Thermally conductive room temperature vulcanizable compositions
Assignee: Wacker Chemical Corp
•
Filing: 1984-10-29
•
Granted: 1986-04-22
•
Expires: 2004-10-29
Abstract
Abstract This invention relates to thermally conductive one-component room temperature vulcanizable organopolysiloxane compositions containing from 30 to 95 percent by weight of filler based on the weight of the composition, of which at least 10 percent by weight of the filler is silicon nitride particles.
Inventors
- 👤 Michelle Pate
- 👤 John C. Getson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:48
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
104 words
A room temperature vulcanizable composition having thermally conductive properties which is stable in the absence of moisture, but when exposed to moisture cures to an elastomer, said composition comprising a hydroxyl-terminated organopolysiloxane, a crosslinking agent having an average of at least two hydrolyzable groups per molecule, in which the hydrolyzable groups are selected from the group consisting of acyloxy, amino, oximo, aminoxy, acylamino and phosphato groups, and from 30 to 95 percent by weight of a filler, based on the weight of the composition of which from 30 to 100 percent by weight based on the weight of the filler is silicon nitride particles.
Claim 2
Dependent Claim
104 words
A room temperature vulcanizable composition having thermally conductive properties which is stable in the absence of moisture, but when exposed to moisture cures to an elastomer, said composition comprising a hydroxyl-terminated organopolysiloxane, a crosslinking agent having an average of at least two hydrolyzable groups per molecule, in which the hydrolyzable groups are selected from the group consisting of acyloxy, amino, oximo, aminoxy, acylamino and phosphato groups, and from 30 to 95 percent by weight of a filler, based on the weight of the composition of which from 30 to 100 percent by weight based on the weight of the filler is silicon nitride particles.
Claim 3
Dependent Claim
30 words
The composition of claim 1, wherein the silicon nitride particles are present in an amount of from 40 to 90 percent by weight based on the weight of the filler.
Claim 4
Dependent Claim
20 words
The composition of claim 1, wherein the silicon nitride particles have a particle size of from 0.5 to 350 microns.
Claim 5
Independent Claim
101 words
A method for preparing a silicone elastomer having thermally conductive properties which comprises mixing under anhydrous conditions a hydroxyl-terminated organopolysiloxane, a crosslinking agent having an average of at least two hydrolyzable groups per molecule, in which the hydrolyzable groups are selected from the group consisting of acyloxy, amino, oximo, aminoxy, acylamino and phosphato groups and from 30 to 95 percent by weight of a filler, based on the weight of the composition of which from 30 to 100 percent by weight based on the weight of the filler is silicon nitride particles, and thereafter exposing the resultant composition to atmospheric moisture.
Claim 6
Independent Claim
101 words
A method for preparing a silicone elastomer having thermally conductive properties which comprises mixing under anhydrous conditions a hydroxyl-terminated organopolysiloxane, a crosslinking agent having an average of at least two hydrolyzable groups per molecule, in which the hydrolyzable groups are selected from the group consisting of acyloxy, amino, oximo, aminoxy, acylamino and phosphato groups and from 30 to 95 percent by weight of a filler, based on the weight of the composition of which from 30 to 100 percent by weight based on the weight of the filler is silicon nitride particles, and thereafter exposing the resultant composition to atmospheric moisture.
References Cited (Backward Citations)
US3070559A
Cited
US3499856A
Cited
US3499859A
Cited
US3642692A
Cited
US3836489A
Cited
US4024933A
Cited
US4123472A
Cited
JPS5571677A
Cited
US4419650A
Cited
US4292225A
Cited
JPS56161461A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-21 | 1989-10-21 | 1990-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-21 | 1993-10-21 | 1994-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-21 | 1997-10-21 | 1998-04-22 | $7700.00 | Window Closed / Lapsed |