US4574078A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process and apparatus for preparing monodispersed, spherical, non-agglomerated metal oxide particles having a size below one micron
Assignee: Montedison SpA
•
Filing: 1984-02-22
•
Granted: 1986-03-04
•
Expires: 2004-02-22
Abstract
Abstract Spherical, submicronic, monodispersed, and non-agglomerated particles of metal oxides by reacting with steam a gaseous stream containing an aerosol of liquid particles of a hydrolyzable metal compound. Into a duct, in which an inert gas stream containing vapors of a hydrolyzable metal compound flows, there is fed through a nozzle a cold inert gas stream, the temperatures and flows of the two gaseous streams being such as to establish in the duct a temperature lower than the condensation temperature of the metal compound; the mixed gaseous streams having a turbulent flow in the duct, with a Reynolds number equal to or higher than 1800. At the duct outlet, the aerosol of metal compound liquid particles, which has formed in the duct, is caused to react with steam, wherefore solid particles of hydrated metal oxide form, which are subsequently calcined to the oxide.
Inventors
- 👤 Paolo Cortesi
- 👤 Gianni Donati
- 👤 Giuseppe Saggese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:40
CPC Classifications
C; C01; C01G; C01G23/00; C01G23/04; C01G23/047; C01G23/07; B; B01; B01F; B01F25/00; B01F25/30; B01F25/31; B01F25/312; B01J; B01J19/00; B01J19/26; C01B; C01B13/00; C01B13/14; C01B13/20; C01F; C01F7/00; C01F7/02; C01F7/30; C01F7/302; C01F7/304; C01G25/00; C01G25/02; B01J2208/00; B01J2208/00008; B01J2208/00017; B01J2208/00327; B01J2208/00336; B01J2208/00353; B01J2208/00371; B01J2219/00; B01J2219/00049; B01J2219/00051; B01J2219/00121; B01J2219/00123; C01P; C01P2002/00; C01P2002/50; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/51; C01P2004/60; C01P2004/62; C01P2006/00; C01P2006/22; Y; Y10; Y10S; Y10S261/00; Y10S261/75
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
173 words
A process for preparing spherical, submicronic, monodispersed, and non-agglomerated particles of metal oxides by reacting with steam a gaseous stream containing an aerosol of liquid particles of a hydrolyzable metal compound of a metal selected from the class consisting of titanium, aluminum, zirconium, chromium, vanadium, gallium and iron, characterized in that into a duct, in which flows an inert gas stream containing vapors of said hydrolyzable metal compound, there is fed through a nozzle a cold inert gas stream, the temperatures and flow rates of the two gaseous streams being such as to establish in the duct a temperature lower than the condensation temperature of the said metal compound; the mixed gaseous streams having a turbulent flow in the duct with a Reynolds number equal to or higher than 1,800; and at the duct outlet, the aerosol of the said metal compound liquid particles, which has formed in the duct, is reacted with steam, wherefore solid particles of hydrated oxide of said metal form, which are then calcined to the corresponding metal oxide.
Claim 2
Dependent Claim
173 words
A process for preparing spherical, submicronic, monodispersed, and non-agglomerated particles of metal oxides by reacting with steam a gaseous stream containing an aerosol of liquid particles of a hydrolyzable metal compound of a metal selected from the class consisting of titanium, aluminum, zirconium, chromium, vanadium, gallium and iron, characterized in that into a duct, in which flows an inert gas stream containing vapors of said hydrolyzable metal compound, there is fed through a nozzle a cold inert gas stream, the temperatures and flow rates of the two gaseous streams being such as to establish in the duct a temperature lower than the condensation temperature of the said metal compound; the mixed gaseous streams having a turbulent flow in the duct with a Reynolds number equal to or higher than 1,800; and at the duct outlet, the aerosol of the said metal compound liquid particles, which has formed in the duct, is reacted with steam, wherefore solid particles of hydrated oxide of said metal form, which are then calcined to the corresponding metal oxide.
Claim 3
Dependent Claim
48 words
The process according to claim 1, characterized in that the inert gas stream containing vapors of a hydrolyzable metal compound is prepared as follows: an aerosol of liquid particles of the metal compound is caused to form in an inert gas stream, and the aerosol is then evaporated.
Claim 4
Dependent Claim
21 words
The process according to claim 1, characterized in that the hydrolyzable metal compound is a compound of titanium, zirconium or aluminum.
Claim 5
Dependent Claim
38 words
The process according to claim 3, characterized in that the hydrolyzable metal compound is selected from the group consisting of: isopropyltitanate, titanium ethoxide, titanium tetrachloride, aluminum sec. butoxide, aluminum ter. butoxide, aluminum n-butoxide, aluminum isobutoxide, isopropylzirconate, and zirconium-n-propoxide.
Claim 6
Dependent Claim
40 words
The process according to claim 1, characterized in that the inert gas stream containing vapors of a hydrolyzable metal compound is fed into the chamber of an ejector, while the cold inert gas stream is fed into the ejector nozzle.
Claim 7
Dependent Claim
36 words
The process according to claim 1, characterized in that, in the hydrolysis reaction, steam is used in an amount corresponding to about 1.5 to 12 times the stoichiometric ratio with respect to the hydrolyzable metal compound.
Claim 8
Dependent Claim
25 words
The process according to claim 1, characterized in that the hydrated metal oxide solid particles are separated from the gas stream prior to their calcination.
Claim 9
Dependent Claim
23 words
The process according to claim 1, characterized in that the metal oxide solid particles are separated from the gas stream after their calcination.
References Cited (Backward Citations)
US1842620A
Cited
US1967235A
Cited
US2347496A
Cited
US2776188A
Cited
US3297414A
Cited
US3954945A
Cited
US4241042A
Cited
EP0067005A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-03 | 1989-09-02 | 1990-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-03 | 1993-09-02 | 1994-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-03 | 1997-09-02 | 1998-03-04 | $7700.00 | Window Closed / Lapsed |