINO (PESARO)
•
Filing: 1984-04-19
•
Granted: 1986-05-27
•
Expires: 2004-04-19
Abstract
Abstract To assure anchorage of a non-stick resin (18) to the ceramic biscuit (10) of a kitchenware a bonding means is used made up of a lead-free frit (12) having a melting point lying between 500° and 950° C. and including a glaze which melts essentially at these temperatures and that penetrates and bonds inside the pores (15) of the biscuit, and at least one substance that does not melt at the melting temperature of the glaze and which forms surface grains, or ovules (17) enclosed in the melted part (16) and anchored to the base of the biscuit. The non-stick resin emulsion (18) is spread over the rough layer which is successively fired by fusion.
Inventors
- 👤 Umberto Lui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:54
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; A; A47; A47J; A47J36/00; A47J36/02; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24926; Y10T428/25; Y10T428/252; Y10T428/29; Y10T428/2982; Y10T428/31504; Y10T428/3154
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
129 words
Soft ceramic kitchenware consisting of a ceramic material having pores, a coating of a non-stick resin on the food contacting surface and an intermediate bonding layer consisting of a lead-free frit, said frit having a melting point between 500° and 950° C., said frit consisting of: (a) A glaze of melting point essentially between 500° and 950° C., said glaze penetrating and anchoring to the pores of said material, thus eliminating the air present in the pores, (b) a substance which does not melt at the melting temperature of the glaze or which solidifies substantially immediately when the temperature drops below said melting temperature of the glaze, said substance constituting more than 15% and less than 50% of said frit, said substance forming hard grains dispersed in the glaze.
Claim 2
Dependent Claim
129 words
Soft ceramic kitchenware consisting of a ceramic material having pores, a coating of a non-stick resin on the food contacting surface and an intermediate bonding layer consisting of a lead-free frit, said frit having a melting point between 500° and 950° C., said frit consisting of: (a) A glaze of melting point essentially between 500° and 950° C., said glaze penetrating and anchoring to the pores of said material, thus eliminating the air present in the pores, (b) a substance which does not melt at the melting temperature of the glaze or which solidifies substantially immediately when the temperature drops below said melting temperature of the glaze, said substance constituting more than 15% and less than 50% of said frit, said substance forming hard grains dispersed in the glaze.
Claim 3
Dependent Claim
40 words
Kitchenware according to claim 1, wherein the substance which essentially does not melt at the melting temperature of the glaze is a member selected from the group consisting of clay, cryolite, alumina, silica, quartz, kaolin, petalite, zirconia, and mixtures thereof.
Claim 4
Dependent Claim
34 words
Kitchenware, according to claim 1, wherein the substance which essentially does not melt at the melting temperature of the glaze is a mixture of clay and quartz containing approximately 7.5% by weight of silica.
Claim 5
Dependent Claim
33 words
Kitchenware according to claim 1, wherein said glaze consists of zinc oxide, potash, silica and boric acid, and melts at about 950° C. and said substance (b) consists of pulverized quartz and kaolin.
Claim 6
Dependent Claim
26 words
The kitchenware according to claim 1 wherein said glaze melts at 530°-550° C. and consists of silica, alumina, zinc oxide, calcium oxide, potash and boric acid.
Claim 7
Dependent Claim
11 words
Kitchenware according to claim 1 wherein the non-stick resin is polytetrafluoro-ethylene.
Claim 8
Dependent Claim
21 words
Kitchenware according to claim 1 wherein said substance (b) is present in the amount of 15-30% by weight of said frit.
Claim 9
Dependent Claim
37 words
The kitchenware according to claim 2 wherein said substance (b) of the frit forms ovules dispersed in said glaze (a) and said ovules enclose grains of said clay, cryolite, silica, quartz, kaolin, petalite, zirconia and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-26 | 1989-11-25 | 1990-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-26 | 1993-11-25 | 1994-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-26 | 1997-11-25 | 1998-05-27 | $7700.00 | Window Closed / Lapsed |