Polyamide-imide foams and methods of making same
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1985-09-23
•
Granted: 1986-04-29
•
Expires: 2005-09-23
Abstract
Abstract Methods of producing high molecular weight polyamide-imide foams having superior flame resistance and the foam products produced thereby. Initially, an imidocarboxylic acid is prepared by reacting a suitable oxoimine with a suitable cyclic dianhydride at a temperature of from about 25° to 250° C. in the presence of a solvent or by melt condensation without a solvent. The ratio of oxoimine to dianhydride may be varied to vary the number of imido groups in the final monomer. The imidocarboxylic acid monomer is reacted with an organic isocyanate in the presence of a suitable tertiary diamine catalyst and water to produce the polyamide-imide foam. The material foams spontaneously at room temperature. The reaction may be accelerated by heat or the addition of suitable metal salts. Additives, such as surfactants, flame retardants, fillers, etc., may be added if desired.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:16
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
135 words
The process for preparing a polyamide-imide foam composition which comprises the steps of: providing a cyclic tetracarboxylic acid containing a functional imido group and having the formula ##STR3## reacting said compound with a di-isocyanate to produce a polyamide-imide and having the recurring units: ##STR4## wherein "n" is a positive integer, "R" is a radical selected from the group consisting of alkyline and phenylene radicals, which may have alkyl or aryl substituted and "X" is an integer from 1 to 6. mixing therewith from about 1% to 3% of a tertiary amine based on the diisocyanate, adding thereto and mixing from about 1.0 to 5.0 parts by weight of an organic diisocyanate per part of the imidocarboxylic acid, and adding thereto and mixing from about 2 to 8 weight % water, based on the imidocarboxylic acid.
Claim 2
Dependent Claim
135 words
The process for preparing a polyamide-imide foam composition which comprises the steps of: providing a cyclic tetracarboxylic acid containing a functional imido group and having the formula ##STR3## reacting said compound with a di-isocyanate to produce a polyamide-imide and having the recurring units: ##STR4## wherein "n" is a positive integer, "R" is a radical selected from the group consisting of alkyline and phenylene radicals, which may have alkyl or aryl substituted and "X" is an integer from 1 to 6. mixing therewith from about 1% to 3% of a tertiary amine based on the diisocyanate, adding thereto and mixing from about 1.0 to 5.0 parts by weight of an organic diisocyanate per part of the imidocarboxylic acid, and adding thereto and mixing from about 2 to 8 weight % water, based on the imidocarboxylic acid.
Claim 3
Dependent Claim
50 words
The process according to claim 1 wherein said cyclic tetracarboxylic acid containing a functional imido group is prepared by mixing together at a temperature of from about 25° to 250° C. an aromatic dianhydride and an oximine, the mole ratio of oxoimine to dianhydride being from about 0.1:1 to 10:1.
Claim 4
Dependent Claim
22 words
The process according to claim 2 wherein the ratio of oxoimine to dianhydride is about 1:1 and a monoimidecarboxylic acid is obtained.
Claim 5
Dependent Claim
22 words
The process according to claim 2 wherein the ratio of oxoimine to dianhydride is about 2:1 and a bisimidocarboxylic acid is obtained.
Claim 6
Dependent Claim
41 words
The process according to claim 1 wherein from about 1.0 to 20 wt %, based on the imidocarboxylic acid, of a surfactant is added to the mixture prior to addition of the water, whereby a foam of improved cellular uniformity results.
Claim 7
Dependent Claim
13 words
The process according to claim 5 wherein said surfactant is a silicone surfactant.
Claim 8
Dependent Claim
39 words
The process according to claim 1 wherein from about 1.0 to 5.0 wt %, based on the diisocyanate of a metal salt catalyst is added to the mixture prior to the addition of the water, whereby foaming is accelerated.
Claim 9
Dependent Claim
34 words
The process according to claim 7 wherein said metal salt catalyst is selected from the group consisting of tin oxide, tin acetate, dibutyl tin diacetate, zinc chloride, cobalt acetate, boron fluoride and mixtures thereof.
Claim 10
Dependent Claim
31 words
The process according to claim 1 wherein said mixture is heated to a temperature of from about 50° to 100° C. prior to addition of the water, whereby foaming is accelerated.
Claim 11
Dependent Claim
32 words
The process according to claim 1 wherein said imidocarboxylic acid is selected from the group consisting of benzophenonetetracarboxyimidocaproic acid monoanhydride, benzenetetracarboxyimidocaproic acid monoanhydride, benzophenonetetracarboxy-bisimidocaproic acid, benzenetetracarboxy-bisimidocaproic acid, and mixtures and oligomers thereof.
Claim 12
Dependent Claim
40 words
The process according to claim 1 wherein said organic diisocyanate is selected from the group consisting of 1,6 hexamethylene diisocyanate, 2,4 toluene diisocyanate, 4,4' methylenediisocyanate, methylenediisocyanate, a polymeric isocyanate available from Upjohn under the PAPI 94 designation and mixtures thereof.
Claim 13
Dependent Claim
25 words
The process according to claim 1 wherein said tertiary amine is selected from the group consisting of N-methyl morpholine, triethyamine, diethylcyclohexylamine, dimethylethanolamine and mixtures thereof.
Claim 14
Dependent Claim
26 words
The process according to claim 1 further including the step of adding a fire retardant composition to the mixture prior to the addition of the water.
Claim 15
Dependent Claim
34 words
The process according to claim 13 wherein said fire retardant composition is selected from the group consisting of aluminum hydroxide, zinc borate, tricresylphosphate, triphenyl phosphate, chlorotrialkyl phosphate, fully cured polyimide powder and mixtures thereof.
References Cited (Backward Citations)
US4546115A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-28 | 1989-10-28 | 1990-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-28 | 1993-10-28 | 1994-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-28 | 1997-10-28 | 1998-04-29 | $7700.00 | Window Closed / Lapsed |