Molecularly orientating plastics material
Assignee: PLG Research Ltd
•
Filing: 1983-10-03
•
Granted: 1986-05-20
•
Expires: 2003-10-03
Abstract
Abstract An integral plastics material starting sheet has a square or rectangular pattern of holes defining strand-forming zones. The strand-forming zones are formed with depressions with the sheet at a low or ambient temperature. The sheet is then stretched to form the strand-forming into orientated strands.
Inventors
- 👤 Frank B. Mercer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:00
CPC Classifications
B; B29; B29D; B29D28/00; B29C; B29C59/00; B29C59/02; Y; Y10; Y10S; Y10S264/00; Y10S264/81
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
74 words
A method of producing a plastics material mesh structure, comprising: providing a plastics material comprising a pattern of holes or mesh openings defining strand-forming zones therebetween, which plastics material mesh structure has a melting range having a lower limit, and forming depressions in at least some of said strand-forming zones without material removal when said plastics material is at a temperature below said lower limit; and stretching said strand-forming zones to form orientated strands.
Claim 2
Independent Claim
74 words
A method of producing a plastics material mesh structure, comprising: providing a plastics material comprising a pattern of holes or mesh openings defining strand-forming zones therebetween, which plastics material mesh structure has a melting range having a lower limit, and forming depressions in at least some of said strand-forming zones without material removal when said plastics material is at a temperature below said lower limit; and stretching said strand-forming zones to form orientated strands.
Claim 3
Dependent Claim
55 words
The method of claim 1, wherein said plastics material defines a plurality of strand-forming zones in series in the direction of said stretching, said depressions are formed in each said strand-forming zone in series, and said plastics material is stretched by applying a stretching force to a plurality of said strand-forming zones in series simultaneously.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein said temperature is at or close to ambient temperature.
Claim 5
Dependent Claim
38 words
The method of claim 1, wherein said depressions are formed with a tool whose cross-section taken parallel to the direction of said stretching is substantially constant across the width of said tool, said tool presenting opposite, inclined faces.
Claim 6
Dependent Claim
31 words
The method of claim 1, wherein said depressions are wedge-shaped, having an apex which extends substantially at right angles to the direction in which the respective said strand-forming zones are stretched.
Claim 7
Dependent Claim
42 words
The method of claim 1, wherein said strand-forming zones are defined between two respective said holes or mesh openings, said depressions being formed so as to extend for substantially the whole length of said holes or mesh openings but not substantially further.
Claim 8
Dependent Claim
32 words
The method of claim 1, wherein said strand-forming zones are between respective said holes or mesh openings, said depressions extending for substantially less than the length of said holes or mesh openings.
Claim 9
Dependent Claim
44 words
The method of claim 1, wherein said depressions are bounded by steps which extend substantially at right angles to the faces of said plastics material, said steps extending substantially at right angles to the direction in which the respective said strand-forming zones are stretched.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein a plurality of said depressions, spaced apart in the direction of said stretching the respective said strand-forming zone, are formed in a said strand-forming zone.
Claim 11
Dependent Claim
47 words
The method of claim 1, wherein said plastics material is biaxially-stretched in a continuously-operating plant by being stretched in the machine direction and in the transverse direction, said depressions being formed in at least said strand-forming zones which are stretched in the direction of said transverse stretching.
Claim 12
Dependent Claim
36 words
The method of claim 1, wherein said holes are formed in said plastics material by punching, said depressions being formed generally at the same time as the punching in an adjacent part of said plastics material.
Claim 13
Dependent Claim
45 words
The method of claim 1, wherein in any said strand-forming zone, there is a said depression on one face only of said plastics material, the depth of said depression being less than about 40% of the thickness of the undepressed zones of said plastics material.
Claim 14
Dependent Claim
16 words
The method of claim 12, wherein said depth is less than about 25% of said thickness.
Claim 15
Dependent Claim
45 words
The method of claim 1, wherein in any said strand-forming zone, there is a said depression on one face only of said plastics material, the depth of said depression being more than about 10% of the thickness of the undepressed zones of said plastics material.
Claim 16
Dependent Claim
41 words
The method of claim 1, wherein there are registering said depressions on opposite faces of said plastics material, the combined depth of said registering depressions being less than about 40% of the thickness of the undepressed zones of said plastics material.
Claim 17
Dependent Claim
25 words
The method of claim 15, wherein said combined depth is less than about 25% of the thickness of the undepressed zones of said plastics material.
Claim 18
Dependent Claim
41 words
The method of claim 1, wherein there are registering said depressions on opposite faces of said plastics material, the combined depth of said registering depressions being more than about 10% of the thickness of the undepressed zones of said plastics material.
Claim 19
Dependent Claim
27 words
The method of claim 1, wherein there are registering said depressions on opposite faces of said plastics materials, said registering depressions being of substantially the same depth.
Claim 20
Independent Claim
153 words
A method of biaxially stretching plastics material to produce a mesh structure, comprising: providing a plastics material comprising a pattern of holes centered on a notional square or rectangular grid whose sides extend in a first direction and in a second direction at right angles to said first direction, transverse strand-forming zones being defined between holes in rows extending in said first direction and longitudinal strand-forming zones being defined between holes in rows extending in said second direction, said plastics material having a melting point range with a lower limit; forming depressions in at least said transverse strand-forming zones without material removal when said plastics material is at a temperature below said lower limit; stretching said plastics material longitudinally in said first direction to stretch said longitudinal strand-forming zones into orientated longitudinal strands; and stretching said plastics material transversely in said second direction to stretch said transverse strand-forming zones into orientated transverse strands.
Claim 21
Independent Claim
153 words
A method of biaxially stretching plastics material to produce a mesh structure, comprising: providing a plastics material comprising a pattern of holes centered on a notional square or rectangular grid whose sides extend in a first direction and in a second direction at right angles to said first direction, transverse strand-forming zones being defined between holes in rows extending in said first direction and longitudinal strand-forming zones being defined between holes in rows extending in said second direction, said plastics material having a melting point range with a lower limit; forming depressions in at least said transverse strand-forming zones without material removal when said plastics material is at a temperature below said lower limit; stretching said plastics material longitudinally in said first direction to stretch said longitudinal strand-forming zones into orientated longitudinal strands; and stretching said plastics material transversely in said second direction to stretch said transverse strand-forming zones into orientated transverse strands.
Claim 22
Dependent Claim
12 words
The method of claim 3 wherein said temperature is about 15°-20° C.
Claim 23
Dependent Claim
34 words
The method of claim 1, wherein the respective depressions extend right across the strand-forming zones, as considered in the direction at right angles to the direction in which the respective strand-forming zones are stretched.
Claim 24
Dependent Claim
15 words
The method of claim 1, wherein the depressions are formed by a low speed punch.
References Cited (Backward Citations)
DE94251C
Cited
GB900914A
Cited
US3386876A
Cited
US3328505A
Cited
GB1075487A
Cited
US3441638A
Cited
FR1601073A
Cited
US3616154A
Cited
GB1261515A
Cited
US3900550A
Cited
GB1506615A
Cited
GB2073090A
Cited
US4374798A
Cited
US4280978A
Cited
EP0062462A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-19 | 1989-11-18 | 1990-05-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-19 | 1993-11-18 | 1994-05-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-19 | 1997-11-18 | 1998-05-20 | $7700.00 | Window Closed / Lapsed |