Process for improved densification of sol-gel produced alumina-based ceramics
Assignee: 3M Co
•
Filing: 1984-05-03
•
Granted: 1986-03-04
•
Expires: 2004-05-03
Abstract
Abstract The sol-gel process for forming dense, alumina-base ceramics, the process comprising 1. preparing a dispersion of aluminum oxide monohydrate containing a precursor of a modifying additive in the form of a soluble salt; 2. gelling the dispersion; 3. drying the gel dispersion to form a solid; 4. calcining the solid; and 5. sintering the calcined solid, is improved by adding to the dispersion at least about 10 weight percent, based on the oxide equivalent of the soluble salt precursor, of at least one densification aid selected from the group consisting of alcohols, glycols and polyether compounds having a vaporization point in excess of the temperature at which the dispersion is dried. This improved process is particularly useful for manufacturing abrasive grains.
Inventors
- 👤 Alvin P. Gerk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:24
CPC Classifications
B; B24; B24D; B24D3/00; B24D3/02; B24D3/20; B24D3/28; B24D3/285; C; C01; C01F; C01F7/00; C01F7/02; C01F7/021; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/1115; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1418
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
143 words
In the sol-gel process for forming a dense, solid, alumina-based ceramic, the process comprising: a. preparing an aqueous dispersion of aluminum oxide monohydrate containing a precursor of a modifying additive which is a metal-containing compound in the form of a strongly oxidizing, soluble salt; b. gelling the dispersion; c. drying the gelled dispersion to form a solid; d. calcining the solid; and e. sintering the calcined solid, the improvement comprising adding to the aqueous dispersion at least about 10 weight percent, based upon the oxide equivalent of the soluble salt precursor, of at least one densification aid selected from the group consisting of ethylene glycol, polyethylene glycol, propylene glycol, polypropylene glycol, glycerine, and di-isopropanol amine, said densification aid providing in the ceramic produced by said process a density which is noticeably increased over that produced by the same process without said densification aid.
Claim 2
Dependent Claim
143 words
In the sol-gel process for forming a dense, solid, alumina-based ceramic, the process comprising: a. preparing an aqueous dispersion of aluminum oxide monohydrate containing a precursor of a modifying additive which is a metal-containing compound in the form of a strongly oxidizing, soluble salt; b. gelling the dispersion; c. drying the gelled dispersion to form a solid; d. calcining the solid; and e. sintering the calcined solid, the improvement comprising adding to the aqueous dispersion at least about 10 weight percent, based upon the oxide equivalent of the soluble salt precursor, of at least one densification aid selected from the group consisting of ethylene glycol, polyethylene glycol, propylene glycol, polypropylene glycol, glycerine, and di-isopropanol amine, said densification aid providing in the ceramic produced by said process a density which is noticeably increased over that produced by the same process without said densification aid.
Claim 3
Dependent Claim
27 words
The process of claim 1 where the metal-containing compound is at least one precursor of the oxides of magnesium, zinc, cobalt, nickel, zirconium, hafnium, chromium and titanium.
Claim 4
Dependent Claim
16 words
The process of claim 2 where the anion of the precursor is a nitrate or perchlorate.
Claim 5
Dependent Claim
21 words
The process of claim 1 where the weight average molecular weight of the densification aid does not exceed about 20 million.
Claim 6
Dependent Claim
20 words
The process of claim 1 where the weight average molecular weight of the densification aid does not exceed about 10,000.
Claim 7
Dependent Claim
29 words
The process of claim 1 where the amount of the densification aid is at least about 25 weight percent of the amount of oxide equivalent of the modifying additive,
Claim 8
Dependent Claim
29 words
The process of claim 6 where the maximum amount of densification aid does not exceed about 200 weight percent of the amount of oxide equivalent of the modifying additive.
Claim 9
Dependent Claim
29 words
The process of claim 6 where the maximum amount of densification aid does not exceed about 75 weight percent of the amount of oxide equivalent of the modifying additive.
Claim 10
Dependent Claim
14 words
The process of claim 1 where the dense, alumina-base ceramic is an abrasive grain.
References Cited (Backward Citations)
US3417028A
Cited
US3325247A
Cited
US3637406A
Cited
US4063856A
Cited
US4181532A
Cited
US4349456A
Cited
GB1594588A
Cited
US4314827A
Cited
US4518397A
Cited
US4472512A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-03 | 1989-09-02 | 1990-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-03 | 1993-09-02 | 1994-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-03 | 1997-09-02 | 1998-03-04 | $7700.00 | Window Closed / Lapsed |