Tobacco filters and method for producing same
Assignee: Shell USA Inc
•
Filing: 1983-12-22
•
Granted: 1986-04-01
•
Expires: 2003-12-22
Abstract
Abstract A process is provided for producing cigarette filters which exhibit desired adhesion properties between the filter fibers, and which may be subjected to a substantially broader operating range during a temperature melt fusion step. A crystalline propylene polymer and a second crystalline polymer are mixed together, and the blend is extruded into fibers which are then heated to a temperature above the original melting point of the second crystalline polymer and below the original melting point of the crystalline propylene polymer. The fibers are twisted and/or crimped to effectuate desired adhesion between the fibers and are subsequently formed into filter rods which display greatly increased cohesiveness.
Inventors
- 👤 Paul M. Coffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:51
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/44; D01F6/46; A; A24; A24D; A24D3/00; A24D3/06; A24D3/08
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
145 words
A method of manufacturing tobacco filters which comprises: mixing a substantial amount of a crystalline propylene polymer and a second crystalline polymer, where the melting point of said second crystalline polymer is less than the melting point of said crystalline propylene polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said fibers in said rods exhibit increased cohesiveness.
Claim 2
Independent Claim
145 words
A method of manufacturing tobacco filters which comprises: mixing a substantial amount of a crystalline propylene polymer and a second crystalline polymer, where the melting point of said second crystalline polymer is less than the melting point of said crystalline propylene polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said fibers in said rods exhibit increased cohesiveness.
Claim 3
Dependent Claim
43 words
The method of claim 1, wherein the amount of said crystalline propylene polymer is from about 25% by weight to about 95% by weight and the amount of said second crystalline polymer is from about 5% by weight to about 75% by weight.
Claim 4
Dependent Claim
43 words
The method of claim 1, wherein the amount of said crystalline propylene polymer is from about 50% by weight to about 85% by weight and the amount of said second crystalline polymer is from about 10% by weight to about 50% by weight.
Claim 5
Dependent Claim
43 words
The method of claim 1, wherein the amount of said crystalline propylene polymer is from about 70% by weight to about 80% by weight and the amount of said second crystalline polymer is from about 20% by weight to about 30% by weight.
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein said second crystalline polymer is selected from the group consisting of butene-1 polymer, ethylene polymer, or copolymers thereof.
Claim 7
Dependent Claim
16 words
The method of claim 1, wherein said fibers of said tow are both twisted and crimped.
Claim 8
Dependent Claim
18 words
A tobacco filter having cohesive fibers in said filter made in accordance with the process of claim 1.
Claim 9
Independent Claim
141 words
A method of manufacturing tobacco filters which comprises: mixing from about 25% by weight to about 95% by weight of a crystalline propylene polymer and from about 5% by weight to about 75% by weight of a crystalline butene-1 polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above the melting point of said second crystalline polymer and below the melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline butene-1 polymer to effectuate desired adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said filters exhibit increased cohesiveness.
Claim 10
Independent Claim
141 words
A method of manufacturing tobacco filters which comprises: mixing from about 25% by weight to about 95% by weight of a crystalline propylene polymer and from about 5% by weight to about 75% by weight of a crystalline butene-1 polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above the melting point of said second crystalline polymer and below the melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline butene-1 polymer to effectuate desired adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said filters exhibit increased cohesiveness.
Claim 11
Dependent Claim
43 words
The method of claim 1, wherein the amount of said crystalline propylene polymer is from about 50% by weight to about 85% by weight and the amount of said second crystalline polymer is from about 10% by weight to about 50% by weight.
Claim 12
Dependent Claim
43 words
The method of claim 1, wherein the amount of said crystalline propylene polymer is from about 70% by weight to about 80% by weight and the amount of said second crystalline polymer is from about 20% by weight to about 30% by weight.
Claim 13
Dependent Claim
16 words
The method of claim 8, wherein said fibers of said tow are both twisted and crimped.
Claim 14
Dependent Claim
18 words
A tobacco filter having cohesive fibers in said filter made in accordance with the process of claim 8.
Claim 15
Independent Claim
141 words
A method of manufacturing tobacco filters which comprises: mixing from about 70% by weight to about 80% by weight of a crystalline propylene polymer and from about 20% by weight to about 30% by weight of a crystalline butene-1 polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above the melting point of said second crystalline polymer and below the melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting and crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline polypropylene polymer to effectuate desired adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said filters exhibit increased cohesiveness.
Claim 16
Independent Claim
141 words
A method of manufacturing tobacco filters which comprises: mixing from about 70% by weight to about 80% by weight of a crystalline propylene polymer and from about 20% by weight to about 30% by weight of a crystalline butene-1 polymer; extruding said mixture into fibers; forming a tow from a multiplicity of said fibers; heating said fibers of said tow to a temperature above the melting point of said second crystalline polymer and below the melting point of said crystalline propylene polymer to effectuate some inter-fiber adhesion; twisting and crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline polypropylene polymer to effectuate desired adhesion between said fibers of said tow; and forming said tow into filter rods, whereby said filters exhibit increased cohesiveness.
Claim 17
Dependent Claim
18 words
A tobacco filter having cohesive fibers in said filter made in accordance with the process of claim 13.
Claim 18
Dependent Claim
94 words
A tobacco filter which comprises a cohesive tow of extruded fibers of a mixture of a crystalline propylene polymer and a second crystalline polymer manufactured by heating said fibers of said tow to a temperature above the melting point of said crystalline polymer and below the melting point of said crystalline propylene polymer and twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate adhesion between said fibers of said tow.
Claim 19
Dependent Claim
94 words
A tobacco filter which comprises a cohesive tow of extruded fibers of a mixture of a crystalline propylene polymer and a second crystalline polymer manufactured by heating said fibers of said tow to a temperature above the melting point of said crystalline polymer and below the melting point of said crystalline propylene polymer and twisting or crimping said fibers of said tow while said temperature remains above said melting point of said second crystalline polymer and below said melting point of said crystalline propylene polymer to effectuate adhesion between said fibers of said tow.
Claim 20
Dependent Claim
44 words
The tobacco filter of claim 15, wherein the amount of said crystalline propylene polymer is from about 25% by weight to about 95% by weight and the amount of said second crystalline polymer is from about 5% by weight to about 75% by weight.
Claim 21
Dependent Claim
44 words
The tobacco filter of claim 15, wherein the amount of said crystalline propylene polymer is from about 50% by weight to about 85% by weight and the amount of said second crystalline polymer is from about 10% by weight to about 50% by weight.
Claim 22
Dependent Claim
44 words
The tobacco filter of claim 15, wherein the amount of said crystalline propylene polymer is from about 70% by weight to about 80% by weight and the amount of said second crystalline polymer is from about 20% by weight to about 30% by weight.
Claim 23
Dependent Claim
25 words
The tobacco filter of claim 18, wherein said second crystalline polymer is selected from the group consisting of butene-1 polymer, ethylene polymer or copolymers thereof.
References Cited (Backward Citations)
CA693929A
Cited
US3039908A
Cited
US3038478A
Cited
US3595245A
Cited
US3960770A
Cited
US4261373A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-31 | 1989-09-30 | 1990-04-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-31 | 1993-09-30 | 1994-04-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-31 | 1997-09-30 | 1998-04-01 | $7700.00 | Window Closed / Lapsed |