Modified aliphatic polyurethane polymers and method of preparing and using same
Assignee: LINAMAR MACHINE Ltd
•
Filing: 1985-04-26
•
Granted: 1986-04-22
•
Expires: 2005-04-26
Abstract
Abstract A process of preparing a fast reacting, light stable, sprayable or injectable polyester-modified polyurethane polymer reaction product to prepare coatings or molded products, which process comprises admixing and reacting together: a trimerized or biuret aliphatic polyisocyanate, such as a trimerized or biuret hexamethylene diisocyanate prepolymer; a polyamine to react as a chain extender for the prepolymer, such as for example, a diethyltoluene diamine, in an amount sufficient to react substantially with the free NCO groups of the trimerized or biuret prepolymer; an unsaturated polyester subject to cross linking by the use of a metal salt promotor, such as a cobalt salt promotor, and a peroxide initiator; the cobalt salt and the peroxide initiator present in an amount to provide for the curing of the unsaturated polyester.
Inventors
- 👤 Stuart B. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:15
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/77; C08G18/78; C08G18/79; C08G18/791; C08G18/792; C08G18/08; C08G18/16; C08G18/18; C08G18/20; C08G18/2045; C08G18/2063; C08G18/28; C08G18/65; C08G18/6505; C08G18/6523; C08G18/6529; C08G18/67; C08G18/68; C08G18/7806; C08G18/7818; C08G18/7831; C08G2120/00; C08G2150/00; C08G2150/50
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
195 words
A process for preparing a light stable, fast reacting, polyester-modified aliphatic polyurethane polymeric reaction product, which process comprises admixing and reacting a composition, which composition comprises: (a) 100 parts by weight of a trimerized or biuret polymethylene polyisocyanate prepolymer having free NCO groups; (b) 10 to 150 parts by weight of an unsaturated polyester prepared by the reaction of an unsaturated polycarboxylic acid with a polyhydroxyl compound, and which polyester contains from about 0 to 40 percent by weight of a compatible unsaturated monomer adapted for a cross linking reaction with the unsaturated polyester; (c) a metal salt promotor for the unsaturated polyester to promote the cross linking of the unsaturated polyester, the metal salt promotor present in an amount sufficient to promote a cross linking reaction; (d) a peroxide initiator for the unsaturated polyester in an amount sufficient to initiate the cross linking reaction of the unsaturated polyester; and (e) an aromatic or cycloaliphatic polyamine in a stoichiometric amount ranging from the amount to react with all or substantially all of the free NCO groups of the prepolymer and in a maximum amount to also react with the hydroxyl groups of the unsaturated polyester.
Claim 2
Dependent Claim
195 words
A process for preparing a light stable, fast reacting, polyester-modified aliphatic polyurethane polymeric reaction product, which process comprises admixing and reacting a composition, which composition comprises: (a) 100 parts by weight of a trimerized or biuret polymethylene polyisocyanate prepolymer having free NCO groups; (b) 10 to 150 parts by weight of an unsaturated polyester prepared by the reaction of an unsaturated polycarboxylic acid with a polyhydroxyl compound, and which polyester contains from about 0 to 40 percent by weight of a compatible unsaturated monomer adapted for a cross linking reaction with the unsaturated polyester; (c) a metal salt promotor for the unsaturated polyester to promote the cross linking of the unsaturated polyester, the metal salt promotor present in an amount sufficient to promote a cross linking reaction; (d) a peroxide initiator for the unsaturated polyester in an amount sufficient to initiate the cross linking reaction of the unsaturated polyester; and (e) an aromatic or cycloaliphatic polyamine in a stoichiometric amount ranging from the amount to react with all or substantially all of the free NCO groups of the prepolymer and in a maximum amount to also react with the hydroxyl groups of the unsaturated polyester.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the polymethylene polyisocyanate prepolymer comprises a trimerized or biuret hexamethylene diisocyanate prepolymer.
Claim 4
Dependent Claim
21 words
The process of claim 1 wherein the prepolymer comprises from about 20 to 25 percent by weight of free NCO groups.
Claim 5
Dependent Claim
14 words
The process of claim 1 wherein the polyamine comprises a dialkyl substituted aromatic diamine.
Claim 6
Dependent Claim
11 words
The process of claim 1 wherein the polyamine comprises diethyltoluene diamine.
Claim 7
Dependent Claim
20 words
The process of claim 1 wherein the polyamine comprises from about 10 to 50 parts by weight of the prepolymer.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein the metal salt promotor comprises from about 0.05 to 3 parts by weight of the unsaturated polyester.
Claim 9
Dependent Claim
14 words
The process of claim 1 wherein the metal salt promotor comprises an organo-cobalt promotor.
Claim 10
Dependent Claim
22 words
The process of claim 1 wherein the peroxide initiator comprises from about 0.5 to 10 parts by weight of the unsaturated polyester.
Claim 11
Dependent Claim
18 words
The process of claim 9 wherein the peroxide initiator comprises methyl ethyl ketone peroxide or an alkyl perbenzoate.
Claim 12
Dependent Claim
25 words
The process of claim 1 wherein the unsaturated polyester contains from about 0 to 40 percent by weight of a styrene or a diallyl phthalate.
Claim 13
Dependent Claim
40 words
The process of claim 1 wherein the unsaturated polyester is prepared by the reaction of a dicarboxylic ethylenically unsaturated acid with a di or tri polyol, and wherein the hydroxyl number of the polyester ranges from about 35 to 300.
Claim 14
Dependent Claim
47 words
The process of claim 1 wherein the unsaturated polyester is prepared by the reaction of a maleic or fumaric acid with propylene glycol or neopentyl glycol, and wherein the compatible unsaturated monomer comprises acrylic acid, methyl acrylic acid, an alkyl acrylate or alkyl methacrylate or combinations thereof.
Claim 15
Dependent Claim
18 words
The process of claim 1 wherein the composition includes a flame retardant amount of a flame retardant compound.
Claim 16
Dependent Claim
25 words
The process of claim 1 which includes a blowing amount of a blowing agent and a surfactant to provide for a polymeric foam reaction product.
Claim 17
Dependent Claim
56 words
The process of claim 1 which includes admixing and reacting the composition by spraying an A side composition and a B side composition onto a substrate surface wherein the A side composition comprises the trimerized prepolymer and the peroxide initiator and the B side composition comprises the unsaturated polyester, the metal salt promotor and the polyamine.
Claim 18
Dependent Claim
27 words
The process of claim 16 which includes spraying the A and B side mixture onto a substrate which contains a fiber strengthening amount of a fibrous material.
Claim 19
Dependent Claim
14 words
The process of claim 17 wherein the fibrous material comprises a glass fiber mat.
Claim 20
Dependent Claim
22 words
The process of claim 16 which includes injecting chopped fiberglass into the sprayed reaction mixture of the A and B side composition.
Claim 21
Dependent Claim
28 words
The process of claim 16 which includes reacting the A side and B side composition together by injecting the compositions onto the substrate surface of an open mold.
Claim 22
Dependent Claim
10 words
The reaction product produced by the process of claim 1.
Claim 23
Dependent Claim
10 words
The reaction product produced by the process of claim 18.
Claim 24
Dependent Claim
165 words
A process for preparing a light stable, fast reacting, polyester modified polyurethane reaction polymer reaction product, which process comprises admixing and adding together: (a) an A side composition which comprises 100 parts by weight of a trimerized or biuret hexamethylene diisocyanate prepolymer having from about 20 to 25 percent by weignt of free NCO groups and about 0.5 to 10 parts by weight of a organo peroxide initiator; and (b) a B side composition which comprises an ethylenically unsaturated polyester prepared by the reaction of an unsaturated dicarboxylic acid with a polyhydroxyl organic compound and which contains from about 0 to 40 percent by weight of a compatible ethylenically unsaturated monomer for a cross linking reaction with the unsaturated polyester, the polyester having a hydroxyl number of from about 100 to 200, and an organo-cobalt promotor in an amount of about 0.05 to 2 parts by weight of the polyester and from about 5 to 100 parts by weight of a dialkyl substituted aromatic diamine.
Claim 25
Dependent Claim
165 words
A process for preparing a light stable, fast reacting, polyester modified polyurethane reaction polymer reaction product, which process comprises admixing and adding together: (a) an A side composition which comprises 100 parts by weight of a trimerized or biuret hexamethylene diisocyanate prepolymer having from about 20 to 25 percent by weignt of free NCO groups and about 0.5 to 10 parts by weight of a organo peroxide initiator; and (b) a B side composition which comprises an ethylenically unsaturated polyester prepared by the reaction of an unsaturated dicarboxylic acid with a polyhydroxyl organic compound and which contains from about 0 to 40 percent by weight of a compatible ethylenically unsaturated monomer for a cross linking reaction with the unsaturated polyester, the polyester having a hydroxyl number of from about 100 to 200, and an organo-cobalt promotor in an amount of about 0.05 to 2 parts by weight of the polyester and from about 5 to 100 parts by weight of a dialkyl substituted aromatic diamine.
Claim 26
Dependent Claim
12 words
The process of claim 23 wherein the aromatic diamine comprises diethyltoluene diamine.
Claim 27
Dependent Claim
18 words
The process of claim 23 wherein the aromatic diamine comprises from about 10 to 50 parts by weight.
Claim 28
Dependent Claim
32 words
The process of claim 23 wherein the unsaturated polyester is prepared by the reaction of an acrylate, a propylene oxide and a maleate, and which is substantially free of a styrene monomer.
Claim 29
Dependent Claim
42 words
The process of claim 23 which includes spraying the compositions A and B together onto an open mold substrate which contains a mat of fiberglass to prepare a fiberglass containing molded product, and removing the reactive polymeric product from the open mold.
Claim 30
Dependent Claim
10 words
The reaction product prepared by the process of claim 23.
Claim 31
Dependent Claim
10 words
The reaction product prepared by the process of claim 27.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-21 | 1989-10-21 | 1990-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-21 | 1993-10-21 | 1994-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-21 | 1997-10-21 | 1998-04-22 | $7700.00 | Window Closed / Lapsed |