High performance cermet electrodes
Assignee: Westinghouse Electric Corp
•
Filing: 1985-03-28
•
Granted: 1986-04-15
•
Expires: 2005-03-28
Abstract
Abstract Disclosed is a method of increasing the operating cell voltage of a solid oxide electrochemical cell having metal electrode particles in contact with an oxygen-transporting ceramic electrolyte. The metal electrode is heated with the cell, and oxygen is passed through the oxygen-transporting ceramic electrolyte to the surface of the metal electrode particles so that the metal electrode particles are oxidized to form a metal oxide layer between the metal electrode particles and the electrolyte. The metal oxide layer is then reduced to form porous metal between the metal electrode particles and the ceramic electrolyte.
Inventors
- 👤 Arnold O. Isenberg
- 👤 Gregory E. Zymboly
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:48
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; C; C25; C25B; C25B11/00; C25B11/02; C25B11/03; C25B11/031; C25B11/04; C25B11/051; C25B11/055; C25B11/057; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
87 words
A method of increasing the cell voltage of an electrochemical cell having a porous metal electrode in contact with a oxygen-transporting vapor deposited ceramic electrolyte comprising (A) heating said metal electrode particles to at least their oxidation temperature; (B) passing oxygen through said oxygen-transporting ceramic electrolyte to the surface of said metal electrode particles, whereby a portion of said metal electrode particles are oxidized, forming a metal oxide layer between said metal electrode particles and said electrolyte; and (C) reducing said metal oxide layer to said metal.
Claim 2
Independent Claim
87 words
A method of increasing the cell voltage of an electrochemical cell having a porous metal electrode in contact with a oxygen-transporting vapor deposited ceramic electrolyte comprising (A) heating said metal electrode particles to at least their oxidation temperature; (B) passing oxygen through said oxygen-transporting ceramic electrolyte to the surface of said metal electrode particles, whereby a portion of said metal electrode particles are oxidized, forming a metal oxide layer between said metal electrode particles and said electrolyte; and (C) reducing said metal oxide layer to said metal.
Claim 3
Dependent Claim
25 words
A method according to claim 1 wherein said electrochemical cell is a fuel cell and said oxidation temperature is about 600° to about 1200° C.
Claim 4
Dependent Claim
20 words
A method according to claim 1 wherein about 1 to about 100 atom % of said metal electrode is oxidized.
Claim 5
Dependent Claim
33 words
A method according to claim 1 wherein said metal oxide layer is reduced by exposing it to a gaseous fuel at a temperature at which said metal oxide layer is reduced to metal.
Claim 6
Dependent Claim
23 words
A method according to claim 4 wherein said fuel is selected from the group consisting of hydrogen, carbon monoxide, methane, and mixtures thereof.
Claim 7
Dependent Claim
28 words
A method according to claim 4 wherein said oxide layer is reduced until the potential across said cell increases to about the potential of said fuel versus air.
Claim 8
Dependent Claim
24 words
A method according to claim 1 wherein said metal oxide layer is reduced electrochemically by applying a reversed polarity from a DC power supply.
Claim 9
Dependent Claim
28 words
A method according to claim 1 wherein said metal electrode particles are selected from the group consisting of nickel, cobalt, iron, copper, chromium, and mixtures and alloys thereof.
Claim 10
Dependent Claim
26 words
A method according to claim 8 wherein said metal electrode particles are selected from the group consisting of nickel and cobalt, and mixtures and alloys thereof.
Claim 11
Dependent Claim
33 words
A method according to claim 1 wherein said metal electrode particles are bonded to said electrolyte by means of a vapor deposited ceramic oxygen-conducting coating, which acts as a portion of said electrolyte.
Claim 12
Dependent Claim
19 words
A method according to claim 10 wherein said ceramic coating is about 0.5 to about 20 μm microns thick.
Claim 13
Dependent Claim
32 words
A method according to claim 1 wherein said metal electrode particles are about 1 to about 50 microns in size, and said metal electrode is about 10 to about 500 microns thick.
Claim 14
Dependent Claim
134 words
In an electrochemical cell having a powdered metal electrode bonded to an oxygen ion conducting ceramic electrolyte by means of an oxygen ion conducting ceramic coating which forms part of said electrolyte, an improved method of increasing the voltage of said cell comprising (A) heating said cell to a temperature at which said metal electrode oxidizes; (B) diffusing oxygen ions through said electrolyte to said metal electrode that is in contact therewith, until about 1 to about 100 atom % of said metal electrode in contact with said electrolyte is oxidized, to form a metal oxide layer between said metal electrode and said electrolyte; and (C) exposing said metal oxide layer to gaseous fuel while heating said fuel cell to a temperature at which said fuel reduces said metal oxide completely to said metal.
Claim 15
Dependent Claim
134 words
In an electrochemical cell having a powdered metal electrode bonded to an oxygen ion conducting ceramic electrolyte by means of an oxygen ion conducting ceramic coating which forms part of said electrolyte, an improved method of increasing the voltage of said cell comprising (A) heating said cell to a temperature at which said metal electrode oxidizes; (B) diffusing oxygen ions through said electrolyte to said metal electrode that is in contact therewith, until about 1 to about 100 atom % of said metal electrode in contact with said electrolyte is oxidized, to form a metal oxide layer between said metal electrode and said electrolyte; and (C) exposing said metal oxide layer to gaseous fuel while heating said fuel cell to a temperature at which said fuel reduces said metal oxide completely to said metal.
Claim 16
Dependent Claim
60 words
An electrochemical cell comprising a powdered metal electrode bonded to an oxygen ion conducting electrolyte by means of an oxygen ion conducting ceramic coating which forms part of said electrolyte, where said cell has been treated according to the method of claim 13 to produce a porous metal layer between said powdered metal electrode and said oxygen ion conducting electrolyte.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-14 | 1989-10-14 | 1990-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-14 | 1993-10-14 | 1994-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-14 | 1997-10-14 | 1998-04-15 | $7700.00 | Window Closed / Lapsed |