Alloy composition and process
Assignee: Crucible Materials Corp
•
Filing: 1984-07-19
•
Granted: 1986-03-18
•
Expires: 2004-07-19
Abstract
Abstract Fully dense consolidated powder alloys of iron, cobalt and/or nickel characterized by having an ultrafine microstructure exhibiting a substantially uniformly dispersed harding phase of particle size essentially less than 3 microns, are produced from prealloyed powders by rapidly quenching an atomized molten alloy charge and subjecting the solidified alloy powder particles to the step of hot consolidation to produce substantially fully dense metal stock directly from prealloyed powder.
Inventors
- 👤 Frederick C. Holtz, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:56
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0292; B; B22; B22F; B22F1/00; B22F1/09; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082; B22F2009/086; B22F2998/00; B22F2998/10; Y; Y10; Y10S; Y10S75/00; Y10S75/95
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
140 words
A consolidated integral high speed steel alloy body which is essentially fully dense formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, Ta, Cb, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is iron or a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is 0% to about 27%.
Claim 2
Dependent Claim
140 words
A consolidated integral high speed steel alloy body which is essentially fully dense formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, Ta, Cb, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is iron or a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is 0% to about 27%.
Claim 3
Dependent Claim
16 words
A high speed steel cutting tool made from an alloy body as defined in claim 1.
Claim 4
Dependent Claim
158 words
A consolidated integral high speed steel alloy body which is substantially fully dense as shown by an improved combination of transverse rupture strength and hardness in cutting tool applications, said body being formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, Ta, Cb, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is about 5% to about 15%.
Claim 5
Dependent Claim
158 words
A consolidated integral high speed steel alloy body which is substantially fully dense as shown by an improved combination of transverse rupture strength and hardness in cutting tool applications, said body being formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, Ta, Cb, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is about 5% to about 15%.
Claim 6
Dependent Claim
16 words
A high speed steel cutting tool made from an alloy body as defined in claim 3.
Claim 7
Dependent Claim
157 words
A consolidated integral high speed steel alloy body which is essentially fully dense as shown by an improved combination of transverse rupture strength and hardness in cutting tool applications, said body being formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is iron or a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is 0% to about 27%.
Claim 8
Dependent Claim
157 words
A consolidated integral high speed steel alloy body which is essentially fully dense as shown by an improved combination of transverse rupture strength and hardness in cutting tool applications, said body being formed of a hot worked super-saturated solid solution of an inherently alloying composition, said alloy body consisting essentially of a continuous metallurgical phase with a uniformly dispersed hard phase of minute dispersed hard phase particle sizes that are essentially entirely less than 3 microns, said alloying composition consisting essentially by weight of from about 0.8% to about 3.4% carbon, at least about 17% of a hard phase-forming element selected from the group consisting of Cr, W, Mo, Ti, and V, and mixtures thereof, and the remainder base metal and incidental impurities, wherein said base metal is iron or a mixture of iron and cobalt, and wherein the amount of iron is at least about 35% and the amount of cobalt is 0% to about 27%.
Claim 9
Dependent Claim
16 words
A high speed steel cutting tool made from an alloy body as defined in claim 5.
References Cited (Backward Citations)
GB781083A
Cited
US2855295A
Cited
US2961312A
Cited
US3150444A
Cited
US3244506A
Cited
US4469514A
Cited
US3561934A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-17 | 1989-09-16 | 1990-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-17 | 1993-09-16 | 1994-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-17 | 1997-09-16 | 1998-03-18 | $7700.00 | Window Closed / Lapsed |