US4581098A
Expired / Lapsed
US
⏱️ 0.0 years remaining
MLC green sheet process
Assignee: International Business Machines Corp
•
Filing: 1984-10-19
•
Granted: 1986-04-08
•
Expires: 2004-10-19
Abstract
Abstract Disclosed is a method of forming a trench pattern in a ceramic green sheet for subsequently filling with a conductive paste resulting in a fully inlaid conductor pattern therefrom. Starting with a green sheet, a high contrast ink drawing of the desired conductor pattern is formed thereon. The drawing may be formed by direct printing on the green sheet or by first printing it on a flexible substrate such as paper and then transferring by xerography to the green sheet. Next, the green sheet is illuminated with an intense noncoherent light source to cause a high degree of absorption of the light energy by the inked areas and volatilization of the green sheet binder material thereunder, thereby forming a trench pattern conforming to the drawn pattern.
Inventors
- 👤 Lawrence V. Gregor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:50
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/0026; H05K3/0029; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K1/09; H05K1/092; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0112; H05K2201/09; H05K2201/09009; H05K2201/09036; H05K3/0032; H05K3/10; H05K3/107; H05K3/12; H05K3/1241; H05K3/1258; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
98 words
A method making a trench pattern in a ceramic green sheet, said method comprising: (a) forming on a surface of said sheet an ink pattern of a high optical contrast in relation to said sheet; and (b) illuminating said sheet with radiation having a wavelength which corresponds to the absorption spectrum of said ink to cause a relatively high absorption of said wavelength by said ink pattern as compared to the remainder of said sheet, thereby heating and volatilizing the areas of said sheet corresponding to said ink pattern and converting said ink pattern into a trench pattern.
Claim 2
Independent Claim
98 words
A method making a trench pattern in a ceramic green sheet, said method comprising: (a) forming on a surface of said sheet an ink pattern of a high optical contrast in relation to said sheet; and (b) illuminating said sheet with radiation having a wavelength which corresponds to the absorption spectrum of said ink to cause a relatively high absorption of said wavelength by said ink pattern as compared to the remainder of said sheet, thereby heating and volatilizing the areas of said sheet corresponding to said ink pattern and converting said ink pattern into a trench pattern.
Claim 3
Dependent Claim
24 words
The method as recited in claim 1 wherein said illuminating step comprises shining a single flash of high intensity radiation for a predetermined duration.
Claim 4
Dependent Claim
25 words
The method as recited in claim 1 wherein said illuminating step comprises repetitiously shining a flash of relatively low intensity radiation for a short duration.
Claim 5
Dependent Claim
13 words
The method as recited in claim 1 wherein said ink is carbon-based ink.
Claim 6
Dependent Claim
13 words
The method as recited in claim 1 wherein said radiation is visible light.
Claim 7
Dependent Claim
13 words
The method as recited in claim 1 wherein said radiation is ultraviolet radiation.
Claim 8
Dependent Claim
18 words
The method as recited in claim 1 wherein said radiation is a mixture of visible and ultraviolet radiation.
Claim 9
Dependent Claim
14 words
The method as recited in claim 1 wherein said step (a) comprises direct printing.
Claim 10
Dependent Claim
35 words
The method as recited in claim 1 wherein said step (a) comprises: forming a high contrast pattern on a flexible substrate; and transferring said pattern on the flexible substrate to said volatilizable substrate by xerography.
Claim 11
Independent Claim
119 words
A method of forming a channel pattern in a ceramic green sheet, said method comprising: (a) forming on a flexible substrate surface a pattern having a high optical contrast with said surface; (b) transferring said pattern to at least a surface portion of said green sheet by xerography obtaining a high optical contrast dark and light image of said substrate pattern; and (c) illuminating the image on said green sheet with an intense radiation having a wavelength which corresponds to the absorption spectrum of the dark portion of said image enabling the dark portion of said image to readily absorb said radiation and volatilize the ceramic sheet corresponding to said dark portion, thereby forming a well-defined channel pattern therein.
Claim 12
Independent Claim
119 words
A method of forming a channel pattern in a ceramic green sheet, said method comprising: (a) forming on a flexible substrate surface a pattern having a high optical contrast with said surface; (b) transferring said pattern to at least a surface portion of said green sheet by xerography obtaining a high optical contrast dark and light image of said substrate pattern; and (c) illuminating the image on said green sheet with an intense radiation having a wavelength which corresponds to the absorption spectrum of the dark portion of said image enabling the dark portion of said image to readily absorb said radiation and volatilize the ceramic sheet corresponding to said dark portion, thereby forming a well-defined channel pattern therein.
Claim 13
Dependent Claim
13 words
The method as recited in claim 9 wherein said radiation is visible light.
Claim 14
Dependent Claim
12 words
The method as recited in claim 9 wherein said radiation is ultraviolet.
Claim 15
Dependent Claim
18 words
The method as recited in claim 10 wherein said radiation is a combination of visible and ultraviolet light.
Claim 16
Independent Claim
143 words
A method of forming a fully inlaid pattern of conductive paste on a sinterable ceramic sheet suitable for fabricating a multilayer ceramic package, said method comprising: (a) forming on a flexible substrate a black and white drawing of said pattern, the black areas of said drawing corresponding to the conductive portions of said pattern; (b) transferring said drawing to said ceramic sheet by xerography to form a dark and light image thereon, the dark and light areas of said image corresponding, respectively, to the black and white areas of said drawing; (c) illuminating the image on the ceramic sheet with an intense radiation having a wavelength which matches the absorption spectrum of said dark areas and volatilizing the ceramic sheet in the dark areas thereof forming trenches in said sheet corresponding to said pattern; and (d) filling said trenches with a conductive paste.
Claim 17
Independent Claim
143 words
A method of forming a fully inlaid pattern of conductive paste on a sinterable ceramic sheet suitable for fabricating a multilayer ceramic package, said method comprising: (a) forming on a flexible substrate a black and white drawing of said pattern, the black areas of said drawing corresponding to the conductive portions of said pattern; (b) transferring said drawing to said ceramic sheet by xerography to form a dark and light image thereon, the dark and light areas of said image corresponding, respectively, to the black and white areas of said drawing; (c) illuminating the image on the ceramic sheet with an intense radiation having a wavelength which matches the absorption spectrum of said dark areas and volatilizing the ceramic sheet in the dark areas thereof forming trenches in said sheet corresponding to said pattern; and (d) filling said trenches with a conductive paste.
Claim 18
Dependent Claim
12 words
The method as in claim 14 wherein said flexible substrate is paper.
Claim 19
Dependent Claim
12 words
The method as in claim 14 wherein said radiation is visible light.
Claim 20
Dependent Claim
14 words
The method as in claim 14 wherein said radiation is visible and ultraviolet light.
Claim 21
Dependent Claim
14 words
The method as in claim 14 wherein said illuminating step comprises shining pulsed radiation.
Claim 22
Independent Claim
97 words
A method of making a trench pattern in a polyimide-based substrate, said method comprising: (a) forming on a surface portion of said substrate an ink pattern having a high optical contrast with said substrate; and (b) illuminating said substrate with radiation having a wavelength which corresponds to the absorption spectrum of said ink to cause a relatively high absorption of said radiation by said ink pattern as compared to the remainder of the substrate, thereby heating and volatilizing the areas of the substrate corresponding to said ink pattern and converting said ink pattern into a trench pattern.
Claim 23
Independent Claim
97 words
A method of making a trench pattern in a polyimide-based substrate, said method comprising: (a) forming on a surface portion of said substrate an ink pattern having a high optical contrast with said substrate; and (b) illuminating said substrate with radiation having a wavelength which corresponds to the absorption spectrum of said ink to cause a relatively high absorption of said radiation by said ink pattern as compared to the remainder of the substrate, thereby heating and volatilizing the areas of the substrate corresponding to said ink pattern and converting said ink pattern into a trench pattern.
Claim 24
Dependent Claim
13 words
The method as recited in claim 19 wherein said ink is carbon-based ink.
References Cited (Backward Citations)
US1996549A
Cited
US3481760A
Cited
US3260584A
Cited
US3770529A
Cited
US3948706A
Cited
US3956052A
Cited
US4109377A
Cited
US4356135A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-04-07 | 1989-10-07 | 1990-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-04-07 | 1993-10-07 | 1994-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-04-07 | 1997-10-07 | 1998-04-08 | $7700.00 | Window Closed / Lapsed |