High expansion dental crown core ceramic composition
Assignee: INNOVISTICS Inc
•
Filing: 1985-01-09
•
Granted: 1986-03-18
•
Expires: 2005-01-09
Abstract
Abstract A strong white ceramic composition and method of making the same wherein said composition is characterized by an average coefficient of thermal expansion over the range of 25 DEG C. to 500 DEG C. ("Proposed American National Standards Institute/American Dental Association Specification No. 38.1 For Porcelain-Alloy Systems") of between 14 to 16x10-6/ DEG C. and a transverse strength of about 18,000 psi or even greater. The ceramic composition comprises about 40 to 60% by weight crystalline magnesium oxide particles (e.g., 74 mu m ) dispersed in a modified silicate glass containing at least 3% by weight of dissolved ZrO2, TiO2 or mixtures thereof and is made by firing a powdered mixture of MgO2 and modified silicate glass at about 1150 DEG C. for sufficient time to produce a fine dispersion of forsterite (Mg2SiO4) in the continuous glass matrix phase along with the crystalline magnesia particles. Such ceramic compositions are useful in high expansion dental crown core applications.
Inventors
- 👤 William J. O'Brien
- 👤 Matthew T. O'Brien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 03:53
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; A; A61; A61K; A61K6/00; A61K6/15; A61K6/17; A61K6/70; A61K6/71; A61K6/77; A61K6/80; A61K6/802; A61K6/807; A61K6/816; A61K6/818; C04; C04B; C04B35/00; C04B35/01; C04B35/03; C04B35/04; C04B35/053
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
77 words
A ceramic composition characterized by a coefficient of thermal expansion in the temperature range from 25° C. to 500° C. of between about 14×10 -6 /°C. to about 16×10 -6 /°C. and further characterized by a transverse strength of about 18,000 psi or greater comprising from about 40 to 60% by weight of a finely ground, magnesium oxide dispersed in silicate glass matrix containing at least 3% by weight of zirconium oxide, titanium oxide, or mixtures thereof.
Claim 2
Dependent Claim
77 words
A ceramic composition characterized by a coefficient of thermal expansion in the temperature range from 25° C. to 500° C. of between about 14×10 -6 /°C. to about 16×10 -6 /°C. and further characterized by a transverse strength of about 18,000 psi or greater comprising from about 40 to 60% by weight of a finely ground, magnesium oxide dispersed in silicate glass matrix containing at least 3% by weight of zirconium oxide, titanium oxide, or mixtures thereof.
Claim 3
Dependent Claim
60 words
A ceramic composition of claim 1 wherein said finely ground, magnesium oxide and said silicate glass matrix containing at least 3% by weight zirconium oxide, titanium oxide or mixtures thereof was obtained after being fired to about 1150° C. resulting in crystalline magnesium oxide particles dispersed in a matrix consisting of a glass phase containing a fine dispersion of forsterite.
Claim 4
Dependent Claim
20 words
A ceramic composition of claim 2 wherein said crystalline magnesium oxide particles are less than about 74 μm in diameter.
Claim 5
Independent Claim
169 words
A method of making a ceramic composition characterized by a coefficient of thermal expansion in the temperature range of from 25° C. to 500° C. of between 14×10 -6 /°C. to about 16×10 -6 /°C. and further characterized by a transverse strength of about 18,000 psi or greater comprising the steps of: (a) mixing from about 40 to 60 parts by weight of a finely ground, magnesium oxide with a corresponding 60 to 40 parts by weight, respectively, of a modified silicate glass containing at least about 3% by weight zirconium oxide, titanium oxide or mixtures thereof said glass having a coefficient of thermal expansion between 9 to 12×10 -6 /°C.; (b) firing said mixture produced in step (a) at about 1150° C. for sufficient time to produce crystalline magnesium oxide particles dispersed in a matrix consisting of a glass phase containing a fine dispersion of forsterite; (c) cooling said fired mixture produced in step (b); and (d) recovering said resulting tough, high coefficient of thermal expansion, ceramic composition.
Claim 6
Independent Claim
169 words
A method of making a ceramic composition characterized by a coefficient of thermal expansion in the temperature range of from 25° C. to 500° C. of between 14×10 -6 /°C. to about 16×10 -6 /°C. and further characterized by a transverse strength of about 18,000 psi or greater comprising the steps of: (a) mixing from about 40 to 60 parts by weight of a finely ground, magnesium oxide with a corresponding 60 to 40 parts by weight, respectively, of a modified silicate glass containing at least about 3% by weight zirconium oxide, titanium oxide or mixtures thereof said glass having a coefficient of thermal expansion between 9 to 12×10 -6 /°C.; (b) firing said mixture produced in step (a) at about 1150° C. for sufficient time to produce crystalline magnesium oxide particles dispersed in a matrix consisting of a glass phase containing a fine dispersion of forsterite; (c) cooling said fired mixture produced in step (b); and (d) recovering said resulting tough, high coefficient of thermal expansion, ceramic composition.
Claim 7
Dependent Claim
12 words
A method of claim 4 wherein said firing is performed in vacuum.
Claim 8
Dependent Claim
13 words
A method of claim 5 wherein said cooling is by quenching in water.
References Cited (Backward Citations)
GB686246A
Cited
US2897595A
Cited
US2980998A
Cited
US3069773A
Cited
GB1105111A
Cited
US3504437A
Cited
US3649732A
Cited
US4101330A
Cited
US4265669A
Cited
GB2080281A
Cited
JPS57183361A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-17 | 1989-09-16 | 1990-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-17 | 1993-09-16 | 1994-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-17 | 1997-09-16 | 1998-03-18 | $7700.00 | Window Closed / Lapsed |