Method for forming metal base composite
Assignee: Toyota Motor Corp
•
Filing: 1984-06-08
•
Granted: 1986-03-04
•
Expires: 2004-06-08
Abstract
Abstract A method for forming metal base composite use a retainer made of water soluble salt with a high melting point. Molten metal and a reinforcement are compounded in the retainer and then solidified. After solidification the retainer is dissolved away by water.
Inventors
- 👤 Tadashi Donomoto
- 👤 Atsuo Tanaka
- 👤 Shinji Katou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 00:02
CPC Classifications
B; B22; B22C; B22C9/00; B22D; B22D27/00; B22D27/09; B22D27/11
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
185 words
A method for forming a metal-base composite, comprising the following steps: a first step in which a mass of fibrous reinforcing material is taken into a retaining tool having a concavity for receiving the said fibrous reinforcing material and at least one opening, said retaining tool being composed of a water-soluble salt having a high melting point, and said concavity having the same shape as the metal-base composite to be formed; a second step in which the said retaining tool containing the said fibrous reinforcing material is heated above a certain temperature and then set into a die having a means for receiving the said retaining tool; a third step in which, through the said opening, a molten matrix metal is made to contact and infiltrate the said fibrous reinforcing material in the said die, and allowing solidification of the said matrix metal to form a composite incorporating the fibrous reinforcing material; a fourth step in which the said retaining tool containing the said composite is removed from the said die; and a fifth step in which said retaining tool is dissolved away with water.
Claim 2
Independent Claim
185 words
A method for forming a metal-base composite, comprising the following steps: a first step in which a mass of fibrous reinforcing material is taken into a retaining tool having a concavity for receiving the said fibrous reinforcing material and at least one opening, said retaining tool being composed of a water-soluble salt having a high melting point, and said concavity having the same shape as the metal-base composite to be formed; a second step in which the said retaining tool containing the said fibrous reinforcing material is heated above a certain temperature and then set into a die having a means for receiving the said retaining tool; a third step in which, through the said opening, a molten matrix metal is made to contact and infiltrate the said fibrous reinforcing material in the said die, and allowing solidification of the said matrix metal to form a composite incorporating the fibrous reinforcing material; a fourth step in which the said retaining tool containing the said composite is removed from the said die; and a fifth step in which said retaining tool is dissolved away with water.
Claim 3
Dependent Claim
32 words
The method of claim 1, wherein pressure is applied to the molten metal during the third step in which the molten metal is made to contact and infiltrate said fibrous reinforcing material.
Claim 4
Dependent Claim
23 words
The method of claim 1, wherein the said certain temperature in the second step is the melting point of the said matrix metal.
Claim 5
Dependent Claim
28 words
The method of claim 1, wherein the said water-soluble salt is at least one member selected from the group consisting of sodium chloride, potassium chloride and barium chloride.
Claim 6
Dependent Claim
36 words
The method of claim 1, wherein the said retaining tool contains at least one member selected from the group consisting of B 2 O 3 , Na 2 O, Li 2 O and K 2 O.
Claim 7
Dependent Claim
21 words
The method of claim 1, wherein said retaining tool is formed by embedding a refractory powder in the said water-soluble salt.
Claim 8
Dependent Claim
39 words
The method of claim 1, wherein the said means for receiving the said retaining tool is a cavity in the said die, wherein the said cavity in the said die is the same shape as the said retaining tool.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-03 | 1989-09-02 | 1990-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-03 | 1993-09-02 | 1994-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-03 | 1997-09-02 | 1998-03-04 | $7700.00 | Window Closed / Lapsed |