US4581406A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fluoroelastomer containing polyethylene composition and process for extruding same
Assignee: EIDP Inc
•
Filing: 1985-06-11
•
Granted: 1986-04-08
•
Expires: 2005-06-11
Abstract
Abstract A composition comprising 2-3 wt. % carbon black, 25-1000 ppm and preferably 75-250 ppm of a fluoroelastomer and the remainder polyethylene is disclosed. The fluoroelastomer prevents die buildup during extrusion of the composition which is believed to be caused by moisture associated with the carbon black. Alternatively, the die may be conditioned by extruding polyethylene containing 0.5-5 wt. % of the fluoroelastomer and then carbon black containing polyethylene without the fluoroelastomer can be extruded for a substantial period before die buildup begins to occur.
Inventors
- 👤 Johan G. Hedberg
- 👤 Lawrence C. Muschiatti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:52
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815; B; B29; B29C; B29C48/00; B29C48/022; C08K; C08K3/00; C08K3/02; C08K3/04; C08L23/06; C08L27/00; C08L27/02; C08L27/12; C08L27/20; B29C48/03; C08L2205/00; C08L2205/02; C08L2205/03; C08L2205/035; C08L2310/00; C08L27/16
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
74 words
A melt extrudable composition consisting essentially of a polyethylene resin containing from 1 to 5 weight percent carbon black and from 235 to 1000 parts per million, based on the total composition, of a fluoroelastomer containing from 30 to 70 parts by weight repeating units derived from vinylidene fluoride, from 25 to 70 parts by weight repeating units derived from hexafluoropropylene and from 0 to 35 parts by weight repeating units derived from tetrafluoroethylene.
Claim 2
Dependent Claim
74 words
A melt extrudable composition consisting essentially of a polyethylene resin containing from 1 to 5 weight percent carbon black and from 235 to 1000 parts per million, based on the total composition, of a fluoroelastomer containing from 30 to 70 parts by weight repeating units derived from vinylidene fluoride, from 25 to 70 parts by weight repeating units derived from hexafluoropropylene and from 0 to 35 parts by weight repeating units derived from tetrafluoroethylene.
Claim 3
Dependent Claim
20 words
The melt extrudable composition of claim 1 wherein from 75 to 250 parts per million of the fluoroelastomer is present.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-07 | 1989-10-07 | 1990-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-07 | 1993-10-07 | 1994-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-07 | 1997-10-07 | 1998-04-08 | $7700.00 | Window Closed / Lapsed |